Polymeric films peelably adhered to a pressure-sensitive adhesive photographic element
Assignee: Eastman Kodak Co
•
Filing: 1977-05-09
•
Granted: 1978-09-19
•
Expires: 1997-05-09
Abstract
Abstract A photograpic element having a pressure-sensitive adhesive layer for mounting of the element as desired, is protected by an ethylene polymer layer having a defined melt index and applied thereto by extrusion, with or without included antioxidant, at temperatures above 450° F. As a consequence of the defined extrusion conditions, the protective ethylene polymer layer can be applied to form the element at high line speeds, and, when subsequently desired, peeled from the adhesive layer to which it is adhered by a force not exceeding 400 grams as defined. Ethylene polymers that are employed include polyethylene, and copolymers of ethylene with other monomers.
Inventors
- 👤 Doyle O. Etter
- 👤 Irvin H. Crawford
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 12:39
CPC Classifications
G; G03; G03C; G03C11/00; G03C11/14; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31855; Y10T428/31931
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
144 words
A photographic element comprising a paper support, an imaging layer on one surface of said support, a pressure-sensitive adhesive layer bonded to the opposite surface of said support, and a layer of an ethylene polymer peelably adhered to said adhesive layer, said polymer layer having been formed by extruding molten ethylene polymer having a melt index in the range from about 3 to 14 and a temperature above 450° F onto said adhesive layer on said support, the bond strength between said polymer layer and said pressure-sensitive adhesive layer being such that a force not exceeding 400 grams will peel a strip of said polymer layer 1/2 inches wide and at least 10 inches long from said adhesive layer at room temperature at a rate of 10 inches per minute after said element is room temperature aged for at least 15 days after extrusion.
Claim 2
Dependent Claim
144 words
A photographic element comprising a paper support, an imaging layer on one surface of said support, a pressure-sensitive adhesive layer bonded to the opposite surface of said support, and a layer of an ethylene polymer peelably adhered to said adhesive layer, said polymer layer having been formed by extruding molten ethylene polymer having a melt index in the range from about 3 to 14 and a temperature above 450° F onto said adhesive layer on said support, the bond strength between said polymer layer and said pressure-sensitive adhesive layer being such that a force not exceeding 400 grams will peel a strip of said polymer layer 1/2 inches wide and at least 10 inches long from said adhesive layer at room temperature at a rate of 10 inches per minute after said element is room temperature aged for at least 15 days after extrusion.
Claim 3
Dependent Claim
21 words
A photographic element as described in claim 1 wherein said temperature is in the range from about 490° to 600° F.
Claim 4
Dependent Claim
16 words
A photographic element as described in claim 2 wherein said ethylene polymer additionally comprises an antioxidant.
Claim 5
Dependent Claim
37 words
A photographic element as described in claim 3 wherein said antioxidant is a phenol, bisphenol, or dialkyl phenol sulfide at a concentration in the range from about 0.2 to about 1 percent by weight of ethylene polymer.
Claim 6
Dependent Claim
27 words
A photographic element as described in claim 4 wherein said antioxidant is octadecyl-3-(3',5'-di-tert-butyl-4'-hydroxyphenyl)propionate and said temperature is in the range from about 575° to about 600° F.
Claim 7
Dependent Claim
46 words
A photographic element as described in claim 1 wherein said ethylene polymer is polyethylene having a melt index in the range from about 6 to 12 and said bond strength is such that a force not exceeding 200 grams will peel said polymer layer as described.
Claim 8
Dependent Claim
30 words
A photographic element as described in claim 6 wherein said melt index is about 7.5 and said extrusion temperature is in the range from about 490° to about 540° F.
Claim 9
Dependent Claim
19 words
A photographic element as in claim 1 wherein said ethylene polymer layer has a thickness less than 1 mil.
References Cited (Backward Citations)
US3135608A
Cited
US3411908A
Cited
US3359107A
Cited
GB1101608A
Cited
US3582337A
Cited
JPS5220014A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-18 | 1982-03-20 | 1982-09-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-18 | 1986-03-20 | 1986-09-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-18 | 1990-03-20 | 1990-09-19 | $7700.00 | Window Closed / Lapsed |