Process of coating aluminum materials molded by extrusion with polysiloxane coating
Assignee: Toa Paint Co Ltd
•
Filing: 1977-03-23
•
Granted: 1978-09-19
•
Expires: 1997-03-23
Abstract
Abstract Shaped aluminum bars fresh from an extruder machine are coated with a specific organopolysiloxane composition while remaining uncooled and staying at temperatures not lower than about 250 DEG C, or at a temperature between about 550 DEG and 250 DEG C. The thus coated aluminum bars are then, preferably, subjected to annealing. The coatings formed on the surfaces of the aluminum materials have a superior resistance to attack by chemicals, weather, stains and heat as well as excellent adhesion and mechanical properties.
Inventors
- 👤 Mutsuo Hasegawa
- 👤 Sunichi Segawa
- 👤 Yuji Koise
- 👤 Hisao Okada
- 👤 Shiro Gomyo
- 👤 Yoshiaki Kudo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 19:34
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/14; B21; B21C; B21C23/00; B21C23/009; C; C09; C09D; C09D183/00; C09D183/04; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/4998; Y10T29/49982; Y10T29/49984; Y10T29/49988
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
158 words
A process for providing protective coatings on the surface of a material composed of aluminum or an aluminum-based alloy molded by extrusion which comprises extruding said material; coating said material while its surface temperature is maintained between 550° and 250° C. following extrusion with an organopolysiloxane composition comprising (a) from 100 to 15 parts by weight of an organopolysiloxane expressed by the average unit formula ##EQU2## where R 1 is the same or different monovalent hydrocarbon group and a is a positive number in the range from 1.10 to 1.90 inclusive, and (b) from 0 to 85 parts by weight of a diorganopolysiloxane represented by the general formula ##STR2## where R 2 is the same or different monovalent hydrocarbon group, A is a group selected from the class consisting of monovalent hydrocarbon groups, alkoxy groups and a hydroxy group and n is a positive integer, and having a viscosity of from 100 to 1,000,000 centistokes at 25° C.
Claim 2
Dependent Claim
158 words
A process for providing protective coatings on the surface of a material composed of aluminum or an aluminum-based alloy molded by extrusion which comprises extruding said material; coating said material while its surface temperature is maintained between 550° and 250° C. following extrusion with an organopolysiloxane composition comprising (a) from 100 to 15 parts by weight of an organopolysiloxane expressed by the average unit formula ##EQU2## where R 1 is the same or different monovalent hydrocarbon group and a is a positive number in the range from 1.10 to 1.90 inclusive, and (b) from 0 to 85 parts by weight of a diorganopolysiloxane represented by the general formula ##STR2## where R 2 is the same or different monovalent hydrocarbon group, A is a group selected from the class consisting of monovalent hydrocarbon groups, alkoxy groups and a hydroxy group and n is a positive integer, and having a viscosity of from 100 to 1,000,000 centistokes at 25° C.
Claim 3
Dependent Claim
23 words
The method as claimed in claim 1, wherein said material is extruded at a temperature in the range from 500° to 580° C.
Claim 4
Dependent Claim
23 words
The method as claimed in claim 1, wherein said material is coated while its surface temperature is staying between 550° to 350° C.
Claim 5
Dependent Claim
35 words
The method as claimed in claim 1, wherein said organopolysiloxane composition is composed of from 70 to 15 parts by weight of component (a) and from 30 to 85 parts by weight of component (b).
Claim 6
Dependent Claim
29 words
The method as claimed in claim 1, wherein the monovalent hydrocarbon group represented by symbol R 1 is selected from the class consisting of methyl, phenyl and vinyl groups.
Claim 7
Dependent Claim
44 words
The method as claimed in claim 5, wherein from 30 to 80 mole %, from 5 to 70 mole % and from 0 to 30 mole % of the monovalent hydrocarbon groups represented by symbol R 1 are methyl, phenyl and vinyl groups, respectively.
Claim 8
Dependent Claim
15 words
The method as claimed in claim 1, wherein component (a) is liquid at room temperature.
Claim 9
Dependent Claim
26 words
The method as claimed in claim 1, wherein the group represented by symbol A is selected from the class consisting of methyl, phenyl and vinyl groups.
Claim 10
Dependent Claim
29 words
The method as claimed in claim 1, wherein the monovalent hydrocarbon group represented by symbol R 2 is selected from the class consisting of methyl, phenyl and vinyl groups.
Claim 11
Dependent Claim
44 words
The method as claimed in claim 9, wherein from 10 to 80 mole %, from 10 to 90 mole % and from 5 to 30 mole % of the monovalent hydrocarbon groups represented by symbol R 2 are methyl, phenyl and vinyl groups, respectively.
Claim 12
Dependent Claim
185 words
A process for providing protective coatings on the surface of a material composed of aluminum or an aluminum-based alloy molded by extrusion which comprises (i) coating said material while its surface temperature is maintained between 550° and 250° C. following extrusion with an organopolysiloxane composition comprising (a) from 100 to 15 parts by weight of an organopolysiloxane expressed by the average unit formula ##EQU3## where R 1 is the same or different monovalent hydrocarbon group and a is a positive number in the range from 1.10 to 1.90 inclusive, and (b) from 0 to 85 parts by weight of a diorganopolysiloxane represented by the general formula ##STR3## where R 2 is the same or different monovalent hydrocarbon group, A is a group selected from the class consisting of monovalent hydrocarbon groups, alkoxy groups and a hydroxy group and n is a positive integer, and having a viscosity of from 100 to 1,000,000 centistokes at 25° C., and (ii) subjecting the thus coated material composed of aluminum or an aluminum-based alloy to annealing at a temperature from 170° to 200° C. for 2 to 6 hours.
Claim 13
Dependent Claim
185 words
A process for providing protective coatings on the surface of a material composed of aluminum or an aluminum-based alloy molded by extrusion which comprises (i) coating said material while its surface temperature is maintained between 550° and 250° C. following extrusion with an organopolysiloxane composition comprising (a) from 100 to 15 parts by weight of an organopolysiloxane expressed by the average unit formula ##EQU3## where R 1 is the same or different monovalent hydrocarbon group and a is a positive number in the range from 1.10 to 1.90 inclusive, and (b) from 0 to 85 parts by weight of a diorganopolysiloxane represented by the general formula ##STR3## where R 2 is the same or different monovalent hydrocarbon group, A is a group selected from the class consisting of monovalent hydrocarbon groups, alkoxy groups and a hydroxy group and n is a positive integer, and having a viscosity of from 100 to 1,000,000 centistokes at 25° C., and (ii) subjecting the thus coated material composed of aluminum or an aluminum-based alloy to annealing at a temperature from 170° to 200° C. for 2 to 6 hours.
References Cited (Backward Citations)
US3061467A
Cited
US2871141A
Cited
US2991204A
Cited
US3455732A
Cited
DE1540632A1
Cited
US3532537A
Cited
US3560244A
Cited
US3899370A
Cited
US3935349A
Cited
US4039355A
Cited
DE2519132A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-18 | 1982-03-20 | 1982-09-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-18 | 1986-03-20 | 1986-09-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-18 | 1990-03-20 | 1990-09-19 | $7700.00 | Window Closed / Lapsed |