Water resistant corrugating adhesive composition
Assignee: Anheuser Busch Companies LLC
•
Filing: 1975-07-18
•
Granted: 1978-09-26
•
Expires: 1995-07-18
Abstract
Abstract This disclosure relates to a water resistant adhesive composition for use in the manufacture of corrugated board and its preparation. The adhesive is prepared by using a thin boiling or modified waxy variety starch of a fluidity of at least 25 as a component in the gelatinized carrier portion of the adhesive. This produces a high solids carrier which results in a final adhesive of good stability whose use enables corrugated board to be produced at faster than normal rates. This adhesive is particularly useful to increase production rates of heavy weight and multiwall board.
Inventors
- 👤 Camillus B. Musselman
- 👤 Edward M. Bovier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 13:12
CPC Classifications
C; C09; C09J; C09J103/00; C09J103/02; C08; C08L; C08L2666/00; C08L2666/02; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1007; Y10T156/1016; Y10T156/1025
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
86 words
A method of making multiwall thickness corrugated board at high speeds comprising the steps of (a) preparing a water resistant adhesive mix having a gelatinized modified waxy starch in the carrier portion and raw starch as a bonding agent, said modified waxy starch having an alkali fluidity of 25 to about 90 mls at 25° C measured with a 5 gram sample, (b) applying said mix to a corrugator, and (c) forming a multiwall board on said corrugator at a higher than normal rate of speed.
Claim 2
Independent Claim
86 words
A method of making multiwall thickness corrugated board at high speeds comprising the steps of (a) preparing a water resistant adhesive mix having a gelatinized modified waxy starch in the carrier portion and raw starch as a bonding agent, said modified waxy starch having an alkali fluidity of 25 to about 90 mls at 25° C measured with a 5 gram sample, (b) applying said mix to a corrugator, and (c) forming a multiwall board on said corrugator at a higher than normal rate of speed.
Claim 3
Dependent Claim
21 words
The method of claim 1 wherein the waxy starch constitutes about 25% to 100% of the starch in the carrier portion.
Claim 4
Independent Claim
198 words
A method of making multiwall thickness corrugated board at high speeds comprising the steps of I. preparing a water resistant adhesive mix which comprises: (a) about 3% to about 12% gelatinized starch solids of which about 25% to 100% is waxy starch modified to increase the fluidity thereof to the range of 25 to about 90 mls. measured at 25° C., (b) about 10% to about 35% raw starch solids, (c) about 0.1% to about 1.0% NaOH, (d) about 1% to about 20% of a water resistant material by weight of the starch, and (e) about 60% to about 85.9% water, said percent being by weight based on the final adhesive mix, the amount of gelatinized starch solids being such as to provide an increased amount of cooked starch solids as compared with conventional corrugating adhesives, the viscosity of said adhesive being 16 to 120 seconds on the brass cup at 105° F., and the waxy starch being modified to allow said increased amount of cooked solids while retaining the viscosity of the adhesive, Ii. applying said mix to a corrugator, and Iii. forming a multiwall board on said corrugator at a higher than normal rate of speed.
Claim 5
Independent Claim
198 words
A method of making multiwall thickness corrugated board at high speeds comprising the steps of I. preparing a water resistant adhesive mix which comprises: (a) about 3% to about 12% gelatinized starch solids of which about 25% to 100% is waxy starch modified to increase the fluidity thereof to the range of 25 to about 90 mls. measured at 25° C., (b) about 10% to about 35% raw starch solids, (c) about 0.1% to about 1.0% NaOH, (d) about 1% to about 20% of a water resistant material by weight of the starch, and (e) about 60% to about 85.9% water, said percent being by weight based on the final adhesive mix, the amount of gelatinized starch solids being such as to provide an increased amount of cooked starch solids as compared with conventional corrugating adhesives, the viscosity of said adhesive being 16 to 120 seconds on the brass cup at 105° F., and the waxy starch being modified to allow said increased amount of cooked solids while retaining the viscosity of the adhesive, Ii. applying said mix to a corrugator, and Iii. forming a multiwall board on said corrugator at a higher than normal rate of speed.
Claim 6
Dependent Claim
15 words
The method of claim 3 in which about 0.1% to about 1.0% borax is present.
Claim 7
Dependent Claim
15 words
The method of claim 3 having about 10% to about 40% total solids by weight.
Claim 8
Dependent Claim
33 words
The method of claim 3 wherein the waxy starch has a solubility of 0.1 to 100% at 77° F., an inherent viscosity of 0.1 to 2 deciliter/gram at 0.5% concentration at 77° F.
Claim 9
Dependent Claim
50 words
The method of claim 3 wherein the water resistant material is selected from the group consisting of urea-formaldehyde resin, resorcinol-formaldehyde resin, phenol-aldehyde resin, mixtures thereof, urea with formaldehyde, resorcinol with formaldehyde, calcium cyanamide with formaldehyde, a phenolic compound with an aldehyde compound, and a phenolic compound with an oxazolidine compound.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-25 | 1982-03-27 | 1982-09-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-25 | 1986-03-27 | 1986-09-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-25 | 1990-03-27 | 1990-09-26 | $7700.00 | Window Closed / Lapsed |