Increasing absorbency of polymeric compositions by curing
Assignee: United States Department of Agriculture
•
Filing: 1977-08-15
•
Granted: 1978-09-26
•
Expires: 1997-08-15
Abstract
Abstract Absorbent polymeric compositions are prepared by drying aqueous dispersions of physical mixtures of polyhydroxy polymers, such as starch, with carboxylate-containing synthetic polymers, such as saponified polyacrylonitrile of partially saponified polyacrylamide, and then curing the resulting dry solids with either heat or prolonged standing at room temperature. These compositions typically absorb several hundred times their weight of deionized water.
Inventors
- 👤 George F. Fanta
- 👤 William M. Doane
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:22
CPC Classifications
C; C08; C08L; C08L3/00; C08L3/02; A; A61; A61L; A61L15/00; A61L15/16; A61L15/42; A61L15/60; C08J; C08J3/00; C08J3/005; C08J3/24; C08J3/246; C08L1/00; C08L29/00; C08L29/02; C08L29/04
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
101 words
A method for producing absorbent polymeric compositions comprising the following steps: a. providing an aqueous dispersion of a physical mixture of a polyhydroxy polymer and a carboxylate-containing synthetic polymer, wherein said synthetic polymer is characterized by the property of remaining water dispersible upon initial drying of the aqueous dispersion of said physical mixture; b. drying said aqueous dispersion to form water-dispersible dry solids of said polyhydroxy polymer and said synthetic polymer; and c. curing said dry solids by treatment with a combination of time and temperature sufficient to render said solids nondispersible and capable of swelling upon absorption of aqueous fluids.
Claim 2
Independent Claim
101 words
A method for producing absorbent polymeric compositions comprising the following steps: a. providing an aqueous dispersion of a physical mixture of a polyhydroxy polymer and a carboxylate-containing synthetic polymer, wherein said synthetic polymer is characterized by the property of remaining water dispersible upon initial drying of the aqueous dispersion of said physical mixture; b. drying said aqueous dispersion to form water-dispersible dry solids of said polyhydroxy polymer and said synthetic polymer; and c. curing said dry solids by treatment with a combination of time and temperature sufficient to render said solids nondispersible and capable of swelling upon absorption of aqueous fluids.
Claim 3
Dependent Claim
29 words
The method as described in claim 1 wherein said polyhydroxy polymer is selected from the group consisting of starches, starch-containing flours, amylose, amylopectin, cellulose, cellulose derivatives, and polyvinyl alcohol.
Claim 4
Dependent Claim
31 words
The method as described in claim 1 wherein said polyhydroxy polymer is selected from the group consisting of cereal grain starches, cereal grain flours, root crop starches, and root crop flours.
Claim 5
Dependent Claim
13 words
The method as described in claim 3 wherein said polyhydroxy polymer is gelatinized.
Claim 6
Dependent Claim
30 words
The method as described in claim 1 wherein said carboxylate-containing synthetic polymer is selected from the group consisting of saponified polyacrylonitrile, saponified polyacrylamide, and copolymers of acrylamide and sodium acrylate.
Claim 7
Dependent Claim
29 words
The method as described in claim 1 wherein the proportion of polyhydroxy polymer to synthetic polymer is in the range of about 75:25 to about 25:75 parts by weight.
Claim 8
Dependent Claim
22 words
The method as described in claim 1 wherein the proportion of polyhydroxy polymer to synthetic polymer is about 50:50 parts by weight.
Claim 9
Dependent Claim
23 words
The method as described in claim 1 wherein said curing is at room temperature for a time of at least about 8 days.
Claim 10
Dependent Claim
29 words
The method as described in claim 1 wherein said curing is at an elevated temperature in the range of about 110°-150° C. for a time of about 15-30 min.
Claim 11
Dependent Claim
10 words
Absorbent polymeric compositions produced by the process of claim 1.
Claim 12
Independent Claim
93 words
A method for producing absorbent polymeric compositions comprising the following steps: a. providing an aqueous dispersion of a graft copolymer of a polyhydroxy polymer and a carboxylate-containing synthetic polymer, wherein said graft copolymer is characterized by the property of remaining water dispersible upon initial drying of the aqueous dispersion thereof; b. drying said aqueous dispersion to form water-dispersible dry solids of said graft copolymer; c. curing said dry solids by treatment with a combination of time and temperature sufficient to render said solids nondispersible and capable of swelling upon absorption of aqueous fluids.
Claim 13
Independent Claim
93 words
A method for producing absorbent polymeric compositions comprising the following steps: a. providing an aqueous dispersion of a graft copolymer of a polyhydroxy polymer and a carboxylate-containing synthetic polymer, wherein said graft copolymer is characterized by the property of remaining water dispersible upon initial drying of the aqueous dispersion thereof; b. drying said aqueous dispersion to form water-dispersible dry solids of said graft copolymer; c. curing said dry solids by treatment with a combination of time and temperature sufficient to render said solids nondispersible and capable of swelling upon absorption of aqueous fluids.
Claim 14
Dependent Claim
35 words
The method as described in claim 11 wherein said polyhydroxy polymer is a gelatinized starch or gelatinized starch-containing flour and said carboxylate-containing synthetic polymer is saponified polyacrylamide or a copolymer of acrylamide and sodium acrylate.
Claim 15
Dependent Claim
23 words
The method as described in claim 11 wherein said curing is at room temperature for a time of at least about 8 days.
Claim 16
Dependent Claim
29 words
The method as described in claim 11 wherein said curing is at an elevated temperature in the range of about 110°-150° C. for a time of about 15-30 minutes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-25 | 1982-03-27 | 1982-09-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-25 | 1986-03-27 | 1986-09-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-25 | 1990-03-27 | 1990-09-26 | $7700.00 | Window Closed / Lapsed |