Glass-ceramics displaying inherent lubricity
Assignee: Corning Glass Works
•
Filing: 1977-08-04
•
Granted: 1978-10-03
•
Expires: 1997-08-04
Abstract
Abstract The instant invention is related to the production of glass-ceramic articles which exhibit a hydrophobic character and an inherent tactile quality of being slippery or oily to the touch. Such articles are dervived from compositions within the MgO--Al 2 O 3 --SiO 2 --F quaternary and contain the humite mineral norbergite (Mg 2 SiO 4 . MgF 2 ) as a major crystal phase. The intrinsic hydrophobic character and lubricity of the inventive compositions recommend their utility in such applications as (1) high temperature bearing or other low friction mechanical devices, an (2) non-sticking and easily-cleaned culinary ware.
Inventors
- 👤 George H. Beall
- 👤 Kenneth Chyung
- 👤 Syed N. Hoda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:34
CPC Classifications
F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/043; C; C03; C03B; C03B32/00; C03B32/02; C03C; C03C10/00; C03C10/16
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
131 words
A method for making a glass-ceramic article exhibiting the properties of lubricity and excellent resistance to wear and having a crystal content in excess of 50% by volume wherein norbergite constitutes the predominant crystal phase, which consists in the steps of: (a) melting a batch for a glass consisting essentially, by weight on the oxide basis, of about 12-40% MgO, 3-15% Al 2 O 3 , 35-55% SiO 2 , and 5-15% F, the sum of those four components constituting at least 75% by weight of the total composition; (b) simultaneously cooling said melt to a temperature at least below the transformation range and shaping a glass article therefrom; and then (c) heating said glass article to a temperature between about 850°-1150° C. to cause the growth in situ of crystals.
Claim 2
Independent Claim
131 words
A method for making a glass-ceramic article exhibiting the properties of lubricity and excellent resistance to wear and having a crystal content in excess of 50% by volume wherein norbergite constitutes the predominant crystal phase, which consists in the steps of: (a) melting a batch for a glass consisting essentially, by weight on the oxide basis, of about 12-40% MgO, 3-15% Al 2 O 3 , 35-55% SiO 2 , and 5-15% F, the sum of those four components constituting at least 75% by weight of the total composition; (b) simultaneously cooling said melt to a temperature at least below the transformation range and shaping a glass article therefrom; and then (c) heating said glass article to a temperature between about 850°-1150° C. to cause the growth in situ of crystals.
Claim 3
Dependent Claim
51 words
A method according to claim 1 wherein said glass article is first heated to a temperature between about 750°-850° C. for about 1-6 hours to cause nucleation therein and thereafter heated to a temperature between about 850°-1150° C. for about 1-8 hours to effect the growth of crystals on said nuclei.
Claim 4
Dependent Claim
17 words
A method according to claim 1 wherein said crystals have diameters of less than about 2 microns.
Claim 5
Dependent Claim
12 words
A glass-ceramic article made in accordance with the method of claim 1.
References Cited (Backward Citations)
US3801295A
Cited
US3939056A
Cited
US3905824A
Cited
US3985531A
Cited
US3985534A
Cited
US4063955A
Cited
US4018612A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-02 | 1982-04-03 | 1982-10-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-10-02 | 1986-04-03 | 1986-10-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-10-02 | 1990-04-03 | 1990-10-03 | $7700.00 | Window Closed / Lapsed |