Flamboyant finish and process for applying same
Assignee: Beatrice Companies Inc
•
Filing: 1976-11-24
•
Granted: 1978-06-27
•
Expires: 1996-11-24
Abstract
Abstract A process for applying a coating exhibiting high gloss, and good depth appearance is disclosed, as well as the resulting coated product. For instance, a first coating is applied to a conductive substrate, wherein the first coating consists of a polyester polymer, a blocked catalyst therefor, and bright reflective leafing metallic flake pigments. The coated substrate is heated to a first temperature high enough to permit the flake pigments to move to a position wherein the flakes are substantially oriented parallel to the coating surface, but not high enough to unblock the catalyst. After the pigment flakes have obtained the desired oriented position, the coating is heated to a second temperature high enough that the catalyst unblocks and cures or gels the polymer. Thereafter, a transparent second coating is applied over the cured first coating, with the second coating being a clear polymer containing a tinting amount of soluble coloring agent therein. The process is highly suitable for coating bicycle frames, motorcycle frames, and the like, wherein a high gloss, decorative coating exhibiting good weather resistance is required. Such coatings are generally called flamboyant finishes.
Inventors
- 👤 John M. Millar
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 19:37
CPC Classifications
B; B05; B05D; B05D5/00; B05D5/06; B05D5/067; B05D5/068; B05D3/00; B05D3/02; B05D3/0209; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975; Y10T428/25; Y10T428/256; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/269
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
277 words
A method of applying a coating having good depth appearance to an electrically conductive substrate, said method comprising applying to said substrate a coating at least 1/2 mil thick of a first coating composition consisting essentially of at least one substantially clear thermosetting film-forming polymer, a catalytic amount of at least one blocked catalyst for said polymer, wherein said catalyst unblocks at a temperature at least 5° F above the melting temperature of said thermosetting polymer, and a pigmenting amount of at least one bright reflective leafing flake pigment, heating the first coating composition on said substrate to a first temperature below the catalyst unblocking temperature and above the polymer melting temperature to permit the flake pigments to substantially become oriented parallel to the surface of said composition away from said substrate, and thereafter gelling or curing said polymer by heating said first coating composition to a higher second temperature which is above the catalyst unblocking temperature while maintaining the flake pigments substantially in said oriented position, to produce a gelled or cured first coating having a bright reflective appearance, and thereafter coating the first coating with a second coating at least one half mil thick of a transparent second coating composition consisting essentially of at least one at least substantially clear film-forming second polymer and a tinctorial amount which is at least about 0.1% by weight, based on the weight of said second coating composition, of at least one coloring agent which is substantially soluble in said second polymer and heat stable at the curing or fusing temperatures of said second polymer, and thereafter curing or fusing said second polymer to form an integral film thereof.
Claim 2
Independent Claim
277 words
A method of applying a coating having good depth appearance to an electrically conductive substrate, said method comprising applying to said substrate a coating at least 1/2 mil thick of a first coating composition consisting essentially of at least one substantially clear thermosetting film-forming polymer, a catalytic amount of at least one blocked catalyst for said polymer, wherein said catalyst unblocks at a temperature at least 5° F above the melting temperature of said thermosetting polymer, and a pigmenting amount of at least one bright reflective leafing flake pigment, heating the first coating composition on said substrate to a first temperature below the catalyst unblocking temperature and above the polymer melting temperature to permit the flake pigments to substantially become oriented parallel to the surface of said composition away from said substrate, and thereafter gelling or curing said polymer by heating said first coating composition to a higher second temperature which is above the catalyst unblocking temperature while maintaining the flake pigments substantially in said oriented position, to produce a gelled or cured first coating having a bright reflective appearance, and thereafter coating the first coating with a second coating at least one half mil thick of a transparent second coating composition consisting essentially of at least one at least substantially clear film-forming second polymer and a tinctorial amount which is at least about 0.1% by weight, based on the weight of said second coating composition, of at least one coloring agent which is substantially soluble in said second polymer and heat stable at the curing or fusing temperatures of said second polymer, and thereafter curing or fusing said second polymer to form an integral film thereof.
Claim 3
Dependent Claim
17 words
Method of claim 1, wherein the flake pigment has an average maximum dimension of about 10 microns.
Claim 4
Dependent Claim
25 words
Method of claim 2, wherein said flake pigment is selected from the group consisting of aluminum, chromium, bronze, nickel, stainless steel, and silver leafing pigments.
Claim 5
Dependent Claim
12 words
Method of claim 3, wherein said pigment is a leafing aluminum pigment.
Claim 6
Dependent Claim
26 words
Method of claim 4, wherein at least about 2.0% by weight, based on the weight of said first coating composition, of said flake pigment is used.
Claim 7
Dependent Claim
17 words
Method according to claim 5, wherein about 2 to 3.5% by weight of flake pigment is used.
Claim 8
Dependent Claim
16 words
Method according to claim 1, wherein said first coating is about 0.5 to 5 mils thick.
Claim 9
Dependent Claim
16 words
Method according to claim 7, wherein said first coating is about 1.5 to 3 mils thick.
Claim 10
Dependent Claim
23 words
Method according to claim 1, wherein said second polymer is selected from the group consisting of thermosetting polyester, epoxy, urethane and acrylic polymers.
Claim 11
Dependent Claim
13 words
Method according to claim 9, wherein said second polymer is a polyester polymer.
Claim 12
Dependent Claim
17 words
Method according to claim 1, wherein said coloring agent is a dye which exhibits high UV resistance.
Claim 13
Dependent Claim
12 words
Method according to claim 11, wherein the dye is an azo dye.
Claim 14
Dependent Claim
26 words
Method according to claim 1, wherein about 1 to 3% by weight, based on the weight of said second coating composition, of coloring agent is used.
Claim 15
Dependent Claim
16 words
Method according to claim 1, wherein the second coating is about 1 to 5 mils thick.
Claim 16
Dependent Claim
16 words
Method according to claim 14, wherein said second coating is about 1.5 to 3 mils thick.
Claim 17
Dependent Claim
47 words
Method according to claim 1, wherein said first temperature is about 250° F to about 325° F, said second temperature is about 350° F to about 450° F, and wherein said second polymer is cured by heating to a temperature of about 300° F to 450° F.
Claim 18
Dependent Claim
96 words
Article consisting essentially of an electrically conductive substrate, a first coating on said substrate, said first coating consisting essentially of a cured thermosetting polymer and a pigmenting amount of at least one bright reflective leafing flake pigment, said flake pigment oriented substantially parallel to the surface of said polymer, and a transparent second coating over said first coating, said second coating consisting essentially of at least one substantially clear film-forming second polymer containing at least about 0.1% by weight of at least one dye substantially dissolved therein, said coatings each at least about 1/2 mil thick.
Claim 19
Dependent Claim
96 words
Article consisting essentially of an electrically conductive substrate, a first coating on said substrate, said first coating consisting essentially of a cured thermosetting polymer and a pigmenting amount of at least one bright reflective leafing flake pigment, said flake pigment oriented substantially parallel to the surface of said polymer, and a transparent second coating over said first coating, said second coating consisting essentially of at least one substantially clear film-forming second polymer containing at least about 0.1% by weight of at least one dye substantially dissolved therein, said coatings each at least about 1/2 mil thick.
Claim 20
Dependent Claim
15 words
Article of claim 17, wherein said article is the frame or fender of a bicycle.
Claim 21
Dependent Claim
15 words
Article of claim 17, wherein said article is the frame or fender of a motorcycle.
Claim 22
Dependent Claim
24 words
Article of claim 17, wherein said pigment is selected from the group consisting of aluminum, chromium, bronze, nickel, stainless steel and silver leafing pigments.
Claim 23
Dependent Claim
12 words
Article of claim 17, wherein said pigment is a leafing aluminum pigment.
Claim 24
Dependent Claim
19 words
Article of claim 17, wherein said first coating contains at least about 2% by weight of said flake pigment.
Claim 25
Dependent Claim
19 words
Article of claim 22, wherein said first coating contains about 2.0 to 3.5% by weight of said flake pigment.
Claim 26
Dependent Claim
15 words
Article of claim 17, wherein said first coating is about 0.5 to 5 mils thick.
Claim 27
Dependent Claim
14 words
Article of claim 24, wherein said first coating is 1.5 to 3 mils thick.
Claim 28
Dependent Claim
21 words
Article of claim 17, wherein said second polymer is selected from the group consisting of polyester, epoxy, urethane and acrylic polymers.
Claim 29
Dependent Claim
12 words
Article of claim 26, wherein said second polymer is a polyester polymer.
Claim 30
Dependent Claim
16 words
Article of claim 17, wherein said coloring agent is a dye which exhibits high UV resistance.
Claim 31
Dependent Claim
11 words
Article of claim 28, wherein said dye is an azo dye.
Claim 32
Dependent Claim
18 words
Article of claim 17, wherein said second coating contains about 1% to 3% by weight of coloring agent.
Claim 33
Dependent Claim
15 words
Article of claim 17, wherein said second coating is about 0.5 to 5 mils thick.
Claim 34
Dependent Claim
14 words
Article of claim 31, wherein said second coating is 1.5 to 3 mils thick.
Claim 35
Dependent Claim
22 words
Method according to claim 1, wherein said first coating is applied by electrostatically spraying said first coating composition on said conductive substrate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-26 | 1981-12-26 | 1982-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-26 | 1985-12-26 | 1986-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-26 | 1989-12-26 | 1990-06-27 | $7700.00 | Window Closed / Lapsed |