Centrifugal forming thin films and semiconductors and semiconductor devices
Assignee: Individual
•
Filing: 1977-04-15
•
Granted: 1978-07-18
•
Expires: 1997-04-15
Abstract
Abstract A method and apparatus for centrifugally forming thin semiconductor films or layers wherein centrifugal force is applied to a molten single-crystal forming material to overcome surface tension and evenly spread the material along a substrate surface substantially parallel to the axis of rotation. The material is thereafter cooled, uniformly or progressively from a seed single crystal, to form a thin layer or film of crystalline material. Desirably, the films or layers will be substantially single crystals. The process and apparatus are useful in forming thin, semiconductor crystal layers useful, for example, in solar cells. Semiconductor devices according to the invention have a porous graphite substrate, a thin film or layer of silicon and a gridwork plated onto the silicon. The interface between the silicon grid graphite substrate is substantially free from silicon carbide.
Inventors
- 👤 Larry P. Kelley
- 👤 Craig A. Hardy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 21:47
CPC Classifications
H; H10; H10F; H10F71/00; H10F71/121; H10F71/1212; C; C30; C30B; C30B11/00; C30B11/008; C30B29/00; C30B29/60; H10F10/00; H10F10/10; H10F10/14; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/547; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
238 words
A method of forming a semiconductor device having a thin crystalline layer on a substrate from single crystal forming semiconductor material consisting essentially of a material which can be grown in single crystalline form onto a seed crystal at the melting point of the material, the method comprising the steps of: providing the single crystal forming semiconductor material in a molten state on a surface portion of the substrate, the substrate being of a conductive material other than the single crystal forming material; heating the crystal forming material to maintain its molten state and while the crystal forming material is in the molten state, rotating the substrate about an axis substantially parallel to the surface thereof at a speed sufficient to overcome the surface tension of the molten material so as to spread by centrifugal force the molten material into a thin, substantially uniform, molten layer of the single crystal forming material, thinner than that obtainable under ordinary gravimetric conditions; cooling the molten layer of the single crystal forming material while maintaining the speed of rotation of the substrate to solidify without epitaxial growth the entire thickness of the molten layer whereby a substantially monocrystalline thin semiconductive layer is formed on the substrate; doping the surface of the semiconductor layer subsequent to the cooling step; plating the doped semiconductor layer with a conductive grid; and wherein the substrate forms a conductor as a part of the semiconductor device.
Claim 2
Independent Claim
238 words
A method of forming a semiconductor device having a thin crystalline layer on a substrate from single crystal forming semiconductor material consisting essentially of a material which can be grown in single crystalline form onto a seed crystal at the melting point of the material, the method comprising the steps of: providing the single crystal forming semiconductor material in a molten state on a surface portion of the substrate, the substrate being of a conductive material other than the single crystal forming material; heating the crystal forming material to maintain its molten state and while the crystal forming material is in the molten state, rotating the substrate about an axis substantially parallel to the surface thereof at a speed sufficient to overcome the surface tension of the molten material so as to spread by centrifugal force the molten material into a thin, substantially uniform, molten layer of the single crystal forming material, thinner than that obtainable under ordinary gravimetric conditions; cooling the molten layer of the single crystal forming material while maintaining the speed of rotation of the substrate to solidify without epitaxial growth the entire thickness of the molten layer whereby a substantially monocrystalline thin semiconductive layer is formed on the substrate; doping the surface of the semiconductor layer subsequent to the cooling step; plating the doped semiconductor layer with a conductive grid; and wherein the substrate forms a conductor as a part of the semiconductor device.
Claim 3
Dependent Claim
22 words
A method of forming a semiconductor device according to claim 1 wherein said substrate surface is substantially perpendicular to the centrifugal force.
Claim 4
Dependent Claim
22 words
A method for forming a semiconductor device according to claim 2 wherein said substrate surface is rotated about a substantially vertical axis.
Claim 5
Dependent Claim
54 words
A method for forming a semiconductor device according to claim 3 wherein the liquid crystal forming material first contacts a seed crystal different form the substrate and on the substrate surface before the cooling step so that at least a portion of the single-crystal layer thus formed has the orientation of the seed crystal.
Claim 6
Dependent Claim
26 words
A method for forming a semiconductor device according to claim 4 wherein said cooling step takes place progessively along the substrate surface from said seed crystal.
Claim 7
Dependent Claim
66 words
A method for forming a semiconductor device according to claim 1 wherein the liquid crystal forming material first contacts a seed crystal different from the substrate and on the substrate before the cooling step and the cooling step takes place progressively along the substrate from the seed crystal so that at least a portion of the resulting crystalline layer has the orientation of the seed crystal.
Claim 8
Dependent Claim
42 words
A method for forming a semiconductor device according to claim 1 wherein the substrate surface is in the shape of a cylindrical section with a radius of curvature substantially equal to the distance from the axis of rotation to the substrate surface.
Claim 9
Dependent Claim
27 words
A method for forming a semiconductor device according to claim 1 wherein the cooling step takes place progressively along the substrate surface from an edge portion thereof.
Claim 10
Dependent Claim
49 words
A method for forming a semiconductor device according to claim 1 wherein the liquid crystal forming material contacts a seed crystal different from the substrate and on the substrate surface prior to the cooling step and the cooling takes place progressively along the substrate surface from the seed crystal.
Claim 11
Dependent Claim
30 words
A method of making a semiconductor device according to claim 1 and further comprising securing a first electrode to the conductive grid and securing a second electrode to the substrate.
Claim 12
Dependent Claim
50 words
A method of making a semiconductor device according to claim 1 wherein the substrate is a porous graphite having a thickness of at least 0.5 mm. and the molten crystal forming material is forced into the pores of the graphite substrate as the molten material is spread by centrifugal force.
Claim 13
Dependent Claim
24 words
A method of making a semiconductor device according to claim 11 wherein the graphite has a porosity in the range of 5% to 23%.
Claim 14
Dependent Claim
33 words
A method of making a semiconductor device according to claim 11 wherein the crystal forming material is silicon and the doping step takes place prior to cooling the semiconductor layer below 1040° C.
Claim 15
Dependent Claim
38 words
A method of making a semiconductor device according to claim 13 wherein the silicon is heated to a temperature in the range of 5° to 40° C above the melting point thereof during the heating and spreading steps.
Claim 16
Dependent Claim
18 words
A method of making a semiconductor device according to claim 1 wherein the crystal forming material is silicon.
Claim 17
Dependent Claim
38 words
A semiconductor device made according to the method of claim 14 wherein the silicon permeates pores of the graphite substrate at the interface between the substrate and the silicon, and the interface is substantially free of silicon carbide.
References Cited (Backward Citations)
US1630045A
Cited
US1831310A
Cited
US2178163A
Cited
US3672429A
Cited
DE2314109A1
Cited
GB1423594A
Cited
US3857436A
Cited
US4052782A
Cited
US3984256A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-17 | 1982-01-16 | 1982-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-17 | 1986-01-16 | 1986-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-17 | 1990-01-16 | 1990-07-18 | $7700.00 | Window Closed / Lapsed |