US4115077A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of continuously producing resinoid abrasive wheels for cutting hard materials
Assignee: Individual
•
Filing: 1977-07-01
•
Granted: 1978-09-19
•
Expires: 1997-07-01
Abstract
Abstract Resinoid abrasive wheels are continuously produced by preparing pore forming granules having predetermined mechanical strength and containing a substance thermally decomposable at a baking temperature for the production of resinoid abrasive wheels, kneading together the pore forming granules, abrasive grins, a binder, a glass fiber reinforcement and a filler to prepare an abrasive composition, molding the abrasive composition into a block, heating the block by a high frequency heater, rolling the heated block into a sheet by rolls, blanking out circular pieces from the sheet, and baking the circular pieces of the uncured abrasive composition containing the pore forming granules uniformly dispersed therein to cure the binder and form pores by the decomposition of at least part of the thermally decomposable substance contained in the granules, whereby resinoid abrasive wheels having pores uniformly dispersed therein are obtained.
Inventors
- 👤 Heijiro Fukuda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 01:24
CPC Classifications
B; B24; B24D; B24D3/00; B24D3/02; B24D3/20; B24D3/28; B24D3/32; B24D18/00
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
137 words
A method of continuously producing a resinoid abrasive wheel for cutting hard materials comprising the steps of preparing pore forming granules having predetermined mechanical strength and containing a substance thermally decomposable at a baking temperature for the production of the resinoid wheel, kneading the pore forming granules with abrasive grains and a thermosetting synthetic resin binder to prepare an abrasive composition, molding the abrasive composition into a block, heating the block by a high frequency heater, rolling the heated block containing the pore forming granules into a sheet by a multiplicity of pairs of rolls, blanking out a circular piece from the rolled sheet, and baking the circular piece to cure the binder and form pores in the resulting abrasive wheel by the decomposition of at least part of the thermally decomposable substance contained in the granules.
Claim 2
Independent Claim
137 words
A method of continuously producing a resinoid abrasive wheel for cutting hard materials comprising the steps of preparing pore forming granules having predetermined mechanical strength and containing a substance thermally decomposable at a baking temperature for the production of the resinoid wheel, kneading the pore forming granules with abrasive grains and a thermosetting synthetic resin binder to prepare an abrasive composition, molding the abrasive composition into a block, heating the block by a high frequency heater, rolling the heated block containing the pore forming granules into a sheet by a multiplicity of pairs of rolls, blanking out a circular piece from the rolled sheet, and baking the circular piece to cure the binder and form pores in the resulting abrasive wheel by the decomposition of at least part of the thermally decomposable substance contained in the granules.
Claim 3
Dependent Claim
34 words
A method as defined in claim 1 wherein the pore forming granules are composed mainly of a substance thermally decomposable at an abrasive composition baking temperature of 180° to 220° C. and an aggregate.
Claim 4
Dependent Claim
49 words
A method as defined in claim 2 wherein the thermally decomposable substance is an organic substance selected from the group consisting of starch and funori, and the aggregate is an inorganic material comprising glass fiber particles 5 to 15 μ in diameter and 0.1 to 1 mm in length.
Claim 5
Dependent Claim
35 words
A method as defined in claim 2 wherein the pore forming granules are composed mainly of 1 to 3 parts by weight of the thermally decomposable substance and 1 parts by weight of the aggregate.
Claim 6
Dependent Claim
66 words
A method as defined in claim 1 wherein in the step of preparing the pore forming granules the granules are prepared by mixing together the thermally decomposable substance and an aggregate of glass fiber particles surface-treated with a dilute solution of a thermosetting resin, kneading the mixture with a suitable amount of water, granulating the kneaded mixture by a granulating machine, and drying the resulting granules.
Claim 7
Dependent Claim
22 words
A method as defined in claim 1 wherein the pore forming granules are substantially spherical and 1.2 to 1.5 mm in diameter.
Claim 8
Dependent Claim
34 words
A method as defined in claim 1 wherein the pore forming granules have mechanical strength sufficient to withstand external pressure involved in the block molding step and external pressure involved in the rolling step.
Claim 9
Dependent Claim
62 words
A method as defined in claim 1 wherein the abrasive grains are made of at least one material selected from the group consisting of silicon carbide, alumina and siliceous sand and are 16 to 220 mesh in size, and the binder is at least one thermosetting synthetic resin selected from the group consisting of phenolic resin, epoxy resin and diallyl phthalate resin.
Claim 10
Dependent Claim
37 words
A method as defined in claim 1 wherein at least one filler selected from the group consisting of cryolite iron disulfide, red iron oxide and clay is further incorporated into the abrasive composition in the kneading step.
Claim 11
Dependent Claim
70 words
A method as defined in claim 1 wherein 60 to 90 weight parts of the abrasive grains, 10 to 30 parts by weight of the binder, 0 to 20 parts by weight of a filler and the pore forming granules are kneaded together in the kneading step, the amount of the pore forming granules being 3 to 20 parts by weight per 100 parts by weight of the abrasive grains.
Claim 12
Dependent Claim
23 words
A method as defined in claim 1 wherein a glass fiber reinforcement is further incorporated into the abrasive composition in the kneading step.
Claim 13
Dependent Claim
34 words
A method as defined in claim 11 wherein 4 to 10 parts by weight of the glass fiber reinforcement is incorporated into the abrasive composition per 100 parts by weight of the abrasive grains.
Claim 14
Dependent Claim
40 words
A method as defined in claim 11 wherein the glass fiber reinforcement incorporated into the abrasive composition in the kneading step is chopped strands of glass fibers 10 to 15 μ in diameter and 5 to 15 mm in length.
References Cited (Backward Citations)
US3529945A
Cited
US2958593A
Cited
US3474048A
Cited
US4038047A
Cited
US3950148A
Cited
US3950149A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-18 | 1982-03-20 | 1982-09-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-18 | 1986-03-20 | 1986-09-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-18 | 1990-03-20 | 1990-09-19 | $7700.00 | Window Closed / Lapsed |