Form retaining hydrogen-storing material
Assignee: Deutsche Automobil GmbH
•
Filing: 1976-11-08
•
Granted: 1978-08-29
•
Expires: 1996-11-08
Abstract
Abstract A hydrogen-storing material of known type, e.g. Mg, Ti, V, Nb, and alloys such as La-, Ti- and Co- alloys, is made form retaining without significant loss of hydrogen absorption and desorption properties by binding with a plastic having sufficient adhesion or binding strength. The hydrogen-storing material in granular form is mixed with the plastic in powder, emulsion, solution or melt form and then molded into the desired shape.
Inventors
- 👤 Horst Buhl
- 👤 Susanne Will
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 11:20
CPC Classifications
F; F17; F17C; F17C11/00; F17C11/005; C; C01; C01B; C01B3/00; C01B3/0005; C01B3/001; C01B3/0078; C01B3/0084; G; G02; G02B; G02B6/00; G02B6/44; G02B6/4401; G02B6/4429; G02B6/44382; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/32
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
96 words
In a hydrogen-storing composition including hydrogen-storing material consisting of metals or alloys which are comminuted when used reversibly as a hydrogen-storing medium by alternating absorption and desorption with hydrogen gas, the improvement whereby the composition is made from retaining, wherein: said hydrogen-storing material in the form of granules having a grain size of 5-200 microns is bound in a shaped form with a plastic having a desired adhesion or binding strength said plastic being present in an amount sufficient to bind said granules with sufficient strength without significantly affecting the hydrogen absorbing and desorbing properties thereof.
Claim 2
Dependent Claim
96 words
In a hydrogen-storing composition including hydrogen-storing material consisting of metals or alloys which are comminuted when used reversibly as a hydrogen-storing medium by alternating absorption and desorption with hydrogen gas, the improvement whereby the composition is made from retaining, wherein: said hydrogen-storing material in the form of granules having a grain size of 5-200 microns is bound in a shaped form with a plastic having a desired adhesion or binding strength said plastic being present in an amount sufficient to bind said granules with sufficient strength without significantly affecting the hydrogen absorbing and desorbing properties thereof.
Claim 3
Dependent Claim
25 words
A composition in accordance with claim 1, wherein said hydrogen-storing material granules are completely or partially dehydrided or completely hydrided when bound with said plastic.
Claim 4
Dependent Claim
41 words
A composition in accordance with claim 1, wherein said hydrogen-storing material is selected from the group consisting of Ti-Ni alloys, Zr-Ni alloys, Fe-Ti alloys, Mg-Ni alloys, Mg-Cu alloys, La-Ni alloys, La-Co alloys, rare earth-Ni alloys, rare earth-Co alloys and mixtures thereof.
Claim 5
Dependent Claim
53 words
A composition in accordance with claim 1, wherein said plastic is a polyolefin or a copolymer including an olefin as a reacted monomer; vinylcarbazole polymer; polyvinylacetate, polyether, a polyhalogenated hydrocarbon, or a copolymer including a polyhalogenated hydrocarbon; a polyamide; a polyimide; polysulfone; polyester; cellulose ester; silicone; polyphenylene sulfide; or a compatible mixture thereof.
Claim 6
Dependent Claim
80 words
A composition in accordance with claim 4, wherein said plastic is polyethylene, polypropylene or polybutylene or a copolymer thereof with ethylacrylate and/or vinyl acetate, vinylcarbazol polymer, polyvinylacetate, polypropylene oxide, an epoxy resin, polyphenylene oxide, a polyhalogenated hydrocarbon selected from the group consisting of a vinyl chloride polymer, polytetrafluoroethylene, PFEP, polychlorotrifluoroethylene, polyvinyl difluoride, and polyvinyl fluoride, a copolymer including one of said polyhalogenated hydrocarbons, a polyamide, a polyimide, polysulfone, polyacetate, polycarbonate, cellulose ester, silicone, polyphenylene sulfide or a compatible mixture thereof.
Claim 7
Dependent Claim
30 words
A composition in accordance with claim 1, wherein said plastic-bound granules are molded into the shape of bodies having gas channels therethrough in the flow direction of the desorbed hydrogen.
Claim 8
Dependent Claim
12 words
A composition in accordance with claim 1, wherein said plastic is polytetrafluoroethylene.
Claim 9
Dependent Claim
58 words
In the method of storing hydrogen comprising absorbing and desorbing, said hydrogen in hydrogen-storing metals, or metal alloys, in form of shaped bodies, the improvement whereby the life of said shaped bodies of hydrogen-storing metals or metal alloys is improved, wherein: said hydrogen-storing metal or metal alloy is provided in the form of the composition of claim 1.
Claim 10
Dependent Claim
107 words
A process for the manufacture of a hydrogen storing material consisting of metals or alloys which are comminuted when used reversibly as a hydrogen-storing medium by alternating absorption and desorption with hydrogen gas, in accordance with claim 1, comprising: homogeneously mixing said hydrogen storing material having a grain size of 5-200 microns with said plastic in the form of fine powder or as a suspension, emulsion, solution or melt, said plastic being present in an amount of up to 50% by volume of the finished material; and shaping the mixture into the desired shape, wherein any solvent or suspending phase is substantially removed before or after shaping.
Claim 11
Dependent Claim
16 words
A process in accordance with claim 9, wherein said compressing step comprises molding in a mold.
Claim 12
Dependent Claim
21 words
A process in accordance with claim 9, wherein said plastic is added in the form of an emulsion or a solution.
Claim 13
Dependent Claim
14 words
A process in accordance with claim 11, wherein said emulsion is a polytetrafluroethylene emulsion.
Claim 14
Dependent Claim
24 words
A process in accordance with claim 11, wherein said plastic is added in an amount of 2-10% by weight based on the hydrogen-storing material.
Claim 15
Dependent Claim
26 words
A process in accordance with claim 9, wherein the plastic is added in the form of a powder with a particle size smaller than 5 microns.
Claim 16
Dependent Claim
24 words
A process in accordance with claim 14, wherein said plastic is added in an amount of 10-25% by weight based on the hydrogen-storing material.
Claim 17
Dependent Claim
28 words
A process in accordance with claim 9, wherein plastic is added in the form of a powder as well as in the form of an emulsion or solution.
Claim 18
Dependent Claim
18 words
A process in accordance with claim 9, wherein the plastic is added in the form of a melt.
Claim 19
Dependent Claim
28 words
A process in accordance with claim 9, further including the step of processing the plastic-bound hydrogen-storage material to produce a granular material, pellets, disks, honeycombed shapes or films.
Claim 20
Dependent Claim
22 words
A process in accordance with claim 9, further including the step of processing the plastic-bound hydrogen-storage material to produce a coarse-grained powder.
Claim 21
Dependent Claim
20 words
A process in accordance with claim 9, further including the step of: sintering the body formed by said shaping step.
References Cited (Backward Citations)
US2933455A
Cited
US3091550A
Cited
US3166615A
Cited
US3803043A
Cited
US3669745A
Cited
US3539672A
Cited
US3881960A
Cited
US4036944A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-08-28 | 1982-02-27 | 1982-08-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-08-28 | 1986-02-27 | 1986-08-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-08-28 | 1990-02-27 | 1990-08-29 | $7700.00 | Window Closed / Lapsed |