US4115178A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of making glued, laminated assemblies in prepressed and final pressed stages
Assignee: Pacific Adhesives Co Inc
•
Filing: 1977-05-19
•
Granted: 1978-09-19
•
Expires: 1997-05-19
Abstract
Abstract Plywood and other glued, laminated assemblies are made by spreading a liquid foamed glue on a surface of a first lamina. A second lamina is superimposed and, while the glue is in a fluid condition, the resulting assembly is prepressed under pressure sufficient to spread the glue and to wet and unite the opposed faces of the laminae. This forms a flat, self-sustaining intermediate laminate which thereafter may be pressed further to develop the glue bond between the laminae.
Inventors
- 👤 Charles N. Cone
- 👤 Julius M. Steinberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 11:54
CPC Classifications
B; B32; B32B; B32B21/00; B32B21/14; B27; B27D; B27D1/00; B27D1/04; B27G; B27G11/00; B32B21/13; B32B37/00; B32B37/10; B32B37/1027; C; C09; C09J; C09J5/00; C09J5/08; B32B2307/00; B32B2307/50; B32B2307/542; B32B2309/00; B32B2309/02; B32B2309/025; B32B2309/12; B32B2309/125; B32B2607/00
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
217 words
The method of making plywood which comprises: (a) extruding on a surface of a first wood veneer a plywood glue comprising a member of the class consisting of the thermosetting phenol-formaldehyde resin glues, the resorcinol-formaldehyde resin glues, the cresol-formaldehyde resin glues, and the urea-formaldehyde resin glues, (b) superimposing a second veneer on the glue-spread surface of the first veneer, (c) the glue being extruded on the first veneer in the form of spaced filaments of foamed liquid glue having a density of from 0.1 to 0.5, (d) the veneer surface between the filaments being substantially unwetted by the glue, (e) the spacing of the filaments and the glue usage being predetermined to insure substantially complete coverage and wetting of both veneers with foamed liquid glue upon the application of prepressing pressure, (f) promptly prepressing the assembled veneers at a pressure and for a time only substantially sufficient to spread the filaments and wet the veneers with a veneer-separating layer of unset glue still in foamed condition, thereby tacking the veneers together for preliminary handling, and (g) thereafter further pressing the assembled and prepressed veneers at a temperature and for a time sufficient to break the foam structure of the foamed thermosetting glue, to press the veneers together, and to set the glue to its final bonding condition.
Claim 2
Independent Claim
217 words
The method of making plywood which comprises: (a) extruding on a surface of a first wood veneer a plywood glue comprising a member of the class consisting of the thermosetting phenol-formaldehyde resin glues, the resorcinol-formaldehyde resin glues, the cresol-formaldehyde resin glues, and the urea-formaldehyde resin glues, (b) superimposing a second veneer on the glue-spread surface of the first veneer, (c) the glue being extruded on the first veneer in the form of spaced filaments of foamed liquid glue having a density of from 0.1 to 0.5, (d) the veneer surface between the filaments being substantially unwetted by the glue, (e) the spacing of the filaments and the glue usage being predetermined to insure substantially complete coverage and wetting of both veneers with foamed liquid glue upon the application of prepressing pressure, (f) promptly prepressing the assembled veneers at a pressure and for a time only substantially sufficient to spread the filaments and wet the veneers with a veneer-separating layer of unset glue still in foamed condition, thereby tacking the veneers together for preliminary handling, and (g) thereafter further pressing the assembled and prepressed veneers at a temperature and for a time sufficient to break the foam structure of the foamed thermosetting glue, to press the veneers together, and to set the glue to its final bonding condition.
Claim 3
Dependent Claim
14 words
The method of claim 1 wherein the glue comprises a thermosetting phenol-formaldehyde resin glue.
Claim 4
Dependent Claim
16 words
The method of claim 1 wherein the glue comprises a phenol-formaldehyde resin-dried animal blood, plywood glue.
Claim 5
Dependent Claim
20 words
The method of claim 1 wherein the filaments of foamed liquid glue have a density of from 0.15 to 0.3.
Claim 6
Dependent Claim
33 words
The method of claim 1 wherein the filaments are substantially round and have a diameter of from 1/64 to 3/8 inch and a spacing on the veneer of from 1/8 to 1/2 inch.
Claim 7
Dependent Claim
29 words
The method of claim 1 wherein the assembled veneers are prepressed with a press roll at a pressure of from 60 to 90 pounds per lineal foot of roll.
Claim 8
Dependent Claim
26 words
The method of claim 1 wherein the assembled veneers are prepressed at about 28 p.s.i. and ambient temperature for a press time of about 1 second.
Claim 9
Dependent Claim
21 words
The method of claim 1 wherein the veneer-separating layer of unset glue still in foamed condition is about 3/100 inch thick.
Claim 10
Dependent Claim
27 words
The method of claim 1 wherein the prepressed veneers are further pressed at about 175 p.s.i. and about 300° F. for a time of about 53/4 minutes.
Claim 11
Independent Claim
204 words
The method of making plywood which comprises: (a) spreading a thermosetting phenol-formaldehyde resin glue on the surface of a first wood veneer, (b) superimposing a second veneer on the glue-spread surface of the first veneer, (c) the glue being spread on the first veneer in the form of filaments of foamed liquid glue having a density from 0.1 to 0.5, the filaments having a diameter of from 1/64 to 3/8 inch and a lateral spacing on the veneers of from 1/8 to 1/2 inch, thereby insuring substantially complete coverage and wetting of both veneers with foamed liquid glue upon the application of prepressing pressure, (d) promptly prepressing the assembled veneers at about 28 p.s.i. and ambient temperature for a time sufficient to spread the filaments and wet the veneers with a veneer-separating layer about 3/100 inches thick of unset glue still in foamed condition, thereby tacking the veneers together for preliminary handling, and (e) thereafter pressing the assembled and prepressed veneers at a pressure of about 175 p.s.i. and a temperature of about 300° F., for a time sufficient to break the foam structure of the foamed glue, to press the veneers together, and to set the thermosetting glue to its final bonding condition.
Claim 12
Independent Claim
204 words
The method of making plywood which comprises: (a) spreading a thermosetting phenol-formaldehyde resin glue on the surface of a first wood veneer, (b) superimposing a second veneer on the glue-spread surface of the first veneer, (c) the glue being spread on the first veneer in the form of filaments of foamed liquid glue having a density from 0.1 to 0.5, the filaments having a diameter of from 1/64 to 3/8 inch and a lateral spacing on the veneers of from 1/8 to 1/2 inch, thereby insuring substantially complete coverage and wetting of both veneers with foamed liquid glue upon the application of prepressing pressure, (d) promptly prepressing the assembled veneers at about 28 p.s.i. and ambient temperature for a time sufficient to spread the filaments and wet the veneers with a veneer-separating layer about 3/100 inches thick of unset glue still in foamed condition, thereby tacking the veneers together for preliminary handling, and (e) thereafter pressing the assembled and prepressed veneers at a pressure of about 175 p.s.i. and a temperature of about 300° F., for a time sufficient to break the foam structure of the foamed glue, to press the veneers together, and to set the thermosetting glue to its final bonding condition.
References Cited (Backward Citations)
US2205600A
Cited
US2290548A
Cited
US2872965A
Cited
US3578543A
Cited
US3706619A
Cited
US3895984A
Cited
US3829338A
Cited
US3929695A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-18 | 1982-03-20 | 1982-09-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-18 | 1986-03-20 | 1986-09-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-18 | 1990-03-20 | 1990-09-19 | $7700.00 | Window Closed / Lapsed |