Stable organic dispersions which can be cured with little shrinkage, based on unsaturated polyester resins and thermoplastic polymers
Assignee: Bayer AG
•
Filing: 1976-03-22
•
Granted: 1978-07-11
•
Expires: 1996-03-22
Abstract
Abstract Organic dispersions which can be cured with little shrinkage and are based on unsaturated polyester, copolymerizable vinyl or vinilydene compounds, thermoplastic polymers which are colloidally soluble and are incompatible with the polyester resin and an ethylene/vinyl acetate copolymer with high vinyl acetate contents show a good stability.
Inventors
- 👤 Bernhard Hess
- 👤 Karl Raichle
- 👤 Ludwig Bottenbruch
- 👤 Hansjochen Schulz-Walz
- 👤 Heinrich Alberts
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 19:18
CPC Classifications
C; C08; C08L; C08L67/00; C08L67/06
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
111 words
An organic dispersion which consists essentially of: (A) 20-70% by weight of an α,β-ethylenically unsaturated polyester; (B) 20-70% by weight of a copolymerizable vinyl or vinylidene compound; (C) 3-30% by weight of a thermoplastic polymer which is colloidally soluble in component B, incompatible with a composition comprising components A plus B and which consists essentially of polyestyrene, polyacrylic acid ester or polymethacrylic acid ester; and (D) 0.001-20% by weight of ethylene/vinyl acetate copolymer having a vinyl acetate content of 50-80% by weight and a Mooney viscosity of 8-60 measured according to DIN 53,523 (L-4), said percentages by weight being based on the sum of weights of components A, B and C.
Claim 2
Dependent Claim
111 words
An organic dispersion which consists essentially of: (A) 20-70% by weight of an α,β-ethylenically unsaturated polyester; (B) 20-70% by weight of a copolymerizable vinyl or vinylidene compound; (C) 3-30% by weight of a thermoplastic polymer which is colloidally soluble in component B, incompatible with a composition comprising components A plus B and which consists essentially of polyestyrene, polyacrylic acid ester or polymethacrylic acid ester; and (D) 0.001-20% by weight of ethylene/vinyl acetate copolymer having a vinyl acetate content of 50-80% by weight and a Mooney viscosity of 8-60 measured according to DIN 53,523 (L-4), said percentages by weight being based on the sum of weights of components A, B and C.
Claim 3
Dependent Claim
34 words
The organic dispersion of claim 1 consisting essentially of 30-50% by weight of component A; 40-60% by weight of component B; 5-20% by weight of component C and 0.15-10% by weight of component D.
Claim 4
Dependent Claim
25 words
The organic dispersion of claim 1 wherein the vinyl acetate content of component D is 60-75% by weight and the Mooney viscosity thereof is 45-65.
Claim 5
Dependent Claim
28 words
The organic dispersion of claim 1 wherein the acid number of component A is 10-100, the OH number thereof is 10-150 and the molecular weight thereof is 500-5000.
Claim 6
Dependent Claim
27 words
The organic dispersion of claim 1 containing 0.1 to 1.0% by weight, based on the sum of the weights of components A, B and C, of water.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-10 | 1982-01-09 | 1982-07-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-10 | 1986-01-09 | 1986-07-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-10 | 1990-01-09 | 1990-07-11 | $7700.00 | Window Closed / Lapsed |