Method for repair of porcelain dental prostheses
Assignee: Den Mat Inc
•
Filing: 1977-04-15
•
Granted: 1978-10-03
•
Expires: 1997-04-15
Abstract
Abstract A kit containing the components essential for repairing, in situ, damaged or fractured porcelain dental prostheses. A method for carrying out such repair includes cleaning, shaping, and priming the damaged area, applying a bonding agent preferably containing two silanes and a water-displacing solvent, then applying a filling agent comprising vitreous powder and a resin binder, allowing the agent to set and harden, and finishing. A filler composition or agent and an advantageous bonding composition are also provided.
Inventors
- 👤 Robert L. Ibsen
- 👤 William Richard Glace
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 16:53
CPC Classifications
A; A61; A61C; A61C19/00; A61C19/005
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
150 words
A method of repairing in situ a damaged dental porcelain prosthesis on a suitable base: (a) mechanically removing all plaque adjacent the damaged site, (b) mechanically removing all friable porcelain at the damaged site, (c) washing the damaged site with a priming agent consisting essentially of an aqueous solution of a weak acid, (d) removing said agent with a water wash and drying said site, (e) applying to the damaged site a bonding agent to adhere a restorative material to said base and to said porcelain and allowing to remain for at least 20 seconds, (f) mixing together a liquid resin and white powder in such amounts that the resulting mixture is wet and just barely too thick to flow, (g) applying said mixture of resin and powder to at least fill the damaged site and allow to set and harden, and (h) finishing the surface of the filled site.
Claim 2
Independent Claim
150 words
A method of repairing in situ a damaged dental porcelain prosthesis on a suitable base: (a) mechanically removing all plaque adjacent the damaged site, (b) mechanically removing all friable porcelain at the damaged site, (c) washing the damaged site with a priming agent consisting essentially of an aqueous solution of a weak acid, (d) removing said agent with a water wash and drying said site, (e) applying to the damaged site a bonding agent to adhere a restorative material to said base and to said porcelain and allowing to remain for at least 20 seconds, (f) mixing together a liquid resin and white powder in such amounts that the resulting mixture is wet and just barely too thick to flow, (g) applying said mixture of resin and powder to at least fill the damaged site and allow to set and harden, and (h) finishing the surface of the filled site.
Claim 3
Dependent Claim
20 words
The method of claim 1 wherein said priming agent consists essentially of a 30% solution of citric acid in water.
Claim 4
Dependent Claim
21 words
The method of claim 1 wherein said bonding agent consists essentially of a butanol solution of gamma-methacryltripropyltrimethoxysilane and gamma-glycidoxypropyltrimethoxysilane, remainder butanol.
Claim 5
Dependent Claim
56 words
The method of claim 1 wherein the surface of any exposed metal after step (c) is coated with a mixture of liquid resin and white vitreous powder containing added pigment in sufficient amount to render the mixture opaque, said resin being added in such amount as to wet the powder and avoid flowing of the mixture.
Claim 6
Dependent Claim
24 words
The method of claim 4 wherein said admixture contains about 1 part by weight resin and about 3-4 parts by weight of said powder.
Claim 7
Dependent Claim
20 words
The method of claim 1 wherein said liquid resin in step (f) is a flowable ethoxylated bisphenol A dimethacrylate resin.
Claim 8
Dependent Claim
28 words
The method of claim 1 wherein there are mixed in step (f) about 3-4 parts by weight of white vitreous powder and about 1 part by weight resin.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-10-02 | 1982-04-03 | 1982-10-03 | $2000.00 | Window Closed / Lapsed |