Induction heating method of steel pipe
Assignee: Nippon Steel Corp
•
Filing: 1977-05-31
•
Granted: 1978-09-19
•
Expires: 1997-05-31
Abstract
Abstract A method for heating steel pipe for induction heating coils, while the pipe is travelling through said coils in the axial direction, which comprises:
Inventors
- 👤 Katsuhiko Narihara
- 👤 Hajime Nakasugi
- 👤 Masanobu Yamaguchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 04:59
CPC Classifications
C; C21; C21D; C21D9/00; C21D9/08
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
203 words
A method for heating steel pipe by induction heating coils, while the pipe is travelling through said coils in the axial direction, which comprises: (a) calculating the limit absorption electric power density Po (W/cm 2 ) by the following formula: Po = 1/40 × T × √d wherein T = heating temperature (° C.) and d = wall thickness (mm); (b) attaching a power supply of low frequency to the induction heating coils; (c) setting said power supply for maximum capacity to be impressed on said induction heating coils, and (d) heating the steel pipe as it is travelling through said induction heating coils heated by said power supply, at such speed as to permit the steel pipe to be heated to the desired temperature, and heating the steel pipe with the set power if the absorption electric power density P by the set power is P ≧ Po, and heating the steel pipe by shortening the effective length of the induction heating coils to obtain P ≧ Po if P < Po; thereby causing the difference in the temperature between the ends and the central portion of the steel pipe in the axial direction to be no greater than about 20° C.
Claim 2
Independent Claim
203 words
A method for heating steel pipe by induction heating coils, while the pipe is travelling through said coils in the axial direction, which comprises: (a) calculating the limit absorption electric power density Po (W/cm 2 ) by the following formula: Po = 1/40 × T × √d wherein T = heating temperature (° C.) and d = wall thickness (mm); (b) attaching a power supply of low frequency to the induction heating coils; (c) setting said power supply for maximum capacity to be impressed on said induction heating coils, and (d) heating the steel pipe as it is travelling through said induction heating coils heated by said power supply, at such speed as to permit the steel pipe to be heated to the desired temperature, and heating the steel pipe with the set power if the absorption electric power density P by the set power is P ≧ Po, and heating the steel pipe by shortening the effective length of the induction heating coils to obtain P ≧ Po if P < Po; thereby causing the difference in the temperature between the ends and the central portion of the steel pipe in the axial direction to be no greater than about 20° C.
Claim 3
Dependent Claim
26 words
A method as defined in the claim 1 in which heating of the steel pipe by the induction coil is performed in 2 to 10 minutes.
Claim 4
Dependent Claim
20 words
A method as defined in the claim 1 in which the absorption electric density is below 150 w/cm 2 .
References Cited (Backward Citations)
US3610861A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-18 | 1982-03-20 | 1982-09-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-18 | 1986-03-20 | 1986-09-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-18 | 1990-03-20 | 1990-09-19 | $7700.00 | Window Closed / Lapsed |