Shell sand with improved thermal shock resistance
Assignee: Hexion Inc
•
Filing: 1976-06-09
•
Granted: 1978-09-12
•
Expires: 1996-06-09
Abstract
Abstract A resin coated sand comprising: (a) particles of sand coated with from about 1% to about 8% by weight sand of phenol-formaldehyde morolak resin; (b) a curing agent; and (c) from about 2% to about 50% by weight of phenol-formaldehyde morolak resin of an epoxy and/or phenoxy resin. The resin coated sands of the present invention provide improved thermal shock resistance without creating smoke and odor problems. In addition, the resin coated sands of the invention can be formed into foundry articles that possess good tensile strength.
Inventors
- 👤 Robert Simpson Craig
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 05:02
CPC Classifications
B; B22; B22C; B22C1/00; B22C1/16; B22C1/20; B22C1/22; B22C1/2233; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2998
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
54 words
A resin coated sand comprising: (a) particles of sand coated with from about 1 to about 8% by weight of the sand, of a phenol-formaldehyde novolak resin; (b) a curing agent; and (c) from about 2 to about 50%, based upon the weight of the phenol-formaldehyde novolak resin, of an epoxy and/or phenoxy resin.
Claim 2
Dependent Claim
54 words
A resin coated sand comprising: (a) particles of sand coated with from about 1 to about 8% by weight of the sand, of a phenol-formaldehyde novolak resin; (b) a curing agent; and (c) from about 2 to about 50%, based upon the weight of the phenol-formaldehyde novolak resin, of an epoxy and/or phenoxy resin.
Claim 3
Dependent Claim
33 words
The resin coated sand of claim 1, wherein said epoxy and/or phenoxy resin is present in amounts ranging from about 5 to about 25% based on the weight of the phenol-formaldehyde novolak resin.
Claim 4
Dependent Claim
29 words
The resin coated sand of claim 1, wherein the phenol-formaldehyde novolak resin is present in amounts ranging from about 1 to about 6% by weight based on the sand.
Claim 5
Dependent Claim
18 words
The resin coated sand in accordance with claim 1, wherein an epoxy resin is employed in the composition.
Claim 6
Dependent Claim
33 words
The resin coated sand of claim 4, wherein the epoxy resin is a reaction product of Bisphenol A and epichlorohydrin having molecular weight in the range of from about 340 to about 5,000.
Claim 7
Dependent Claim
153 words
A process for forming foundry cores and molds comprising the steps of: (1) contacting a hot pattern with a free-flowing resin coated sand comprising: (a) particles of sand coated with from about 1 to about 8%, by weight of the sand, of a phenol-formaldehyde novolak resin; (b) a curing agent; (c) from about 2 to about 50%, by weight of the phenol-formaldehyde novolak resin of an epoxy and/or phenoxy resin; (2) holding the resin coated sand against the hot pattern to bond a portion of the particles of resin coated sand together to form a foundry mold or core of suitable thickness; (3) removing bonded particles of resin coated sand from bonded particles of sand forming the foundry mold or core; (4) curing the foundry mold or core, the hot pattern having a temperature of from about 175° C. to 370° C. and (5) removing the foundry mold or core from the pattern.
Claim 8
Dependent Claim
153 words
A process for forming foundry cores and molds comprising the steps of: (1) contacting a hot pattern with a free-flowing resin coated sand comprising: (a) particles of sand coated with from about 1 to about 8%, by weight of the sand, of a phenol-formaldehyde novolak resin; (b) a curing agent; (c) from about 2 to about 50%, by weight of the phenol-formaldehyde novolak resin of an epoxy and/or phenoxy resin; (2) holding the resin coated sand against the hot pattern to bond a portion of the particles of resin coated sand together to form a foundry mold or core of suitable thickness; (3) removing bonded particles of resin coated sand from bonded particles of sand forming the foundry mold or core; (4) curing the foundry mold or core, the hot pattern having a temperature of from about 175° C. to 370° C. and (5) removing the foundry mold or core from the pattern.
Claim 9
Dependent Claim
23 words
The process in accordance with claim 6, wherein the temperature of the hot pattern is from about 200° C. to about 290° C.
Claim 10
Dependent Claim
12 words
The process in accordance with claim 6, wherein said pattern is metal.
Claim 11
Dependent Claim
29 words
The process in accordance with claim 6, wherein the phenol-formaldehyde novolak resin is present in amounts ranging from about 1 to about 6% by weight based on the sand.
Claim 12
Dependent Claim
42 words
The process in accordance with claim 6, wherein an epoxy resin is employed in the composition, said epoxy resin being the reaction product of Bisphenol A and epichlorohydrin having a molecular weight in the range of from about 340 to about 5,000.
Claim 13
Dependent Claim
59 words
A resinous-coated sand comprising: (a) particles of sand coated with from about 1 to about 8%, by weight of the sand, of a phenol-formaldehyde novolak resin; (b) a curing agent; (c) from about 2 to about 50%, by weight, based upon the weight of the phenol-formaldehyde novolak resin of an epoxy resin produced by reaction of bisphenol-A and epichlorohydrin.
Claim 14
Dependent Claim
59 words
A resinous-coated sand comprising: (a) particles of sand coated with from about 1 to about 8%, by weight of the sand, of a phenol-formaldehyde novolak resin; (b) a curing agent; (c) from about 2 to about 50%, by weight, based upon the weight of the phenol-formaldehyde novolak resin of an epoxy resin produced by reaction of bisphenol-A and epichlorohydrin.
References Cited (Backward Citations)
US3838095A
Cited
US3860561A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-11 | 1982-03-13 | 1982-09-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-11 | 1986-03-13 | 1986-09-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-11 | 1990-03-13 | 1990-09-12 | $7700.00 | Window Closed / Lapsed |