Method and apparatus for forming a deposit by means of ion plating using a magnetron cathode target as source of coating material
Assignee: ASU COMPOSANTS S A A CORP OF SWITZERLAND
•
Filing: 1977-05-18
•
Granted: 1978-09-26
•
Expires: 1997-05-18
Abstract
Abstract A substrate to be coated by the ion-plating technique is placed on or in the immediate vicinity of a first cathode confronting a second cathode in an enclosure containing a rarefied gaseous atmosphere, the second cathode constituting a target of material to be deposited on the substrate. The application of a relatively high negative biasing voltage to the first cathode, relative to the grounded enclosure, generates a glow discharge resulting in ionic cleaning of the substrate. A sputtering discharge generated by a relatively low negative biasing voltage on the second cathode is intensified by a toroidal magnet on its far side (remote from the first cathode) whose lines of force penetrate the target and close in the intercathode space to form an endless track for circulating electrons. During the cleaning phase, the substrate is protected against premature particle deposition by the temporary interposition of a shield between itself and the target or by being located at a distance from the active portion of the second cathode; energization of the latter thereafter builds up a coating of target material on the cleaned substrate.
Inventors
- 👤 Bogdan Zega
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 22:53
CPC Classifications
H; H01; H01J; H01J37/00; H01J37/32; H01J37/34; H01J37/3402; H01J37/3405; C; C23; C23C; C23C14/00; C23C14/22; C23C14/34; C23C14/35
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
227 words
A method of ionically cleaning and coating a substrate, comprising the steps of: placing the substrate in the immediate vicinity of a cathode within a conductive enclosure containing a rarefied gaseous atmosphere; biasing said cathode sufficiently negative with reference to said enclosure to generate a glow discharge resulting in an ionic cleaning of the substrate with formation of a dark space adjacent said cathode; energizing a target electrode of coating material, confronting said cathode at a location in said enclosure beyond said dark space, with a negative voltage of lower absolute magnitude than that of cathode to generate a sputtering discharge between said target electrode and said enclosure, the potential difference between said cathode and said target electrode being sufficient to produce a discharge current at said target electrode of a magnitude substantially equal to that produced upon a like energization of the target electrode in the absence of said cathode; and setting up a magnetic field across said target electrode with lines of force closed on the side facing said cathode to establish an endless track for the circulation of secondary electrons emitted by said target electrode, with resulting intensification of the rate of emission of ions of coating material toward said substrate to exceed the rate of substrate erosion by said glow discharge whereby a deposit of coating material is built up on said substrate.
Claim 2
Independent Claim
227 words
A method of ionically cleaning and coating a substrate, comprising the steps of: placing the substrate in the immediate vicinity of a cathode within a conductive enclosure containing a rarefied gaseous atmosphere; biasing said cathode sufficiently negative with reference to said enclosure to generate a glow discharge resulting in an ionic cleaning of the substrate with formation of a dark space adjacent said cathode; energizing a target electrode of coating material, confronting said cathode at a location in said enclosure beyond said dark space, with a negative voltage of lower absolute magnitude than that of cathode to generate a sputtering discharge between said target electrode and said enclosure, the potential difference between said cathode and said target electrode being sufficient to produce a discharge current at said target electrode of a magnitude substantially equal to that produced upon a like energization of the target electrode in the absence of said cathode; and setting up a magnetic field across said target electrode with lines of force closed on the side facing said cathode to establish an endless track for the circulation of secondary electrons emitted by said target electrode, with resulting intensification of the rate of emission of ions of coating material toward said substrate to exceed the rate of substrate erosion by said glow discharge whereby a deposit of coating material is built up on said substrate.
Claim 3
Dependent Claim
35 words
A method as defined in claim 1 wherein the energization of said target electrode is deferred beyond the initiation of said glow discharge to establish a time interval for the ionic cleaning of the substrate.
Claim 4
Dependent Claim
23 words
A method as defined in claim 2 wherein a screen is interposed between said target electrode and said cathode during said time interval.
Claim 5
Dependent Claim
24 words
A method as defined in claim 2 wherein the gas pressure of said rarefied atmosphere is lowered at the end of said time interval.
Claim 6
Dependent Claim
21 words
A method as defined in claim 1, comprising the further step of preheating said substrate before juxtaposing it with said cathode.
Claim 7
Dependent Claim
41 words
A method as defined in claim 1 wherein said substrate is first subjected to said glow discharge at a location remote from said magnetic field for ionic cleaning before being brought into the vicinity of said field for receiving said deposit.
Claim 8
Dependent Claim
29 words
A method as defined in claim 1 wherein said rarefied atmosphere comprises an inert gas, comprising the further step of admixing therewith a gas reactive with said coating material.
Claim 9
Dependent Claim
46 words
A method as defined in claim 7 wherein an initial deposit of coating material on said substrate is carried out in said inert gas, followed by a progressive replacement of the inert gas by said reactive gas with continuation of said glow discharge and sputtering discharge.
Claim 10
Dependent Claim
19 words
A method as defined in claim 8 wherein said coating material is metallic and said reactive gas is nitrogen.
Claim 11
Dependent Claim
55 words
A method as defined in claim 9 wherein said coating material is titanium and said substrate is made of steel, the pressure of said rarefied atmosphere being on the order of 10 -2 Torr during buildup of said initial deposit and being lowered to the order of 10 -3 Torr with introduction of the nitrogen.
Claim 12
Dependent Claim
27 words
A method as defined in claim 10, comprising the further step of heating said substrate during ionic cleaning to a temperature of substantially 450° to 600° C.
Claim 13
Dependent Claim
34 words
A method as defined in claim 11, comprising the further step of allowing said target to heat up to a temperature above a level of about 700° C. upon the lowering of said pressure.
Claim 14
Dependent Claim
34 words
A method as defined in claim 7 wherein said inert gas is argon and said reactive gas is oxygen, said coating material is an alloy of indium and tin, and said substrate is glass.
Claim 15
Dependent Claim
27 words
A method as defined in claim 13, comprising the further step of heating said substrate in air after the formation of said deposit to render same transparent.
Claim 16
Dependent Claim
50 words
A method as defined in claim 1 wherein said coating material is titanium nitride, said substrate is glass and said rarefied atmosphere consists of an inert gas, comprising the further step of preheating said substrate to a temperature on the order of 300° C. before juxtaposing it with said cathode.
Claim 17
Independent Claim
328 words
An apparatus for ionically cleaning and coating a substrate, comprising: a conductive enclosure forming an ionization chamber, said enclosure being provided with circulation means for maintaining a rarefied gaseous atmosphere in said chamber; a cathode in said chamber insulated from said enclosure; a first direct-current source connected between said enclosure and said cathode for maintaining the latter at a negative potential relative to said enclosure sufficient to generate a glow discharge therebetween resulting in an ionic cleaning of a substrate disposed in the immediate vicinity of said cathode in said chamber, with formation of a dark space adjacent said cathode; a generally plate-shaped target electrode adapted to carry a coating material disposed in said chamber opposite said cathode at a location beyond said dark space in insulated relationship with said enclosure; a second direct-current source connected between said target electrode and said enclosure for biasing said target electrode with reference to said enclosure at a negative potential less than that of said cathode but high enough to generate a sputtering discharge between said target electrode and said enclosure, the first and second direct-current sources being adapted to maintain the potential difference between said target electrode and said cathode at a value sufficient to produce a discharge current at said target electrode of a magnitude substantially equal to that produced by said second source in the absence of said cathode; and magnetic means adjacent said target electrode with north and south poles trained along concentric lines upon a surface of said target electrode remote from said cathode, for providing a magnetic field with lines of force closed on the side facing said cathode to establish an endless track for the circulation of secondary electrons emitted by said target electrode with resulting intensification of the rate of emission of ions of coating material toward said substrate to exceed the rate of substrate erosion by said glow discharge whereby a deposit of said coating material is built up on said substrate.
Claim 18
Independent Claim
328 words
An apparatus for ionically cleaning and coating a substrate, comprising: a conductive enclosure forming an ionization chamber, said enclosure being provided with circulation means for maintaining a rarefied gaseous atmosphere in said chamber; a cathode in said chamber insulated from said enclosure; a first direct-current source connected between said enclosure and said cathode for maintaining the latter at a negative potential relative to said enclosure sufficient to generate a glow discharge therebetween resulting in an ionic cleaning of a substrate disposed in the immediate vicinity of said cathode in said chamber, with formation of a dark space adjacent said cathode; a generally plate-shaped target electrode adapted to carry a coating material disposed in said chamber opposite said cathode at a location beyond said dark space in insulated relationship with said enclosure; a second direct-current source connected between said target electrode and said enclosure for biasing said target electrode with reference to said enclosure at a negative potential less than that of said cathode but high enough to generate a sputtering discharge between said target electrode and said enclosure, the first and second direct-current sources being adapted to maintain the potential difference between said target electrode and said cathode at a value sufficient to produce a discharge current at said target electrode of a magnitude substantially equal to that produced by said second source in the absence of said cathode; and magnetic means adjacent said target electrode with north and south poles trained along concentric lines upon a surface of said target electrode remote from said cathode, for providing a magnetic field with lines of force closed on the side facing said cathode to establish an endless track for the circulation of secondary electrons emitted by said target electrode with resulting intensification of the rate of emission of ions of coating material toward said substrate to exceed the rate of substrate erosion by said glow discharge whereby a deposit of said coating material is built up on said substrate.
Claim 19
Dependent Claim
45 words
An apparatus as defined in claim 16, further comprising a box within said chamber closed on one side by said target electrode and provided with inlet and outlet means for the circulation of a cooling fluid therethrough, said magnetic means being disposed in said box.
Claim 20
Dependent Claim
18 words
An apparatus as defined in claim 16 wherein said magnetic means comprises a permanent magnet of toroidal configuration.
Claim 21
Dependent Claim
23 words
An apparatus as defined in claim 16, further comprising screen means in said chamber selectively interposable between said target electrode and said cathode.
Claim 22
Dependent Claim
27 words
An apparatus as defined in claim 16 wherein said cathode is disposed below said target electrode and has an upper surface forming a support for said substrate.
Claim 23
Dependent Claim
33 words
An apparatus as defined in claim 16 wherein said cathode is disposed above said target electrode, further comprising support means in said chamber for holding said substrate in the vicinity of said cathode.
Claim 24
Dependent Claim
25 words
An apparatus as defined in claim 21 wherein said cathode is in the shape of a grid, said support means being located above said grid.
Claim 25
Dependent Claim
46 words
An apparatus as defined in claim 16 wherein said cathode is in the shape of a drum centered on a generally horizontal axis, further comprising drive means for rotating said drum about said axis, said target electrode and magnetic means being nonrotatably disposed in said drum.
Claim 26
Dependent Claim
69 words
An apparatus as defined in claim 23 wherein said axis is inclined at an angle to the horizontal, said enclosure being provided at opposite ends with an entrance port near a raised edge of the drum bottom and with an exit port near a lowered edge of the drum bottom for enabling the continuous passage of substrate parts through said chamber between the drum bottom and said target electrode.
Claim 27
Dependent Claim
37 words
An apparatus as defined in claim 24 wherein said magnetic means is axially separated from the entrance side of said drum to form a zone in which the entering substrate parts are subjected only to ionic cleaning.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-25 | 1982-03-27 | 1982-09-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-25 | 1986-03-27 | 1986-09-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-25 | 1990-03-27 | 1990-09-26 | $7700.00 | Window Closed / Lapsed |