Hard, heat-resistant nickel electrodeposits
Assignee: Huntington Alloys Corp
•
Filing: 1977-05-25
•
Granted: 1978-08-22
•
Expires: 1997-05-25
Abstract
Abstract An article such as a screen printing cylinder prepared from a hard nickel electrodeposit is characterized by improved resistance to embrittlement when exposed to temperatures above about 200° C. Electrodeposits affording improved resistance to embrittlement contain 0.007-1% sulfur and 0.02-5% manganese. The amount of manganese in the electrodeposits is correlated to the amount of sulfur present so that the manganese is present in an amount in excess of the stoichiometric amount required to form manganese sulfide. The electrodeposits which are also characterized by usefully low levels of internal stress are prepared using conventional nickel plating baths modified by the addition of sources of manganese ions and sulfur.
Inventors
- 👤 William Ronald Wearmouth
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 23:48
CPC Classifications
C; C25; C25D; C25D3/00; C25D3/02; C25D3/56; C25D3/562
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
81 words
An electroformed, hard nickel, screen printing cylinder for exposure in use or manufacture to temperatures exceeding 200° C, said hard nickel portion of said cylinder consisting essentially of, in weight percent: from about 0.007 to about 1% sulfur, sufficient manganese, in the range of from about 0.02 to about 5%, in excess of the stoichiometric amount necessary to form manganese sulfide with the sulfur, to improve embrittlement resistance of said electrodeposit at temperatures exceeding 200° C; and the balance essentially nickel.
Claim 2
Dependent Claim
81 words
An electroformed, hard nickel, screen printing cylinder for exposure in use or manufacture to temperatures exceeding 200° C, said hard nickel portion of said cylinder consisting essentially of, in weight percent: from about 0.007 to about 1% sulfur, sufficient manganese, in the range of from about 0.02 to about 5%, in excess of the stoichiometric amount necessary to form manganese sulfide with the sulfur, to improve embrittlement resistance of said electrodeposit at temperatures exceeding 200° C; and the balance essentially nickel.
Claim 3
Dependent Claim
18 words
A cylinder as defined in claim 1, wherein said cylinder contains from about 0.03 to about 3.5% manganese.
Claim 4
Dependent Claim
18 words
A cylinder as defined in claim 2, wherein said cylinder contains from about 0.02 to about 0.065% sulfur.
Claim 5
Dependent Claim
18 words
A cylinder as defined in claim 1, wherein said cylinder contains from about 0.07 to about 0.35% manganese.
Claim 6
Dependent Claim
18 words
A cylinder as defined in claim 4, wherein said cylinder contains from about 0.02 to about 0.065% sulfur.
Claim 7
Dependent Claim
18 words
A cylinder as defined in claim 1, wherein said cylinder contains from about 0.1 to about 0.25% manganese.
Claim 8
Dependent Claim
18 words
A cylinder as defined in claim 6, wherein said cylinder contains from about 0.02 to about 0.065% sulfur.
Claim 9
Dependent Claim
24 words
A cylinder as defined in claim 1, wherein said cylinder contains manganese in an amount at least 0.03% in excess of said stoichiometric amount.
Claim 10
Dependent Claim
24 words
A cylinder as defined in claim 1, wherein said cylinder contains at least one element selected from a group consisting of iron and cobalt.
Claim 11
Dependent Claim
88 words
A process for preparing a hard nickel screen printing cylinder affording improved resistance to embrittlement at temperatures exceeding 200° C comprising: preparing a nickel electrolyte containing a source of nickel ions, a source of manganese ions, and a source of sulfur; and electrodepositing said cylinder consisting essentially of, in weight percent: from about 0.007 to about 1% sulfur, sufficient manganese, in the range from about 0.02 to about 5%, in excess of a stoichiometric amount necessary to form manganese sulfide with the sulfur, and the balance essentially nickel.
Claim 12
Dependent Claim
88 words
A process for preparing a hard nickel screen printing cylinder affording improved resistance to embrittlement at temperatures exceeding 200° C comprising: preparing a nickel electrolyte containing a source of nickel ions, a source of manganese ions, and a source of sulfur; and electrodepositing said cylinder consisting essentially of, in weight percent: from about 0.007 to about 1% sulfur, sufficient manganese, in the range from about 0.02 to about 5%, in excess of a stoichiometric amount necessary to form manganese sulfide with the sulfur, and the balance essentially nickel.
Claim 13
Dependent Claim
31 words
A process as defined in claim 10, wherein said source of nickel ions is at least one member selected from the group consisting of nickel sulfate, nickel sulfamate, and nickel chloride.
Claim 14
Dependent Claim
21 words
A process as defined in claim 11, wherein said source of sulfur is an aryl compound containing a functional sulfonate group.
Claim 15
Dependent Claim
15 words
A process as defined in claim 12, wherein said source of sulfur is sodium benzosulfimide.
Claim 16
Dependent Claim
30 words
A process as defined in claim 12, wherein said source of sulfur provides a free sulfur content in the electrolyte of from about 0.01 to about 0.065 grams per liter.
Claim 17
Dependent Claim
13 words
A process as defined in claim 12, wherein said electrolyte contains butyne diol.
Claim 18
Dependent Claim
31 words
A process as defined in claim 12, wherein said source of manganese ions is at least one member selected from the group consisting of manganese sulfamate, manganese sulfate, and manganese chloride.
Claim 19
Dependent Claim
36 words
A process as defined in claim 16, wherein said electrolyte contains said source of manganese ions in an amount sufficient to provide a manganese ion content of from about 12 to about 20 grams per liter.
Claim 20
Dependent Claim
30 words
A process as defined in claim 10, wherein said electrolyte is operated at a current density in the range of from about 2.7 to about 20 amperes per square decimeter.
Claim 21
Dependent Claim
30 words
A process as defined in claim 10, wherein said electrolyte is operated at a current density in the range of from about 4.3 to about 12.9 amperes per square decimeter.
References Cited (Backward Citations)
US2304059A
Cited
US2242865A
Cited
US3244603A
Cited
US3282689A
Cited
US3355268A
Cited
US3574067A
Cited
US3582480A
Cited
US3713997A
Cited
US3763030A
Cited
US3759799A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-08-21 | 1982-02-20 | 1982-08-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-08-21 | 1986-02-20 | 1986-08-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-08-21 | 1990-02-20 | 1990-08-22 | $7700.00 | Window Closed / Lapsed |