Method of preparing epoxy-glass prepregs
Assignee: General Electric Co
•
Filing: 1974-11-20
•
Granted: 1978-07-18
•
Expires: 1994-11-20
Abstract
Abstract Epoxy resin compositions comprising a first epoxy resin having a relatively low epoxy equivalent weight of about 170 to 200 and an average functionality of 2 or less, a second epoxy resin having a relatively high epoxy equivalent weight of about 900 to 1900 and an average functionality of 2 or less, and a curing system. Glass fabric is impregnated with the epoxy resin composition and formed into laminates, which are especially useful in the manufacture of printed circuit boards.
Inventors
- 👤 Lo Kwang Tsen
- 👤 John Louis Palkiewicz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 20:05
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/18; C08G59/20; C08G59/22; C08G59/226; C08J; C08J5/00; C08J5/24; C08J5/241; C08J5/244; C08J5/249; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/032; H05K1/0326; H05K1/0353; C08J2363/00; Y; Y10; Y10T; Y10T442/00; Y10T442/30; Y10T442/3472; Y10T442/3528; Y10T442/3569; Y10T442/3585
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
188 words
A method for preparing prepregs for use in the manufacture of epoxy glass circuit board substrate laminates characterized by improved antimeasling, solvent resistance and anti-smearing upon drilling, which comprises a) impregnating a glass fabric with an epoxy resin composition comprising a first epoxy resin of diglycidy ether of bisphenol A having an epoxy equivalent weight of 170 to 200 and an average functionality of not more than 2, and a second epoxy resin comprising the reaction product of diglycidyl ether bisphenol A epoxy resin and a polyhydric phenol selected from the group consisting of bisphenol A and tetrabromobisphenol A, said resulting second epoxy resin having an epoxy equivalent weight of 900 to 1900 and an average functionality of not more than 2, the proportions of said first resin ranging from about 30 to 60% by weight of resin solids and of said second resin from about 70 to 40% by weight of resin solids, a curing system, and a suitable solvent, and b) passing the epoxy impregnated glass fabric through an oven maintained at an elevated temperature to partially advance said epoxy resin and to remove said solvent.
Claim 2
Independent Claim
188 words
A method for preparing prepregs for use in the manufacture of epoxy glass circuit board substrate laminates characterized by improved antimeasling, solvent resistance and anti-smearing upon drilling, which comprises a) impregnating a glass fabric with an epoxy resin composition comprising a first epoxy resin of diglycidy ether of bisphenol A having an epoxy equivalent weight of 170 to 200 and an average functionality of not more than 2, and a second epoxy resin comprising the reaction product of diglycidyl ether bisphenol A epoxy resin and a polyhydric phenol selected from the group consisting of bisphenol A and tetrabromobisphenol A, said resulting second epoxy resin having an epoxy equivalent weight of 900 to 1900 and an average functionality of not more than 2, the proportions of said first resin ranging from about 30 to 60% by weight of resin solids and of said second resin from about 70 to 40% by weight of resin solids, a curing system, and a suitable solvent, and b) passing the epoxy impregnated glass fabric through an oven maintained at an elevated temperature to partially advance said epoxy resin and to remove said solvent.
Claim 3
Dependent Claim
31 words
A method for preparing a prepreg according to claim 1 wherein said polyhydric phenol is bisphenol A and the epoxy equivalent weight of said second epoxy resin is 900 to 1400.
Claim 4
Dependent Claim
31 words
A method for preparing a prepreg according to claim 1 wherein said polyhydric phenol is tetrabromobisphenol A and the epoxy equivalent weight of said second epoxy resin is 1200 to 1900.
Claim 5
Dependent Claim
37 words
An method according to claim 1 wherein said curing system includes about 2.5 to 5 parts by weight per 100 parts of resin solids of dicyandiamide as a cross-linking agent and a tertiary amine as a catalyst.
Claim 6
Dependent Claim
33 words
An method according to claim 1 wherein the proportions of said first resin ranges from about 35 to 50% by weight and of said second resin from about 65 to 50% by weight.
Claim 7
Independent Claim
215 words
A method for preparing prepregs for use in the manufacture of epoxy glass circuit board substrate laminates characterized by improved anti-measling, solvent resistance and anti-measling upon drilling, which comprises a) impregnating a glass fabric with an epoxy resin composition comprising a first epoxy resin of diglycidyl ether of bisphenol A having an epoxy equivalent weight of 170 to 200 and an average functionality of not more than 2, a second epoxy resin comprising the reaction product of diglycidyl ether bisphenol A epoxy resin and bisphenol A, said resulting second epoxy resin having an epoxy equivalent weight of 900 to 1400 and an average functionality of not more than 2, the proportions of said first resin ranging from about 35 to 50% by weight of total resin solids and of said second resin from about 65 to 50% by weight of total resin solids, about 2.5 to 5 parts by weight per 100 parts of total resin solids of dicyandiamide as a cross-linking agent, a tertiary amine as a catalyst, and a suitable solvent whereby the resultant composition includes about 40 to 60% by weight of total resin solids, and b) passing the epoxy impregnated glass fabric through an oven maintained at an elevated temperature to partially advance said epoxy resin and to remove said solvent.
Claim 8
Independent Claim
215 words
A method for preparing prepregs for use in the manufacture of epoxy glass circuit board substrate laminates characterized by improved anti-measling, solvent resistance and anti-measling upon drilling, which comprises a) impregnating a glass fabric with an epoxy resin composition comprising a first epoxy resin of diglycidyl ether of bisphenol A having an epoxy equivalent weight of 170 to 200 and an average functionality of not more than 2, a second epoxy resin comprising the reaction product of diglycidyl ether bisphenol A epoxy resin and bisphenol A, said resulting second epoxy resin having an epoxy equivalent weight of 900 to 1400 and an average functionality of not more than 2, the proportions of said first resin ranging from about 35 to 50% by weight of total resin solids and of said second resin from about 65 to 50% by weight of total resin solids, about 2.5 to 5 parts by weight per 100 parts of total resin solids of dicyandiamide as a cross-linking agent, a tertiary amine as a catalyst, and a suitable solvent whereby the resultant composition includes about 40 to 60% by weight of total resin solids, and b) passing the epoxy impregnated glass fabric through an oven maintained at an elevated temperature to partially advance said epoxy resin and to remove said solvent.
Claim 9
Independent Claim
215 words
A method for preparing prepregs for use in the manufacture of epoxy glass circuit board substrate laminates characterized by improved anti-measling, solvent resistance and anti-smearing upon drilling, which comprises a) impregnating a glass fabric with an epoxy resin composition comprising a first epoxy resin of diglycidyl ether of bisphenol A having an epoxy equivalent weight of 170 to 200 and an average functionality of not more than 2, a second epoxy resin comprising the reaction product of diglycidyl ether bisphenol A epoxy resin and tetrabromobisphenol A, said resulting second epoxy resin having an epoxy equivalent weight of 1200 to 1900 and an average functionality of not more than 2, the proportions of said first resin ranging from about 35 to 50% by weight of total resin solids and of said second resin from about 65 to 50% by weight of total resin solids, about 2.5 to 5 parts by weight per 100 parts of total resin solids of dicyandiamide as a cross-linking agent, a tertiary amine as a catalyst, and a suitable solvent whereby the resultant composition includes about 40 to 60% by weight of total resin solids, and b) passing the epoxy impregnated glass fabric through an oven maintained at an elevated temperature to partially advance said epoxy resin and to remove said solvent.
Claim 10
Independent Claim
215 words
A method for preparing prepregs for use in the manufacture of epoxy glass circuit board substrate laminates characterized by improved anti-measling, solvent resistance and anti-smearing upon drilling, which comprises a) impregnating a glass fabric with an epoxy resin composition comprising a first epoxy resin of diglycidyl ether of bisphenol A having an epoxy equivalent weight of 170 to 200 and an average functionality of not more than 2, a second epoxy resin comprising the reaction product of diglycidyl ether bisphenol A epoxy resin and tetrabromobisphenol A, said resulting second epoxy resin having an epoxy equivalent weight of 1200 to 1900 and an average functionality of not more than 2, the proportions of said first resin ranging from about 35 to 50% by weight of total resin solids and of said second resin from about 65 to 50% by weight of total resin solids, about 2.5 to 5 parts by weight per 100 parts of total resin solids of dicyandiamide as a cross-linking agent, a tertiary amine as a catalyst, and a suitable solvent whereby the resultant composition includes about 40 to 60% by weight of total resin solids, and b) passing the epoxy impregnated glass fabric through an oven maintained at an elevated temperature to partially advance said epoxy resin and to remove said solvent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-17 | 1982-01-16 | 1982-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-17 | 1986-01-16 | 1986-07-18 | $3760.00 | Window Closed / Lapsed |