Chromium base alloy composite materials reinforced with continuous silicon carbide fibers and a method for producing the same

Claim 1

Chromium base alloy composite materials reinforced with silicon carbide fibers obtained by incorporating silicon carbide fibers containing 0.01 - 20% by weight of free carbon into chromium base alloy consisting of 20 - 98% by weight of chromium and the remainder iron in a volume fraction of 5 - 20%.

Claim 5

A method for producing chromium base alloy composite materials reinforced with silicon carbide fibers, which comprises laminating and arranging a volume fraction of 2 - 50% of silicon carbide fibers containing 0.01 - 20% by weight of free carbon which have been produced by heating the spun fibers composed of organosilicon high molecular weight compounds having silicon and carbon as the main skeleton components at a temperature of 1,000°- 2,000° C, in chromium base alloy powders consisting of 20 - 98% by weight of Cr and the remainder Fe and then compressing and sintering the resulting assembly to react the free carbon in the silicon carbide fibers with chromium base alloy powders to form carbides, whereby the binding ability of the silicon carbide fibers and chromium base alloy is increased.

Claim 6

A method for producing chromium base alloy composite materials reinforced with silicon carbide fibers, which comprises laminating and arranging a volume fraction of 2 - 50% of silicon carbide fibers containing 0.01 - 20% by weight of free carbon which have been produced by heating the spun fibers composed of organosilicon high molecular weight compounds having silicon and carbon as the main skeleton components at a temperature of 1,000°- 2,000° C, in chromium base alloy powders consisting of 20 - 98% by weight of Cr and the remainder Fe and then compressing and sintering the resulting assembly to react the free carbon in the silicon carbide fibers with chromium base alloy powders to form carbides, whereby the binding ability of the silicon carbide fibers and chromium base alloy is increased.

Claim 7

A method for producing chromium base alloy composite materials reinforced with silicon carbide fibers, which comprises laminating and arranging a volume fraction of 2 - 50% of silicon carbide fibers containing 0.01 - 20% by weight of free carbon which have been produced by heating the spun fibers composed of organosilicon high molecular weight compounds having silicon and carbon as the main skeleton components at a temperature of 1,000°- 2,000° C, into chromium base alloy powders consisting of 20 - 98% by weight of Cr, if necessary containing at least one of Ni and Co; at least one of Ru and Re; C; at least one of Nb, Ta, T, V, Zr, Hf and V; W; Mo; Si; Mn; Be; B; Al; at least one of Ca, Mg and Y; at least one of rare earth metals, and the remainder Fe, provided that Ni and Co being 30 - 60% by weight, Ru and Re being 15 - 40% by weight, C being not more than 0.7% by weight, Nb, Ta, Ti, V, Zr, Hf and V being 0.01 - 5.0% by weight, W being not more than 20% by weight, Mo being not more than 30% by weight, Si being not more than 5% by weight, Mn being not more than 10% by weight, Be being not more than 1% by weight, B being not more than 0.1% by weight, Al being not more than 10% by weight, Ca, Mg and Y being not more than 0.5% by weight and rare earth metals being not more than 1.0% by weight or into mixture powders obtained by mixing metal powders constituting the above described chromium base alloy in the above described contituting ratio, and then compressing and sintering the resulting assembly to react the free carbon in the silicon carbide fibers with chromium base alloy powders or the above described mixture powders to form carbides, whereby the binding ability of the silicon carbide fibers and chromium base alloy is increased.

Claim 8

A method for producing chromium base alloy composite materials reinforced with silicon carbide fibers, which comprises laminating and arranging a volume fraction of 2 - 50% of silicon carbide fibers containing 0.01 - 20% by weight of free carbon which have been produced by heating the spun fibers composed of organosilicon high molecular weight compounds having silicon and carbon as the main skeleton components at a temperature of 1,000°- 2,000° C, into chromium base alloy powders consisting of 20 - 98% by weight of Cr, if necessary containing at least one of Ni and Co; at least one of Ru and Re; C; at least one of Nb, Ta, T, V, Zr, Hf and V; W; Mo; Si; Mn; Be; B; Al; at least one of Ca, Mg and Y; at least one of rare earth metals, and the remainder Fe, provided that Ni and Co being 30 - 60% by weight, Ru and Re being 15 - 40% by weight, C being not more than 0.7% by weight, Nb, Ta, Ti, V, Zr, Hf and V being 0.01 - 5.0% by weight, W being not more than 20% by weight, Mo being not more than 30% by weight, Si being not more than 5% by weight, Mn being not more than 10% by weight, Be being not more than 1% by weight, B being not more than 0.1% by weight, Al being not more than 10% by weight, Ca, Mg and Y being not more than 0.5% by weight and rare earth metals being not more than 1.0% by weight or into mixture powders obtained by mixing metal powders constituting the above described chromium base alloy in the above described contituting ratio, and then compressing and sintering the resulting assembly to react the free carbon in the silicon carbide fibers with chromium base alloy powders or the above described mixture powders to form carbides, whereby the binding ability of the silicon carbide fibers and chromium base alloy is increased.