Fluid solventless epoxy-anhydride compositions containing metal acetylacetonate accelerators and organic carboxylic acid co-accelerators
Assignee: Teco Holdings USA Inc
•
Filing: 1977-03-03
•
Granted: 1978-09-12
•
Expires: 1997-03-03
Abstract
Abstract A resinous composition, suitable as a high voltage insulation for electrical members, is made from an admixture containing: 100 parts of an epoxy resin, about 25 to 200 parts of an acid anhydride reactive with the epoxy resin, about 0.01 to 2.0 parts of chromium or zirconium acetylacetonate, acting as a latent accelerator and about 0.3 to 30 parts of a selected organic carboxylic acid, acting as a co-accelerator.
Inventors
- 👤 James D. B. Smith
- 👤 Robert N. Kauffman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 08:08
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/40; C; C08; C08G; C08G59/00; C08G59/18; C08G59/68; C08G59/681; C08G59/685; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31529
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
236 words
A highly fluid, solventless, high voltage capability, resinous impregnating composition consisting essentially of the admixture of: (A) 100 parts by weight of a resin comprising: (1) a first epoxy resin consisting of a diglycidyl ether of an aliphatic diol; and (2) a second epoxy resin selected from the group consisting of bisphenol A epoxy resins, bisphenol F epoxy resins, novolac epoxy resins, glycidyl ester epoxy resins, hydantoin epoxy resins, cycloaliphatic epoxy resins and mixtures thereof, wherein the weight ratio of diglycidyl ether of an aliphatic diol:second epoxy resin is from about 1.0:0.0 to about 1.0:9.0, (B) about 25 parts to about 200 parts by weight of an organic carboxylic acid anhydride, (C) about 0.01 part to about 2.0 parts by weight of a metal acetylacetonate selected from the group consisting of chromium (III) acetylacetonate, zirconium (IV) acetylacetonate, and mixtures thereof, acting as a latent accelerator, and (D) about 0.3 to about 30 parts by weight of an organic carboxylic acid selected from the group consisting of acetic acid, propionic acid, butyric acid, isobutyric acid, valeric acid, caproic acid, heptanoic acid, caprylic acid, benzoic acid, toluic acids, chlorobenzoic acids, nitrobenzoic acids, succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, phthalic acid, isophthalic acid, terephthalic acid and mixtures thereof, acting as sole co-accelerator, wherein the resinous composition is highly fluid, having an initial viscosity of below about 350 cps. at 25° C.
Claim 2
Dependent Claim
236 words
A highly fluid, solventless, high voltage capability, resinous impregnating composition consisting essentially of the admixture of: (A) 100 parts by weight of a resin comprising: (1) a first epoxy resin consisting of a diglycidyl ether of an aliphatic diol; and (2) a second epoxy resin selected from the group consisting of bisphenol A epoxy resins, bisphenol F epoxy resins, novolac epoxy resins, glycidyl ester epoxy resins, hydantoin epoxy resins, cycloaliphatic epoxy resins and mixtures thereof, wherein the weight ratio of diglycidyl ether of an aliphatic diol:second epoxy resin is from about 1.0:0.0 to about 1.0:9.0, (B) about 25 parts to about 200 parts by weight of an organic carboxylic acid anhydride, (C) about 0.01 part to about 2.0 parts by weight of a metal acetylacetonate selected from the group consisting of chromium (III) acetylacetonate, zirconium (IV) acetylacetonate, and mixtures thereof, acting as a latent accelerator, and (D) about 0.3 to about 30 parts by weight of an organic carboxylic acid selected from the group consisting of acetic acid, propionic acid, butyric acid, isobutyric acid, valeric acid, caproic acid, heptanoic acid, caprylic acid, benzoic acid, toluic acids, chlorobenzoic acids, nitrobenzoic acids, succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, phthalic acid, isophthalic acid, terephthalic acid and mixtures thereof, acting as sole co-accelerator, wherein the resinous composition is highly fluid, having an initial viscosity of below about 350 cps. at 25° C.
Claim 3
Dependent Claim
25 words
The composition of claim 1, wherein the epoxy resins of (A)(1) and (A)(2) have an epoxy equivalent weight of from about 100 to about 500.
Claim 4
Dependent Claim
23 words
The composition of claim 2, wherein the composition has a storage lifetime of at least 60 days under 1,000 cps. at 25° C..
Claim 5
Dependent Claim
46 words
The composition of claim 2, wherein the metal acetylacetonate is chromium (III) acetylacetonate, and the organic carboxylic acid is selected from the group consisting of acetic acid, butyric acid, heptanoic acid, benzoic acid, toluic acids, chlorobenzoic acids, nitrobenzoic acids, succinic acid, isophthalic acid and mixtures thereof.
Claim 6
Dependent Claim
48 words
The composition of claim 2, wherein the diglycidyl ether of an aliphatic diol has a viscosity of between about 5 cps. to about 60 cps. at 25° C. and the second epoxy resin has a viscosity of between about 250 cps. to about 20,000 cps. at 25° C..
Claim 7
Dependent Claim
44 words
The composition of claim 2, wherein the diglycidyl ether of an aliphatic diol is selected from the group consisting of diglycidyl ethers of neopentyl glycol, diglycidyl ethers of 1,4 butane diol, diglycidyl ethers of ethylene glycol, diglycidyl ethers of polyether glycols and mixtures thereof.
Claim 8
Dependent Claim
13 words
The composition of claim 2, wherein the organic carboxylic acid is acetic acid.
Claim 9
Dependent Claim
31 words
The composition of claim 2, wherein the composition also contains up to about 100 parts of filler particles, of average particle sizes of from about 10 microns to about 300 microns.
References Cited (Backward Citations)
US3624032A
Cited
US3956241A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-11 | 1982-03-13 | 1982-09-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-11 | 1986-03-13 | 1986-09-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-11 | 1990-03-13 | 1990-09-12 | $7700.00 | Window Closed / Lapsed |