Process for drying polymer-modified cellulose fibres and products produced thereby
Assignee: FPInnovations
•
Filing: 1975-06-24
•
Granted: 1977-05-24
•
Expires: 1995-06-24
Abstract
Abstract An economic process is provided for effectively drying wet, highly swollen, polymer-modified, cellulosic fibres to provide fibres having enhanced properties of both water and physiological liquid retention. The essential steps of the drying process are as follows: First, the hydrolyzed fibres are thoroughly washed with water, thus rendering them to a substantially maximum swollen state. The fibres are then acidified to a low, critical pH whereby the water previously retained by the alkaline fibre is released and filtered off, thus rendering them to a substantially minimum swollen state. The product may be subjected to an optional non-shearing stirring step while in a low consistency dispersion prior to the acidification step. Further treatment with an alkali non-swelling solvent mixture renders the fibres substantially water-free in their alkaline salt form. A final wash and drying step using substantially water-free solvent and heat complete the process to yield dry, polymer-modified, cellulosic fibres having enhanced properties of both water and physiological liquid retention. New fibres can be produced having water retention values above 40g/g and aqueous salt retention values above 16 g/g.
Inventors
- 👤 Pierre Lepoutre
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 21:55
CPC Classifications
D; D21; D21C; D21C9/00; D21C9/001; D21C9/002; D21C9/005; A; A61; A61L; A61L15/00; A61L15/16; A61L15/22; A61L15/28; C; C08; C08F; C08F251/00; C08F251/02; C08F8/00; C08F8/44
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
157 words
In a process for drying modified cellulosic material having water retention properties, said cellulosic material being a graft polymerized cellulose, the grafting monomer being an alpha ethylenically unsaturated compound containing at least one functional moiety selected from the group consisting of acrylamide, acyl halide, nitrile, ester, alkenyl halide, carboxylate salt, and carboxylic acid and having been reacted with an aqueous alkali solution to hydrolyze or neutralize said functional moiety; wherein the improvement comprises: (a) washing resultant alkali treated cellulosic material with water to lower the pH of said material so as to swell the material to at least 50% of the maximum swollen state thereof; (b) acidifying resultant swollen material to render the product to substantially the minimum swollen state thereof; (c) neutralizing the resultant acidified material with alkali dissolved in a non-swelling solvent to obtain the alkali salt form of said cellulosic material; and (d) thermally drying resultant alkali salt form of the graft-polymerized cellulosic material.
Claim 2
Dependent Claim
157 words
In a process for drying modified cellulosic material having water retention properties, said cellulosic material being a graft polymerized cellulose, the grafting monomer being an alpha ethylenically unsaturated compound containing at least one functional moiety selected from the group consisting of acrylamide, acyl halide, nitrile, ester, alkenyl halide, carboxylate salt, and carboxylic acid and having been reacted with an aqueous alkali solution to hydrolyze or neutralize said functional moiety; wherein the improvement comprises: (a) washing resultant alkali treated cellulosic material with water to lower the pH of said material so as to swell the material to at least 50% of the maximum swollen state thereof; (b) acidifying resultant swollen material to render the product to substantially the minimum swollen state thereof; (c) neutralizing the resultant acidified material with alkali dissolved in a non-swelling solvent to obtain the alkali salt form of said cellulosic material; and (d) thermally drying resultant alkali salt form of the graft-polymerized cellulosic material.
Claim 3
Dependent Claim
35 words
A process according to claim 1, wherein intermediate said steps (a) and (b), the swollen material is agitated under non-shearing, non-gel-forming conditions, thereby resulting in a final product having enhanced water and physiological fluid retention.
Claim 4
Dependent Claim
15 words
The process of claim 1, wherein the pH of the swollen material is 6- 10.
Claim 5
Dependent Claim
15 words
The process of claim 1, wherein the pH of the swollen material is 6- 9.
Claim 6
Dependent Claim
20 words
The process of claim 1, wherein the cellulosic material in step (a) is swollen to substantially the maximum swollen state.
Claim 7
Dependent Claim
18 words
The process of claim 1, wherein the pH of the acidified material in step (b) is 2.5- 4.
Claim 8
Dependent Claim
18 words
The process of claim 1, wherein the pH of the acidified material in step (b) is 3- 3.7.
Claim 9
Dependent Claim
18 words
The process of claim 3, wherein the pH of the acidified material in step (b) is 2.5- 4.
Claim 10
Dependent Claim
18 words
The process of claim 4, wherein the pH of the acidified material in step (b) is 3- 3.7.
Claim 11
Dependent Claim
35 words
A process according to claim 9, wherein intermediate said steps (a) and (b), the swollen material is agitated under non-shearing, non-gel-forming conditions, thereby resulting in a final product having enhanced water and physiological fluid retention.
Claim 12
Dependent Claim
11 words
A process according to claim 1, wherein the monomer is acrylonitrile.
Claim 13
Dependent Claim
11 words
A process according to claim 10, wherein the monomer is acrylonitrile.
Claim 14
Dependent Claim
35 words
A process according to claim 12, wherein intermediate said steps (a) and (b), the swollen material is agitated under non-shearing, non-gel-forming conditions, thereby resulting in a final product having enhanced water and physiological fluid retention.
Claim 15
Dependent Claim
25 words
A process according to claim 1, wherein the non-swelling solvent of step (c) is a lower alkyl alcohol and the alkali is an alkali hydroxide.
Claim 16
Dependent Claim
35 words
A process according to claim 1, wherein the monomer is acrylamide, acrylonitrile, methacrylonitrile, acrylic esters, methacrylic esters, vinyl acetate, acrylyl chloride, vinyl chloride, vinylidene chloride, vinylidene cyanide, p-chloro-styrene, maleic anhydride, maleimide, fumaramide, or combinations thereof.
Claim 17
Dependent Claim
47 words
A dry cellulosic material graft polymerized with a polymer of an alpha ethylenically unsaturated monomer, said polymer having alkali carboxylate groups attached thereto, said cellulosic material exhibiting a water retention value over 40 g/g and over 16 g/g of a 1% by weight aqueous sodium chloride solution.
Claim 18
Dependent Claim
47 words
A dry cellulosic material graft polymerized with a polymer of an alpha ethylenically unsaturated monomer, said polymer having alkali carboxylate groups attached thereto, said cellulosic material exhibiting a water retention value over 40 g/g and over 16 g/g of a 1% by weight aqueous sodium chloride solution.
Claim 19
Dependent Claim
17 words
A cellulosic material according to claim 16, exhibiting retention over 41 g/g and over 17 g/g respectively.
Claim 20
Dependent Claim
17 words
A cellulosic material according to claim 16, exhibiting retention over 42 g/g and over 18 g/g respectively.
Claim 21
Dependent Claim
17 words
A cellulosic material according to claim 16, exhibiting retention over 43 g/g and over 19 g/g respectively.
Claim 22
Dependent Claim
17 words
A cellulosic material according to claim 16, exhibiting retention over 44 g/g and over 20 g/g respectively.
Claim 23
Dependent Claim
43 words
A cellulosic material according to claim 20, being a never-dried softwood bleached kraft pulp grafted with about 160% by weight of polyacrylonitrile and having been hydrolyzed in an aqueous alkali solution after the graft polymerization then subjected to the process of claim 2.
References Cited (Backward Citations)
US3935099A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1980-05-23 | 1980-11-22 | 1981-05-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1984-05-23 | 1984-11-22 | 1985-05-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1988-05-23 | 1988-11-22 | 1989-05-24 | $7700.00 | Window Closed / Lapsed |