Method for making steel wire
Assignee: Monsanto Co
•
Filing: 1975-10-20
•
Granted: 1978-08-01
•
Expires: 1995-10-20
Abstract
Abstract A method for making filamentary steel wire from particulate iron oxides with the aid of a fiber-forming acrylic polymer is disclosed. A precursor filament is first formed by wet-spinning an acrylic polymer spin dope in which particles of iron oxide are dispersed. The resulting precursor filament is then exposed to a reducing atmosphere (e.g., a gaseous mixture of hydrogen and carbon monoxide) at a temperature in the range of from about 900° C. to 1150° C. for a period of about 3 to 8 minutes. Under these conditions, the iron oxide particles are reduced to the metallic state and the polymer in the precursor is pyrolized to carbon and byproduct gases. The carbon diffuses into the resulting metallic iron, and the individual metal particles sinter to form continuous steel wire. The method has the capability of producing steel wire of an essentially ferritic/pearlitic structure with a tensile property in excess of 140,000 psi. When the product is converted to a tempered martensite structure tensile strengths exceeding 260,000 psi are achievable.
Inventors
- 👤 Emerick J. Dobo
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 08:05
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0235; B; B22; B22F; B22F1/00; B22F1/06; B22F1/062; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/1216; Y10T428/12167; Y10T428/12229; Y10T428/12389; Y10T428/12403
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
186 words
A method for producing filamentary steel wire wherein particles of iron oxide are combined with a fiber-forming acrylic polymer to first form a precursor filament which is then converted to steel wire, said method comprising the following steps in sequence: (A) providing a spinning dope wherein particles of iron oxide having an average diameter of about 5 microns or less are uniformly dispersed within a solution of acrylic polymer with the weight ratio of iron oxide to acrylic polymer being within the range of from about 3:1 to 7:1 respectively; (B) forming a precursor filament by extruding said dope through a spinnerette and into a coagulation bath; and (C) converting said precursor filament to filamentary steel wire by subjecting the filament to a temperature in the range of from 900° C. to 1150° C. for a period of from about 3 to 8 minutes while being exposed to a gaseous atmosphere consisting of from about 80 to 94 percent by volume of hydrogen, from about 2 to 15 percent by volume of carbon monoxide and from 0 to 10 percent by volume of a gaseous hydrocarbon.
Claim 2
Independent Claim
186 words
A method for producing filamentary steel wire wherein particles of iron oxide are combined with a fiber-forming acrylic polymer to first form a precursor filament which is then converted to steel wire, said method comprising the following steps in sequence: (A) providing a spinning dope wherein particles of iron oxide having an average diameter of about 5 microns or less are uniformly dispersed within a solution of acrylic polymer with the weight ratio of iron oxide to acrylic polymer being within the range of from about 3:1 to 7:1 respectively; (B) forming a precursor filament by extruding said dope through a spinnerette and into a coagulation bath; and (C) converting said precursor filament to filamentary steel wire by subjecting the filament to a temperature in the range of from 900° C. to 1150° C. for a period of from about 3 to 8 minutes while being exposed to a gaseous atmosphere consisting of from about 80 to 94 percent by volume of hydrogen, from about 2 to 15 percent by volume of carbon monoxide and from 0 to 10 percent by volume of a gaseous hydrocarbon.
Claim 3
Dependent Claim
26 words
The method in accordance with claim 1, wherein said iron oxide is selected from the group consisting of hematite, magnetite or mixtures of hematite and magnetite.
Claim 4
Dependent Claim
30 words
The method in accordance with claim 1, wherein said acrylic polymer is a copolymer consisting of 93 percent by weight of acrylonitrile and 7 percent by weight of vinyl acetate.
Claim 5
Dependent Claim
18 words
The method in accordance with claim 1, wherein the solvent in said solution of acrylic polymer is dimethylacetamide.
Claim 6
Dependent Claim
32 words
The method in accordance with claim 1, wherein said coagulation bath consists essentially of 40 to 60 percent by volume of ethylene glycol and 40 to 60 percent by volume of dimethylacetamide.
Claim 7
Dependent Claim
22 words
The method in accordance with claim 1, wherein the hydrogen in said reducing atmosphere is a mixture of molecular and atomic hydrogen.
Claim 8
Independent Claim
203 words
A method for producing filamentary steel wire wherein particles of iron oxide are combined with a fiber-forming acrylic polymer to first form a precursor filament which is then converted to steel wire, said method comprising the following steps in sequence: (A) providing a spinning dope wherein particles of iron oxide having an average diameter of about 5 microns or less are uniformly dispersed in a solution of acrylic polymer with the weight ratio of iron oxide to acrylic polymer being within the range of from about 3:1 to 7:1, respectively; (B) forming a precursor filament by extruding said dope through a spinnerette and into a coagulation bath; (C) stretching said precursor filament from about one to three times its initial length in a boiling water bath; and (D) converting said precursor filament to filamentary steel wire by exposing the filament to a gaseous atmosphere consisting of from about 80 to 94 percent by volume of hydrogen, from about 2 to 15 percent by volume of carbon monoxide, and from 0 to 10 percent by volume of a gaseous hydrocarbon at a temperature in the range of from about 900° C. to 1150° C. for a period of from about 3 to 8 minutes.
Claim 9
Independent Claim
203 words
A method for producing filamentary steel wire wherein particles of iron oxide are combined with a fiber-forming acrylic polymer to first form a precursor filament which is then converted to steel wire, said method comprising the following steps in sequence: (A) providing a spinning dope wherein particles of iron oxide having an average diameter of about 5 microns or less are uniformly dispersed in a solution of acrylic polymer with the weight ratio of iron oxide to acrylic polymer being within the range of from about 3:1 to 7:1, respectively; (B) forming a precursor filament by extruding said dope through a spinnerette and into a coagulation bath; (C) stretching said precursor filament from about one to three times its initial length in a boiling water bath; and (D) converting said precursor filament to filamentary steel wire by exposing the filament to a gaseous atmosphere consisting of from about 80 to 94 percent by volume of hydrogen, from about 2 to 15 percent by volume of carbon monoxide, and from 0 to 10 percent by volume of a gaseous hydrocarbon at a temperature in the range of from about 900° C. to 1150° C. for a period of from about 3 to 8 minutes.
Claim 10
Independent Claim
236 words
A method for producing filamentary steel wire from particles of iron oxide with the aid of a fiber-forming acrylic polymer, said method comprising the following steps in sequence: (A) providing a spinning dope wherein particles of iron oxide having an average diameter of about 5 microns or less are uniformly dispersed in a solution of acrylic polymer with the weight ratio of iron oxide to acrylic polymer being within the range of from about 3:1 to 7:1, respectively; (B) forming a precursor filament by extruding said dope through a spinnerette and into a coagulation bath; (C) stretching said precursor filament from about one to three times its initial length in a boiling water bath; (D) shrinking said precursor filament in a boiling water bath such that the ratio of its length before and after shrinking is in the range of from 1:0.9 to 1:0.7, respectively. (E) converting said precursor filament to filamentary steel wire having an essentially ferritic-pearlitic structure by exposing the filament to a gaseous atmosphere consisting of from 80 to 94 percent by volume of hydrogen, from about 0 to 10 percent by volume of methane and from about 2 to 15 percent by volume of carbon monoxide at a temperature in the range of from about 900° C. to 1150° C. for a period of from about 3 to 8 minutes; and (F) converting the filamentary steel wire to a tempered martensite structure.
Claim 11
Independent Claim
236 words
A method for producing filamentary steel wire from particles of iron oxide with the aid of a fiber-forming acrylic polymer, said method comprising the following steps in sequence: (A) providing a spinning dope wherein particles of iron oxide having an average diameter of about 5 microns or less are uniformly dispersed in a solution of acrylic polymer with the weight ratio of iron oxide to acrylic polymer being within the range of from about 3:1 to 7:1, respectively; (B) forming a precursor filament by extruding said dope through a spinnerette and into a coagulation bath; (C) stretching said precursor filament from about one to three times its initial length in a boiling water bath; (D) shrinking said precursor filament in a boiling water bath such that the ratio of its length before and after shrinking is in the range of from 1:0.9 to 1:0.7, respectively. (E) converting said precursor filament to filamentary steel wire having an essentially ferritic-pearlitic structure by exposing the filament to a gaseous atmosphere consisting of from 80 to 94 percent by volume of hydrogen, from about 0 to 10 percent by volume of methane and from about 2 to 15 percent by volume of carbon monoxide at a temperature in the range of from about 900° C. to 1150° C. for a period of from about 3 to 8 minutes; and (F) converting the filamentary steel wire to a tempered martensite structure.
Claim 12
Dependent Claim
63 words
A synthetic filament which is convertible to filamentary steel wire when exposed to a reducing environment at temperatures in the range of from about 900° C. to 1150° C. for a period of from 3 to 8 minutes, said synthetic filament comprising a mixture of iron oxide particles and an acrylic polymer in a weight ratio of from about 3:1 to 7:1, respectively.
Claim 13
Dependent Claim
63 words
A synthetic filament which is convertible to filamentary steel wire when exposed to a reducing environment at temperatures in the range of from about 900° C. to 1150° C. for a period of from 3 to 8 minutes, said synthetic filament comprising a mixture of iron oxide particles and an acrylic polymer in a weight ratio of from about 3:1 to 7:1, respectively.
Claim 14
Dependent Claim
51 words
A filamentary steel wire product obtained from the reduction, carbonization and sintering of iron oxide particles which has a tensile strength of at least 140,000 psi, said steel wire product being further characterized by an essentially ferritic-pearlitic structure and a carbon content of from about 0.6 to 0.8 percent by weight.
Claim 15
Dependent Claim
51 words
A filamentary steel wire product obtained from the reduction, carbonization and sintering of iron oxide particles which has a tensile strength of at least 140,000 psi, said steel wire product being further characterized by an essentially ferritic-pearlitic structure and a carbon content of from about 0.6 to 0.8 percent by weight.
Claim 16
Dependent Claim
58 words
A filamentary steel wire product having a carbon content in the range of from about 0.6 to 0.8 percent by weight which has been obtained from the reduction, carbonization and sintering of iron oxide particles and thereafter converted to a tempered martensite structure, said steel wire product being characterized by a tensile strength of at least 260,000 psi.
Claim 17
Dependent Claim
58 words
A filamentary steel wire product having a carbon content in the range of from about 0.6 to 0.8 percent by weight which has been obtained from the reduction, carbonization and sintering of iron oxide particles and thereafter converted to a tempered martensite structure, said steel wire product being characterized by a tensile strength of at least 260,000 psi.
Claim 18
Independent Claim
220 words
A method for producing filamentary steel alloy wire wherein a mixture of metal oxide particles consisting of iron oxide and one or more other metal oxides capable of being reduced and sintered at conditions effective for accomplishing a reduction and sintering of iron oxide are combined with a fiber-forming acrylic polymer to first form a precursor filament which is then converted to steel alloy wire, said method comprising the following steps in sequence: (A) providing a spinning dope wherein said mixture of metal oxide particles having an average diameter of about 5 microns or less are uniformly dispersed within a solution of acrylic polymer with the weight ratio of iron oxide to acrylic polymer being within the range of from about 3:1 to 7:1, respectively; (B) forming a precursor filament by extruding said dope through a spinnerette and into a coagulation bath; and (C) converting said precursor filament to filamentary steel alloy wire by exposing the filament to a gaseous atmosphere consisting of from about 80 to 94 percent by volume of hydrogen, from about 2 to 15 percent by volume of carbon monoxide, and from 0 to 10 percent by volume of a gaseous hydrocarbon at a temperature in the range of from about 900° C. to 1150° C. for a period of from about 3 to 8 minutes.
Claim 19
Independent Claim
220 words
A method for producing filamentary steel alloy wire wherein a mixture of metal oxide particles consisting of iron oxide and one or more other metal oxides capable of being reduced and sintered at conditions effective for accomplishing a reduction and sintering of iron oxide are combined with a fiber-forming acrylic polymer to first form a precursor filament which is then converted to steel alloy wire, said method comprising the following steps in sequence: (A) providing a spinning dope wherein said mixture of metal oxide particles having an average diameter of about 5 microns or less are uniformly dispersed within a solution of acrylic polymer with the weight ratio of iron oxide to acrylic polymer being within the range of from about 3:1 to 7:1, respectively; (B) forming a precursor filament by extruding said dope through a spinnerette and into a coagulation bath; and (C) converting said precursor filament to filamentary steel alloy wire by exposing the filament to a gaseous atmosphere consisting of from about 80 to 94 percent by volume of hydrogen, from about 2 to 15 percent by volume of carbon monoxide, and from 0 to 10 percent by volume of a gaseous hydrocarbon at a temperature in the range of from about 900° C. to 1150° C. for a period of from about 3 to 8 minutes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-31 | 1982-01-30 | 1982-08-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-31 | 1986-01-30 | 1986-08-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-31 | 1990-01-30 | 1990-08-01 | $7700.00 | Window Closed / Lapsed |