Non-aqueous water-displacing sealant composition for vehicle glass joints
Assignee: Premier Industrial Corp
•
Filing: 1977-05-02
•
Granted: 1978-07-18
•
Expires: 1997-05-02
Abstract
Abstract A non-aqueous sealant composition particularly adapted for use in the installation or sealing of fixed glass in vehicles. The composition has a thermoplastic rubber base, suitably modified by plasticizers, tackifyers and a cationic surfactant to provide a sealant system which displaces water from a wetted substrate to which it is applied, permitting it to be utilized under either wet or dry conditions.
Inventors
- 👤 John J. Moskal
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 12:08
CPC Classifications
C; C09; C09K; C09K3/00; C09K3/10; C08; C08K; C08K3/00; C08K5/00; C08L; C08L23/00; C08L23/02; C08L23/18; C08L23/24; C08L53/00; C08L53/02; C08L67/00; C09J; C09J153/00; C09J153/02; C08L2666/00; C08L2666/02; C08L2666/28; C08L2666/54; C09K2200/00; C09K2200/02; C09K2200/0239; C09K2200/0243; C09K2200/0247; C09K2200/0278; C09K2200/0286; C09K2200/06; C09K2200/0607; C09K2200/061; C09K2200/0615; C09K2200/0632; C09K2200/0642; C09K2200/0645; C09K2200/0655
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
181 words
A non-aqueous, water-displacing sealant composition for application to vehicle glass joints and the like, comprising a homogeneous mixture of: (A) from 5% to 20% by weight of a thermoplastic rubber base, and (B) from 0.5% to 12% by weight of a liquid plasticizer selected from the group consisting of oxidation-resistant balsamic resins and aromatic hydrocarbons, and (C) from 1% to 20% by weight of a tackifying resin, and (D) from 0.1% to 3% by weight of an anti-oxidant for rubber, and (E) from 0.25% to 0.70% by weight of a cationic surfactant selected from the group consisting of imidazoline derivatives, and (F) from zero to 48% by weight of inert inorganic solids as fillers, and (G) from zero to 5% by weight of a bodying agent, and (H) from 20% to 70% by weight of a liquid solvent selected from the group consisting of aliphatic and aromatic hydrocarbons, and said composition being essentially free of water and being characterized by its ability to displace water, without absorption thereof into the composition, from a water-wetted substrate to which said sealant is applied.
Claim 2
Dependent Claim
181 words
A non-aqueous, water-displacing sealant composition for application to vehicle glass joints and the like, comprising a homogeneous mixture of: (A) from 5% to 20% by weight of a thermoplastic rubber base, and (B) from 0.5% to 12% by weight of a liquid plasticizer selected from the group consisting of oxidation-resistant balsamic resins and aromatic hydrocarbons, and (C) from 1% to 20% by weight of a tackifying resin, and (D) from 0.1% to 3% by weight of an anti-oxidant for rubber, and (E) from 0.25% to 0.70% by weight of a cationic surfactant selected from the group consisting of imidazoline derivatives, and (F) from zero to 48% by weight of inert inorganic solids as fillers, and (G) from zero to 5% by weight of a bodying agent, and (H) from 20% to 70% by weight of a liquid solvent selected from the group consisting of aliphatic and aromatic hydrocarbons, and said composition being essentially free of water and being characterized by its ability to displace water, without absorption thereof into the composition, from a water-wetted substrate to which said sealant is applied.
Claim 3
Dependent Claim
13 words
A composition according to claim 1, wherein (A) is a styrene block copolymer.
Claim 4
Dependent Claim
11 words
A composition according to claim 1, wherein (A) is butyl rubber.
Claim 5
Dependent Claim
13 words
A composition according to claim 2, wherein (A) is a styrene-butadiene-styrene block copolymer.
Claim 6
Dependent Claim
13 words
A composition according to claim 2, wherein (A) is a styrene-isoprene-styrene block copolymer.
Claim 7
Dependent Claim
16 words
A composition according to claim 1, wherein (C) is a thermoplastic ester resin derived from pentaerythritol.
Claim 8
Dependent Claim
12 words
A composition according to claim 1, wherein (C) is a polyterpene resin.
Claim 9
Dependent Claim
12 words
A composition according to claim 1, wherein (D) is a hindered phenol.
Claim 10
Dependent Claim
12 words
A composition according to claim 1, wherein (E) is a 1-hydroxyethyl-2 alkyl-imidazoline.
Claim 11
Dependent Claim
12 words
A composition according to claim 1, wherein (F) is powdered calcium carbonate.
Claim 12
Dependent Claim
22 words
A composition according to claim 1, wherein (G) is selected from the group consisting of asbestos and fumed silicas with thixotropic characteristics.
Claim 13
Dependent Claim
10 words
A composition according to claim 1, wherein (H) is naphtha.
Claim 14
Dependent Claim
17 words
A composition according to claim 1, having a Shore A Durometer hardness of no more than 50.
Claim 15
Dependent Claim
14 words
A composition according to claim 13, having a Brookfield viscosity greater than 100 cps.
Claim 16
Dependent Claim
62 words
A composition according to claim 1, wherein the constituent: (A) is from 5% to 13% by weight, and (B) is from 1.5% to 7% by weight, and (C) is from 1% to 15% by weight, and (F) is from 25% to 48% by weight, and (G) is from 3% to 5% by weight, and (H) is from 20% to 50% by weight.
Claim 17
Dependent Claim
15 words
A composition according to claim 15, having a Brookfield viscosity of more than 75,000 cps.
Claim 18
Dependent Claim
64 words
A composition according to claim 15, wherein the constituent: (A) is about 8.5% by weight, and (B) is about 6.6% by weight, and (C) is about 7.0% by weight, and (D) is about 0.1% by weight, and (E) is about 0.6% by weight, and (F) is about 37.8% by weight, and (G) is about 3.8% by weight, and (H) is about 35.6% by weight.
Claim 19
Dependent Claim
51 words
A composition according to claim 1, wherein the constituent: (A) is from 8% to 20% by weight, and (B) is from 3% to 12% by weight, and (C) is from 10% to 20% by weight, and (F) is from zero to 25%, and (H) is from 50% to 70% by weight.
Claim 20
Dependent Claim
15 words
A composition according to claim 18, having a Brookfield viscosity of less than 5000 cps.
Claim 21
Dependent Claim
61 words
A composition according to claim 18, wherein the constituent: (A) is about 16.4% by weight, and (B) is about 6.3% by weight, and (C) is about 14.0% by weight, and (D) is about 1.5% by weight, and (E) is about 0.25% by weight, and (F) is zero, and (G) is about 2.7% by weight, and (H) is about 58.85% by weight.
Claim 22
Dependent Claim
20 words
A composition according to claim 17, with the addition of a minor proportion of a coloring ingredient for the composition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-17 | 1982-01-16 | 1982-07-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-17 | 1986-01-16 | 1986-07-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-17 | 1990-01-16 | 1990-07-18 | $7700.00 | Window Closed / Lapsed |