Catalyst for oxidation of carbon monoxide and hydrocarbons in combustion engine exhaust gas
Assignee: Nissan Motor Co Ltd
•
Filing: 1977-06-16
•
Granted: 1978-09-05
•
Expires: 1997-06-16
Abstract
Abstract A catalyst which consists essentially of a carrier of active alumina and, distributed upon the carrier, at least one catalytic metal selected from Pt, Pd, Rh and Ir and is produced by impregnating the carrier with an aqueous solution of thermally decomposable catalytic metal salt(s) and baking the impregnated carrier in 100% steam at 300°-600° C. The total amount of the catalytic metal(s) in the catalyst is 0.03-0.3 Wt%, and the amounts of Rh and Ir both are limited to 0-0.03 Wt%. The catalyst features a high conversion ability for hydrocarbons, good durability and a low activity on the conversion of SO 2 to SO 3 particularly when a combination of Pt and/or Pd, and either Rh or Ir is used as the catalytic metals.
Inventors
- 👤 Shinkity Torii
- 👤 Sakae Kawagoshi
- 👤 Tetsuhiko Yoneshige
- 👤 Hidehumi Ito
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 14:27
CPC Classifications
B; B01; B01D; B01D53/00; B01D53/34; B01D53/92; B01D53/94; B01D53/944; B01J; B01J23/00; B01J23/38; B01J23/40; Y; Y02; Y02A; Y02A50/00; Y02A50/20
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
140 words
A catalyst for conversion of carbon monoxide and hydrocarbons in the exhaust gas of a combustion engine, the catalyst consisting essentially of a carrier of active alumina and at least one catalytic metal which is selected from the group consisting of Pt, Pd, Rh and Ir and is distributed upon said carrier, the total amount of said at least one catalytic metal being in the range from 0.03 to 0.3 Wt% of the catalyst, both the amount of Rh and the amount of Ir being 0-0.03 Wt%, the catalyst being produced by a method comprising the steps of impregnating said carrier with an aqueous solution of at least one thermally decomposable compound of a catalytic metal selected from said group, and baking the impregnated carrier in a stream of substantially 100% steam at a temperature between 300° and 600° C.
Claim 2
Dependent Claim
140 words
A catalyst for conversion of carbon monoxide and hydrocarbons in the exhaust gas of a combustion engine, the catalyst consisting essentially of a carrier of active alumina and at least one catalytic metal which is selected from the group consisting of Pt, Pd, Rh and Ir and is distributed upon said carrier, the total amount of said at least one catalytic metal being in the range from 0.03 to 0.3 Wt% of the catalyst, both the amount of Rh and the amount of Ir being 0-0.03 Wt%, the catalyst being produced by a method comprising the steps of impregnating said carrier with an aqueous solution of at least one thermally decomposable compound of a catalytic metal selected from said group, and baking the impregnated carrier in a stream of substantially 100% steam at a temperature between 300° and 600° C.
Claim 3
Dependent Claim
31 words
A catalyst as claimed in claim 1, wherein said at least one thermally decomposable compound is selected from the group consisting of chloroplatinic acid, palladium chloride, rhodium trichloride and iridium tetrachloride.
Claim 4
Dependent Claim
14 words
A catalyst as claimed in claim 2, wherein said carrier comprises a granular form.
Claim 5
Dependent Claim
18 words
A catalyst as claimed in claim 2, wherein said at least one catalytic metal comprises Pt or Pd.
Claim 6
Dependent Claim
30 words
A catalyst as claimed in claim 2, wherein said at least one catalytic metal comprises Pt and Pd, the weight ratio of Pt to Pd being from 9:1 to 1:9.
Claim 7
Dependent Claim
36 words
A catalyst as claimed in claim 2, wherein said at least one catalytic metal comprises Pt, Pd and Rh, the weight ratio of the total of Pt and Pd to Rh being from 60:1 to 60:4.
Claim 8
Dependent Claim
36 words
A catalyst as claimed in claim 2, wherein said at least one catalytic metal comprises Pt and one of Rh and Ir, the weight ratio of Pt to Rh or Ir being from 100:1 to 10:1.
Claim 9
Dependent Claim
36 words
A catalyst as claimed in claim 2, wherein said at least one catalytic metal comprises Pd and one of Rh and Ir, the weight ratio of Pd to Rh or Ir being from 10:1 to 30:1.
Claim 10
Dependent Claim
155 words
A catalyst for conversion of carbon monoxide and hydrocarbons in a combustion engine exhaust gas, the catalyst consisting essentially of a carrier of active alumina and at least one catalytic metal which is distributed upon said carrier and comprises at least one of Pt and Pd, the total amount of Pt and Pd being from 0.0273 to 0.3 Wt% of the catalyst, 0-0.03 Wt% Rh and 0-0.03 Wt% Ir, the total amount of Pt, Pd, Rh and Ir being from 0.03 to 0.3 Wt% of the catalyst, the catalyst being produced by a method comprising the steps of impregnating said carrier with an aqueous solution containing at least one of chloroplatinic acid and palladium chloride, and, optionally depending on the amount of Rh and Ir in the catalyst, one of rhodium trichloride and iridium tetrachloride, and baking the impregnated carrier in a stream of substantially 100% steam at a temperature between 300° and 600° C.
Claim 11
Dependent Claim
155 words
A catalyst for conversion of carbon monoxide and hydrocarbons in a combustion engine exhaust gas, the catalyst consisting essentially of a carrier of active alumina and at least one catalytic metal which is distributed upon said carrier and comprises at least one of Pt and Pd, the total amount of Pt and Pd being from 0.0273 to 0.3 Wt% of the catalyst, 0-0.03 Wt% Rh and 0-0.03 Wt% Ir, the total amount of Pt, Pd, Rh and Ir being from 0.03 to 0.3 Wt% of the catalyst, the catalyst being produced by a method comprising the steps of impregnating said carrier with an aqueous solution containing at least one of chloroplatinic acid and palladium chloride, and, optionally depending on the amount of Rh and Ir in the catalyst, one of rhodium trichloride and iridium tetrachloride, and baking the impregnated carrier in a stream of substantially 100% steam at a temperature between 300° and 600° C.
Claim 12
Dependent Claim
20 words
The catalyst as claimed in claim 1, wherein said thermally decomposable compound of said catalytic metal comprises a chlorine-containing compound.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-04 | 1982-03-06 | 1982-09-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-04 | 1986-03-06 | 1986-09-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-04 | 1990-03-06 | 1990-09-05 | $7700.00 | Window Closed / Lapsed |