Grid braze application mold
Assignee: Westinghouse Electric Corp
•
Filing: 1977-03-09
•
Granted: 1978-09-05
•
Expires: 1997-03-09
Abstract
Abstract Method and apparatus for forming a braze joint along the intersection of grid straps of a nuclear fuel assembly. A substantially cylindrical mold having a cavity therein for holding a braze material and having notches near its bottom end complementary to the grid straps is placed on the grid such that the centerline of the mold is substantially colinear with the intersection of the grid straps. Upon heating the grid and mold assembly, the braze material that has been placed in the mold cavity flows by gravity along the intersection of the grid straps which upon cooling forms a brazed joint.
Inventors
- 👤 Willy S. Laird
- 👤 Ben O. Kendall
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 11:21
CPC Classifications
B; B23; B23K; B23K1/00; B23K1/14; B23K3/00; B23K3/08; B23K3/087; G; G21; G21C; G21C3/00; G21C3/30; G21C3/32; G21C3/34; G21C3/356; G21C3/3563; Y; Y02; Y02E; Y02E30/00; Y02E30/30
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
135 words
A method of brazing together grid straps of a grid of a nuclear fuel assembly comprising: assembling said grid whereby a multiplicity of said straps intersect defining lines of intersection; placing a mold having a cavity thereon on said straps near their intersection and in vertical alignment with said line of intersection; placing a predetermined amount of braze material in said cavity of said mold; placing said mold and said grid in a furnace; heating said grid and said mold until said braze material melts and flows downward by gravity along said lines of intersection thereby contacting the adjoining straps and filling spaces between said straps; and cooling said grid and said mold thus solidifying said braze material and thereby establishing a permanent brazed joint along said line of intersection and permanently joining said straps.
Claim 2
Independent Claim
135 words
A method of brazing together grid straps of a grid of a nuclear fuel assembly comprising: assembling said grid whereby a multiplicity of said straps intersect defining lines of intersection; placing a mold having a cavity thereon on said straps near their intersection and in vertical alignment with said line of intersection; placing a predetermined amount of braze material in said cavity of said mold; placing said mold and said grid in a furnace; heating said grid and said mold until said braze material melts and flows downward by gravity along said lines of intersection thereby contacting the adjoining straps and filling spaces between said straps; and cooling said grid and said mold thus solidifying said braze material and thereby establishing a permanent brazed joint along said line of intersection and permanently joining said straps.
Claim 3
Dependent Claim
39 words
The method according to claim 1 wherein said step of placing said mold and said grid in said furnace includes placing said grid and said mold in a vacuum furnace at a pressure of 10 -3 torr or less.
Claim 4
Dependent Claim
26 words
The method according to claim 2 wherein said step of heating includes raising the temperature of said furnace to between about 954° and about 1024° C.
Claim 5
Dependent Claim
25 words
The method according to claim 3 wherein said step of heating further includes maintaining said temperature for between about 60 minutes and about 70 minutes.
Claim 6
Dependent Claim
40 words
The method according to claim 4 wherein said step of cooling includes cooling said grid and said mold by reducing said temperature of said furnace at a rate of 650° C per hour down to a temperature of 593° C.
Claim 7
Dependent Claim
32 words
The method according to claim 5 wherein said step of cooling includes cooling said grid and said mold from 593° C to room temperature at the natural cooling rate for said furnace.
Claim 8
Dependent Claim
37 words
The method according to claim 6 wherein said step of cooling further includes maintaining said grid and said mold in said furnace until said grid and said mold have been cooled to at least about 149° C.
Claim 9
Dependent Claim
19 words
The method according to claim 7 wherein said steps of heating and cooling are performed in a nitrogen atmosphere.
Claim 10
Dependent Claim
19 words
The method according to claim 8 including the step of nickel plating said straps before assembly into said grid.
Claim 11
Dependent Claim
33 words
The method according to claim 9 wherein said step of nickel plating includes plating said straps with a layer of nickel having a thickness of between about 0.00003 inches to about 0.00035 inches.
References Cited (Backward Citations)
US3913210A
Cited
US3948431A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-04 | 1982-03-06 | 1982-09-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-04 | 1986-03-06 | 1986-09-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-04 | 1990-03-06 | 1990-09-05 | $7700.00 | Window Closed / Lapsed |