Method for diametrically expanding thermally contractive ptfe resin tube
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1976-12-14
•
Granted: 1978-08-01
•
Expires: 1996-12-14
Abstract
Abstract An unsintered tube of extruded ptfe resin is heated above its melting temperature of 327 DEG C, a positive pressure is established within the tube relative to the external pressure thereon to radially expand it, and the pressure is maintained until the tube is cooled below its melting point and set. Such a tube demonstrates superior strength and crack resistance when it is thereafter radially contracted around a core member by reheating, and its longitudinal shrinkage is minimized.
Inventors
- 👤 Koichi Okita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 19:22
CPC Classifications
B; B01; B01D; B01D71/00; B01D71/06; B01D71/30; B01D71/32; B01D71/36; A; A61; A61F; A61F2/00; A61F2/02; A61F2/04; A61F2/06; B01D39/00; B01D39/14; B01D39/16; B01D39/1692; B01D63/00; B01D63/06; B01D63/061; B01D67/00; B01D67/0002; B01D67/002; B29; B29C; B29C48/00; B29C48/022; B29C48/03; B29C48/09; B29C48/25; B29C48/30; B29C48/32; B29C48/33; B29C55/00; B29C55/22; B29C67/00; B29C67/0003; B29C67/02; B29C67/04; F; F16; F16L; F16L11/00; F16L11/04; F16L11/06; B01D2239/00; B01D2239/06; B01D2239/069; B01D2239/0695; B01D2239/10; B29C48/36; B29C48/475; B29K; B29K2027/00; B29K2027/12; B29K2027/18; Y; Y10; Y10S; Y10S264/00; Y10S264/71
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
123 words
A method of manufacturing a thermall contractive tube of a desired diameter from a polytetrafluoroethylene resin, comprising the ordered steps of: a. extruding a mixture of liquid lubricant and tetrafluoroethylene resin to form an unsintered tube; b. removing said lubricant; c. heating said unsintered tube to a temperature higher than 327° C under atmospheric pressure; d. immediately after the heating step, and while the tube temperature is still above 327° C, reducing the pressure applied to the outer surface of the tube to provide a pressure differential between the inner and outer surfaces of the tube sufficient to thereby radially expand the tube to said desired diameter: and e. cooling the tube to a temperature below 327° C while maintaining the pressure differential.
Claim 2
Independent Claim
123 words
A method of manufacturing a thermall contractive tube of a desired diameter from a polytetrafluoroethylene resin, comprising the ordered steps of: a. extruding a mixture of liquid lubricant and tetrafluoroethylene resin to form an unsintered tube; b. removing said lubricant; c. heating said unsintered tube to a temperature higher than 327° C under atmospheric pressure; d. immediately after the heating step, and while the tube temperature is still above 327° C, reducing the pressure applied to the outer surface of the tube to provide a pressure differential between the inner and outer surfaces of the tube sufficient to thereby radially expand the tube to said desired diameter: and e. cooling the tube to a temperature below 327° C while maintaining the pressure differential.
Claim 3
Dependent Claim
33 words
A method as claimed in claim 1, further comprising the step of applying a pressure greater than 0.7 Kg/cm 2 to the inner surface of the tube to assist the radial expansion thereof.
Claim 4
Dependent Claim
37 words
A method as claimed in claim 1, wherein the unsintered tube formed by the extrusion step has a fibrous structure, the direction of orientation of the fibrous structure having a lateral component perpendicular to the extrusion direction.
Claim 5
Dependent Claim
37 words
A method as claimed in claim 2, wherein the unsintered tube formed by the extrusion step has a fibrous structure, the direction of orientation of the fibrous structure having a lateral component perpendicular to the extrusion direction.
Claim 6
Dependent Claim
33 words
A method as clamed in claim 1, wherein the tube is surrounded by a fixed diameter jacket during the radial expansion and cooling steps to thereby limit the radial expansion of the tube.
Claim 7
Dependent Claim
33 words
A method as claimed in claim 2, wherein the tube is surrounded by a fixed diameter jacket during the radial expansion and cooling steps to thereby limit the radial expansion of the tube.
Claim 8
Dependent Claim
33 words
A method as claimed in claim 3, wherein the tube is surrounded by a fixed diameter jacket during the radial expansion and cooling steps to thereby limit the radial expansion of the tube.
Claim 9
Dependent Claim
33 words
A method as claimed in claim 4, wherein the tube is surrounded by a fixed diameter jacket during the radial expansion and cooling steps to thereby limit the radial expansion of the tube.
Claim 10
Dependent Claim
34 words
A method as claimed in claim 1, further comprising the step of heating the outlet nozzle of the extruder, whereby the exit temperature of the extruded tube is higher than that of the mixture.
Claim 11
Dependent Claim
34 words
A method as claimed in claim 2, further comprising the step of heating the outlet nozzle of the extruder, whereby the exit temperature of the extruded tube is higher than that of the mixture.
Claim 12
Dependent Claim
34 words
A method as claimed in claim 3, further comprising the step of heating the outlet nozzle of the extruder, whereby the exit temperature of the extruded tube is higher than that of the mixture.
Claim 13
Dependent Claim
34 words
A method as claimed in claim 4, further comprising the step of heating the outlet nozzle of the extruder, whereby the exit temperature of the extruded tube is higher than that of the mixture.
Claim 14
Dependent Claim
29 words
A method as claimed in claim 9, wherein the difference between the exit temperature of the extruded tube and the temperature of the mixture is at least 50° C.
Claim 15
Dependent Claim
29 words
A method as claimed in claim 10, wherein the difference between the exit temperature of the extruded tube and the temperature of the mixture is at least 50° C.
Claim 16
Dependent Claim
29 words
A method as claimed in claim 11, wherein the difference between the exit temperature of the extruded tube and the temperature of the mixture is at least 50° C.
Claim 17
Dependent Claim
29 words
A method as claimed in claim 12, wherein the difference between the exit temperature of the extruded tube and the temperature of the mixture is at least 50° C.
Claim 18
Dependent Claim
88 words
A method as claimed in claim 3, wherein the fibrous structure is directionally oriented by effecting relative rotation between an axial mandrel of the extruder and an outlet nozzle of a die thereof during extrusion, said axial mandrel having a smooth surface tapering from a large diameter approximately equal to the inside diameter of the extruded tubing material, said die having a smooth inner surface tapering from a cylinder to a relatively smaller diameter at said nozzle approximately equal to the outside diameter of the extruded tubing material.
Claim 19
Dependent Claim
88 words
A method as claimed in claim 4, wherein the fibrous structure is directionally oriented by effecting relative rotation between an axial mandrel of the extruder and an outlet nozzle of a die thereof during extrusion, said axial mandrel having a smooth surface tapering from a large diameter approximately equal to the inside diameter of the extruded tubing material, said die having a smooth inner surface tapering from a cylinder to a relatively smaller diameter at said nozzle approximately equal to the outside diameter of the extruded tubing material.
Claim 20
Dependent Claim
88 words
A method as claimed in claim 8, wherein the fibrous structure is directionally oriented by effecting relative rotation between an axial mandrel of the extruder and an outlet nozzle of a die thereof during extrusion, said axial mandrel having a smooth surface tapering from a large diameter approximately equal to the inside diameter of the extruded tubing material, said die having a smooth inner surface tapering from a cylinder to a relatively smaller diameter at said nozzle approximately equal to the outside diameter of the extruded tubing material.
Claim 21
Dependent Claim
88 words
A method as claimed in claim 16, wherein the fibrous structure is directionally oriented by effecting relative rotation between an axial mandrel of the extruder and an outlet nozzle of a die thereof during extrusion, said axial mandrel having a smooth surface tapering from a large diameter approximately equal to the inside diameter of the extruded tubing material, said die having a smooth inner surface tapering from a cylinder to a relatively smaller diameter at said nozzle approximately equal to the outside diameter of the extruded tubing material.
References Cited (Backward Citations)
US2456621A
Cited
US2791806A
Cited
US2821155A
Cited
US3008187A
Cited
US3086242A
Cited
US3225129A
Cited
US3370112A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-31 | 1982-01-30 | 1982-08-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-31 | 1986-01-30 | 1986-08-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-31 | 1990-01-30 | 1990-08-01 | $7700.00 | Window Closed / Lapsed |