Epoxy curing agent
Assignee: Texaco Development Corp
•
Filing: 1977-07-05
•
Granted: 1978-08-29
•
Expires: 1997-07-05
Abstract
Abstract Epoxy resins, particularly those of the polyglycidyl ether of a polyhydric phenol type, are cured by incorporating therein a polyoxyalkylenepolyamine usually with an accelerator such as a combination of piperazine and an alkanolamine. Rapidity of curing is further improved by substituting from about 50 wt% to 100 wt% of the dithiocarbamate salt of the polyoxyalkylenepolymine for the polyoxyalkylenepolyamine. The epoxy resin products are useful in protective coatings, adhesives, seamless and terrazzo flooring, castings, laminates, and in grouting, potting, encapsulating, caulking and sealing compositions.
Inventors
- 👤 Heinz Schulze
- 👤 Harold G. Waddill
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 19:55
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/18; C08G59/68; C08G59/686; C08G59/40; C08G59/4007; C08G59/4014; C08G59/4057; C08L; C08L63/00
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
67 words
A method for acclerating the curing of an epoxy resin with at least a stoichiometric amount of a polyoxyalkylenepolyamine curing component wherein the curing component comprises a polyoxyalkylene-polyamine having a molecular weight of from about 230 to about 2000 and a dithiocarbamate salt of the polyoxyalkylene polyamine, wherein about 50 wt% to about 100 wt% of said polyoxyalkylenepolyamine is replaced by the dithiocarbamate salt of said polyoxyalkylenepolyamine.
Claim 2
Independent Claim
67 words
A method for acclerating the curing of an epoxy resin with at least a stoichiometric amount of a polyoxyalkylenepolyamine curing component wherein the curing component comprises a polyoxyalkylene-polyamine having a molecular weight of from about 230 to about 2000 and a dithiocarbamate salt of the polyoxyalkylene polyamine, wherein about 50 wt% to about 100 wt% of said polyoxyalkylenepolyamine is replaced by the dithiocarbamate salt of said polyoxyalkylenepolyamine.
Claim 3
Dependent Claim
14 words
The method of claim 1, wherein the polyoxyalkylenepolyamine is a polyoxypropylene diamine or triamine.
Claim 4
Dependent Claim
18 words
The method of claim 1, wherein the polyoxypropylenediamine or triamine has an average molecular weight of about 400.
Claim 5
Dependent Claim
14 words
The method of claim 1, wherein the curing component also includes an additional accelerator.
Claim 6
Dependent Claim
30 words
The method of claim 4, wherein the additional accelerator is a mixture of piperazine and an alkanolamine having a weight ratio of piperazine to alkanolamine of from 1:8 to 1:1.
Claim 7
Independent Claim
110 words
The method of curing an epoxy resin by mixing with said resin at least a stoichiometric amount of a curing composition consisting essentially of from about 50 wt% to about 100 wt% of a dithiocarbamate salt of a polyoxypropylenediamine or triamine having an average molecular weight of from about 230 to about 2000; from about 10 wt% to about 40 wt% of an accelerator combination consisting of piperazine and an alkanolamine in a weight ratio of piperazine to the alkanolamine of from about 1:8 to 1:1; with the balance of the curing composition being a polyoxypropylene diamine or triamine having a molecular weight of from about 230 to about 2000.
Claim 8
Independent Claim
110 words
The method of curing an epoxy resin by mixing with said resin at least a stoichiometric amount of a curing composition consisting essentially of from about 50 wt% to about 100 wt% of a dithiocarbamate salt of a polyoxypropylenediamine or triamine having an average molecular weight of from about 230 to about 2000; from about 10 wt% to about 40 wt% of an accelerator combination consisting of piperazine and an alkanolamine in a weight ratio of piperazine to the alkanolamine of from about 1:8 to 1:1; with the balance of the curing composition being a polyoxypropylene diamine or triamine having a molecular weight of from about 230 to about 2000.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-08-28 | 1982-02-27 | 1982-08-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-08-28 | 1986-02-27 | 1986-08-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-08-28 | 1990-02-27 | 1990-08-29 | $7700.00 | Window Closed / Lapsed |