Abstract An improvement in the process of melt spinning ethylene terephthalate polyester to produce textile fibers with decreased pilling in the threads, fibers or fabrics made therefrom. The ethylene terephthalate is melt polymerized in the presence of a condensation catalyst to a final temperature of about 250°-300° C and a final pressure of less than 10 mm mercury to form an anhydrous melt. A vinyl copolymer having more than two carboxyl and/or hydroxyl groups is added to the melt polymerization at a concentration of about 0.005 to 2.0 percent referred to the dicarboxylic acid component. Melt spinning of the modified polyester is then carried out. The vinyl copolymer has the following general formula- ##STR1## where N IS AN INTEGER FROM 10 TO 10,000; a is zero or an integer from 1 to 100; b is an integer from 1 to 100; R 1 through R 6 are hydrogen, an alkyl group with 1 to 3 carbon atoms or an oxalkyl group -OR 7 ; R 7 is an alkyl group with 1 to 6 carbon atoms or an aryl group with 6 to 10 carbon atoms; X 1 is hydrogen, an alkyl group with 1 to 3 carbon atoms, or a carboxyl group, an esterified carboxyl group; and X 2 is a carboxyl group, a hydroxyl group, an esterified carboxyl group or an esterified hydroxyl group.
An improvement in the process of melt spinning ethylene terephthalate polyester to produce textile fibers having substantially decreased pilling in fabrics containing the fibers comprising melt polymerizing ethylene terephthalate in the presence of a condensation catalyst to a final temperature of about 250° to 300° C and a final pressure of less than 10 mm of mercury to form an anhydrous melt, the improvement comprising: conducting said melt polymerizing in the presence of about 0.005 to 2.0 percent by weight, with respect to the dicarboxylic acid component of a substance having the general formula: ##STR3## where: n is an integer from 10 to 10,000; a is zero or an integer from 1 to 100; b is an integer from 1 to 100; R 1 through R 6 are hydrogen, an alkyl group with 1 to 3 carbon atoms or an oxalykyl group --OR 7 ; R 7 is an alkyl group with 1 to 6 carbon atoms or an aryl group with 6 to 10 carbon atoms; X 1 is hydrogen, an alkyl group with 1 to 3 carbon atoms, a carboxyl group, or an esterified carboxyl group; and X 2 is a carboxyl group, a hydroxyl group, an esterified carboxyl group or an esterified hydroxyl group; building polymerous compounds selected from the group consisting of at least ten carboxyl and hydroxyl groups or at least ten hydroxyl groups as branching components in said polyester; and melt spinning said anhydrous melt.
Claim 2
Dependent Claim
241 words
An improvement in the process of melt spinning ethylene terephthalate polyester to produce textile fibers having substantially decreased pilling in fabrics containing the fibers comprising melt polymerizing ethylene terephthalate in the presence of a condensation catalyst to a final temperature of about 250° to 300° C and a final pressure of less than 10 mm of mercury to form an anhydrous melt, the improvement comprising: conducting said melt polymerizing in the presence of about 0.005 to 2.0 percent by weight, with respect to the dicarboxylic acid component of a substance having the general formula: ##STR3## where: n is an integer from 10 to 10,000; a is zero or an integer from 1 to 100; b is an integer from 1 to 100; R 1 through R 6 are hydrogen, an alkyl group with 1 to 3 carbon atoms or an oxalykyl group --OR 7 ; R 7 is an alkyl group with 1 to 6 carbon atoms or an aryl group with 6 to 10 carbon atoms; X 1 is hydrogen, an alkyl group with 1 to 3 carbon atoms, a carboxyl group, or an esterified carboxyl group; and X 2 is a carboxyl group, a hydroxyl group, an esterified carboxyl group or an esterified hydroxyl group; building polymerous compounds selected from the group consisting of at least ten carboxyl and hydroxyl groups or at least ten hydroxyl groups as branching components in said polyester; and melt spinning said anhydrous melt.
Claim 3
Dependent Claim
23 words
The process of claim 1, wherein said compound having the general formula has a concentration of about 0.05 to 1.0 percent by weight.