Laminated three-layer resinoid wheels having core layer of reinforcing material and method for producing same
Assignee: Individual
•
Filing: 1974-08-01
•
Granted: 1976-04-13
•
Expires: 1994-08-01
Abstract
Abstract Laminated three-layer resinoid wheels having a core layer of reinforcing material are continuously produced by placing into a die a resinoid abrasive composition and a sheet of reinforcing material having a binder previously deposited thereon, with the reinforcing sheet interposed between layers of the abrasive composition, molding the mass of layers into a block, heating the block by a high frequency heater, passing the heated block through multiple pairs of rolls to roll the block into a sheet, blanking out circular pieces from the rolled sheet and baking the circular pieces.
Inventors
- 👤 Heijiro Fukuda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 10:00
CPC Classifications
B; B24; B24D; B24D18/00
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
275 words
A method for the continuous production of a laminated three-layer resin-bonded abrasive wheel having a core layer of reinforcing material, comprising the steps of: a. preparing a moldable resinous abrasive composition by admixing abrasive grains having a mesh size in the range of about 16 to 220 mesh, with an uncured thermosetting synthetic resin binder therefor, in the proportion of about 60 to 90 parts by weight of abrasive grains to about 10 to 20 parts by weight of said binder; b. placing a specified amount of said abrasive composition into a die in the form of a thin layer; c. placing over said layer a sheet of a glass reinforcing material having said binder previously deposited thereon to form a reinforcing core to a total thickness between about 0.4 and 4.5 mm; d. placing a specified amount of said resinous abrasive composition upon said reinforcing layer to form a three-layer mass; e. molding said three-layer mass at a temperature of about 70° to 90°C at a pressure of about 80 to 140 kg/cm 2 for 20 to 60 seconds to form a molded block of laminated abrasive composition having a thickness of about 25 to 40 mm; f. heating said molded block by high frequency wave energy heating at a temperature of about 40° to 75°C for about 15 to 25 seconds; g. rolling said block by multiple rolling to a resin-binded laminated sheetblank having a thickness of 1 to 15 mm; h. blanking out a circular piece from said sheet; and i. baking said circular piece at a temperature from room temperature to 180°C for a period of about 20 to 30 hours.
Claim 2
Independent Claim
275 words
A method for the continuous production of a laminated three-layer resin-bonded abrasive wheel having a core layer of reinforcing material, comprising the steps of: a. preparing a moldable resinous abrasive composition by admixing abrasive grains having a mesh size in the range of about 16 to 220 mesh, with an uncured thermosetting synthetic resin binder therefor, in the proportion of about 60 to 90 parts by weight of abrasive grains to about 10 to 20 parts by weight of said binder; b. placing a specified amount of said abrasive composition into a die in the form of a thin layer; c. placing over said layer a sheet of a glass reinforcing material having said binder previously deposited thereon to form a reinforcing core to a total thickness between about 0.4 and 4.5 mm; d. placing a specified amount of said resinous abrasive composition upon said reinforcing layer to form a three-layer mass; e. molding said three-layer mass at a temperature of about 70° to 90°C at a pressure of about 80 to 140 kg/cm 2 for 20 to 60 seconds to form a molded block of laminated abrasive composition having a thickness of about 25 to 40 mm; f. heating said molded block by high frequency wave energy heating at a temperature of about 40° to 75°C for about 15 to 25 seconds; g. rolling said block by multiple rolling to a resin-binded laminated sheetblank having a thickness of 1 to 15 mm; h. blanking out a circular piece from said sheet; and i. baking said circular piece at a temperature from room temperature to 180°C for a period of about 20 to 30 hours.
Claim 3
Dependent Claim
64 words
The method as set forth in claim 1 wherein the sheet of glass reinforcing material is selected from the group consisting of glass cloth, glass mat and glass fiber net and has a thickness of 0.4 to 0.9 mm, at least one reinforcing sheet being interposed between the abrasive layers in the form of a layer having a thickness of 0.4 to 4.5 mm.
Claim 4
Dependent Claim
34 words
The method as set forth in claim 1 wherein at least one filler selected from the group consisting of creolite, iron disulfide, red iron oxide and clay is further incorporated into the abrasive composition.
Claim 5
Dependent Claim
42 words
The method as set forth in claim 1 wherein the abrasive composition comprises 60 to 90 parts by weight of the abrasive grains, 10 to 20 parts by weight of the binder and 0 to 20 parts by weight of the filler.
Claim 6
Dependent Claim
33 words
The method as set forth in claim 4 wherein the sheet of abrasive composition is eventually rough-surfaced on its front and rear surfaces by the terminal unit of rolls during the rolling step.
Claim 7
Dependent Claim
13 words
A laminated three-layer resin-bonded abrasive wheel made by the method of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-04-13 | 1979-10-13 | 1980-04-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-04-13 | 1983-10-13 | 1984-04-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-04-13 | 1987-10-13 | 1988-04-13 | $7700.00 | Window Closed / Lapsed |