Method of repairing slag and cinder pots and other heavy steel articles
Assignee: United States Steel Corp
•
Filing: 1977-04-25
•
Granted: 1978-09-05
•
Expires: 1997-04-25
Abstract
Abstract A method of repairing erosion cavities in large steel articles, such as slag and cinder pots by employing a plurality of successive aluminothermic reduction reaction charges without using containment perimeters and without preheating the article. The resultant repaired article has a metallurgically bonded plug in the eroded surface.
Inventors
- 👤 Robert H. Kachik
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 10:13
CPC Classifications
B; B23; B23K; B23K23/00; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49718; Y10T29/49746
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
173 words
A method of repairing an erosion cavity in slag and cinder pots, and other heavy steel articles comprising (a) placing into said cavity an exothermic reaction mixture comprising a fuel powder and a metal oxide, the amount of said mixture having a volume insufficient to overflow said cavity, (b) igniting said mixture to form a superheated melt comprising a metal phase and a slag phase, such that the melt is substantially contained entirely within said cavity, (c) maintaining said melt in said cavity for a time sufficient to allow said melt to separate so that said metal phase settles to the bottom with the slag phase thereover, (d) permitting said melt to solidify with the metal phase securely bonded in the bottom of said cavity, (e) removing said slag phase to expose the metal phase and the remaining unfilled portion of the cavity, and (f) repeating steps (a) through (e) at least one more time to provide a plurality of metal phase layers which fill at least a significant portion of the cavity.
Claim 2
Independent Claim
173 words
A method of repairing an erosion cavity in slag and cinder pots, and other heavy steel articles comprising (a) placing into said cavity an exothermic reaction mixture comprising a fuel powder and a metal oxide, the amount of said mixture having a volume insufficient to overflow said cavity, (b) igniting said mixture to form a superheated melt comprising a metal phase and a slag phase, such that the melt is substantially contained entirely within said cavity, (c) maintaining said melt in said cavity for a time sufficient to allow said melt to separate so that said metal phase settles to the bottom with the slag phase thereover, (d) permitting said melt to solidify with the metal phase securely bonded in the bottom of said cavity, (e) removing said slag phase to expose the metal phase and the remaining unfilled portion of the cavity, and (f) repeating steps (a) through (e) at least one more time to provide a plurality of metal phase layers which fill at least a significant portion of the cavity.
Claim 3
Dependent Claim
13 words
A method according to claim 1 in which said fuel powder is aluminum.
Claim 4
Dependent Claim
21 words
A method according to claim 2 in which said aluminum powder has a size consisting of -100 mesh and +400 mesh.
Claim 5
Dependent Claim
17 words
A method according to claim 1 in which said metallic oxide is Fe 2 O 3 .
Claim 6
Dependent Claim
21 words
A method according to claim 4 in which said Fe 2 O 3 is at least as fine as -35 mesh.
Claim 7
Dependent Claim
30 words
A method according to claim 1 in which said fuel powder is aluminum and said metallic oxide is Fe 2 O 3 and said mixture further contains approximately 10% lime.
Claim 8
Dependent Claim
26 words
A method according to claim 1 in which said mixture is provided in an amount of at least 50 pounds, but not more than 100 pounds.
Claim 9
Dependent Claim
35 words
A method according to claim 7 in which the subsequent exothermic reaction mixtures provided pursuant to step (f) are placed into the cavity and ignited while said casting is still hot from the preceding reaction.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-04 | 1982-03-06 | 1982-09-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-04 | 1986-03-06 | 1986-09-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-04 | 1990-03-06 | 1990-09-05 | $7700.00 | Window Closed / Lapsed |