Article and method of forming porous coating on electrode layer of concentration cell type oxygen sensor
Assignee: Nissan Motor Co Ltd
•
Filing: 1976-06-10
•
Granted: 1978-06-27
•
Expires: 1996-06-10
Abstract
Abstract A porous coating, which is effective in restricting the flow of a gas under measurement relatively to the electrode layer of the sensor and protecting the electrode against detrimental influences, is formed by spraying fine particles of a heat-resistant and chemically stable material at a high temperature onto the electrode surface to form a porous layer with pores of a moderate size, then impregnating the porous layer with an aqueous dispersion of fine particles of a similar material followed by baking the impregnated layer, so that the finished coating has pores of appropriate size and total volume.
Inventors
- 👤 Katsuhiro Kishida
- 👤 Hiroshi Takao
- 👤 Kimmochi Togawa
- 👤 Kazuo Matoba
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 17:28
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/26; G01N27/403; G01N27/406; G01N27/407; G01N27/4075; G01N27/4077
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
265 words
A method of forming a porous coating on an electrode layer of an oxygen sensor, said sensor comprising a layer of a solid oxygen-ion electrolyte for use in a combustion engine exhaust gas, said layer of said solid electrolyte having first and second sides and having first and second electrode layers formed on said first and second sides respectively; said first electrode layer being in communication with said exhaust gases, said second layer being in communication with a reference gas, said porous coating being formed only on said first electrode layer which is exposed to, and in communication with, said exhaust gases, said method comprising the steps of: applying fine particles of a heat-resistant and chemically stable first material onto the surface of the electrode layer to form a porous layer by plasma-spraying said fine particles, said first material being selected from the group consisting of alumina, spinel, alumina cement, beryllia, zirconia, nickel oxide, silicon carbide, boron carbide and boron nitride; applying a dispersion of fine particles of a heat-resistant and chemically stable second material in a liquid onto said porous layer to impregnate said porous layer with said dispersion, said dispersion containing at least one compound selected from the group consisting of alumina and silica; and baking the impregnated porous layer to fix said particles of said second material to said porous coating, said fine particles and said dispersion being applied such that the total pore volume in the porous coating after the completion of the baking step ranges from between about 0.09 to 0.16 cm 3 per one gram of the porous coating.
Claim 2
Independent Claim
265 words
A method of forming a porous coating on an electrode layer of an oxygen sensor, said sensor comprising a layer of a solid oxygen-ion electrolyte for use in a combustion engine exhaust gas, said layer of said solid electrolyte having first and second sides and having first and second electrode layers formed on said first and second sides respectively; said first electrode layer being in communication with said exhaust gases, said second layer being in communication with a reference gas, said porous coating being formed only on said first electrode layer which is exposed to, and in communication with, said exhaust gases, said method comprising the steps of: applying fine particles of a heat-resistant and chemically stable first material onto the surface of the electrode layer to form a porous layer by plasma-spraying said fine particles, said first material being selected from the group consisting of alumina, spinel, alumina cement, beryllia, zirconia, nickel oxide, silicon carbide, boron carbide and boron nitride; applying a dispersion of fine particles of a heat-resistant and chemically stable second material in a liquid onto said porous layer to impregnate said porous layer with said dispersion, said dispersion containing at least one compound selected from the group consisting of alumina and silica; and baking the impregnated porous layer to fix said particles of said second material to said porous coating, said fine particles and said dispersion being applied such that the total pore volume in the porous coating after the completion of the baking step ranges from between about 0.09 to 0.16 cm 3 per one gram of the porous coating.
Claim 3
Dependent Claim
29 words
The method in accordance with claim 1 wherein the particle size of said fine particles of said first material is in the range of from 5 to 50 μm.
Claim 4
Dependent Claim
19 words
The method in accordance with claim 2 wherein said dispersion is applied to said porous coating by vacuum impregnation.
Claim 5
Dependent Claim
21 words
The method in accordance with claim 3 wherein the baking step is carried out at a temperature of about 900° C.
Claim 6
Dependent Claim
44 words
The method in accordance with claim 2 wherein said particles of said first material and said dispersion are applied in such quantities that the porous coating has a thickness in the range from 5 to 500 μm after the completion of the baking step.
Claim 7
Independent Claim
310 words
A method of forming a porous coating on an electrode layer of an oxygen sensor, said sensor comprising a layer of a solid oxygen-ion electrolyte for use in a combustion engine exhaust gas, said layer of said solid electrolyte having first and second sides and having first and second electrode layers formed on said first and second sides respectively; said first electrode layer being in communication with said exhaust gases, said second layer being in communication with a reference gas, said porous coating being formed only on said first electrode layer which is exposed to, and in communication with, said exhaust gases, said method comprising the steps of: applying by plasma-spraying fine particles of a heat-resistant and chemically stable first material selected from the group consisting of alumina, spinel, alumina cement, beryllia, zirconia, nickel oxide, silicon carbide, boron carbide and boron nitride onto the outer surface of the electrode layer to form a porous layer, the particle size of said fine particles being in the range from 5 to 50 microns; impregnating said porous layer with at least one aqueous dispersion system selected from the group consisting of alumina sol, silica sol and an aqueous dispersion of fine particles of alumina; and baking the impregnated porous layer to turn said at least one dispersion system into a solid matrix which consists essentially of at least one of alumina and silica and is intimately fixed to said porous layer, said plasma-spraying of said first material and the impregnation with said at least one dispersion system being performed such that said porous coating has a thickness in the range from 5.0 to 500 microns after the completion of the baking step and that the total pore volume in the porous coating after the completion of the baking step ranges from 0.09 to 0.16 cm 3 per one gram of the porous coating.
Claim 8
Independent Claim
310 words
A method of forming a porous coating on an electrode layer of an oxygen sensor, said sensor comprising a layer of a solid oxygen-ion electrolyte for use in a combustion engine exhaust gas, said layer of said solid electrolyte having first and second sides and having first and second electrode layers formed on said first and second sides respectively; said first electrode layer being in communication with said exhaust gases, said second layer being in communication with a reference gas, said porous coating being formed only on said first electrode layer which is exposed to, and in communication with, said exhaust gases, said method comprising the steps of: applying by plasma-spraying fine particles of a heat-resistant and chemically stable first material selected from the group consisting of alumina, spinel, alumina cement, beryllia, zirconia, nickel oxide, silicon carbide, boron carbide and boron nitride onto the outer surface of the electrode layer to form a porous layer, the particle size of said fine particles being in the range from 5 to 50 microns; impregnating said porous layer with at least one aqueous dispersion system selected from the group consisting of alumina sol, silica sol and an aqueous dispersion of fine particles of alumina; and baking the impregnated porous layer to turn said at least one dispersion system into a solid matrix which consists essentially of at least one of alumina and silica and is intimately fixed to said porous layer, said plasma-spraying of said first material and the impregnation with said at least one dispersion system being performed such that said porous coating has a thickness in the range from 5.0 to 500 microns after the completion of the baking step and that the total pore volume in the porous coating after the completion of the baking step ranges from 0.09 to 0.16 cm 3 per one gram of the porous coating.
Claim 9
Dependent Claim
23 words
The method in accordance with claim 6 wherein said at least one dispersion system is applied to said porous layer by vacuum impregnation.
Claim 10
Dependent Claim
228 words
In an oxygen sensor for detecting a variation in the oxygen concentration in a combustion engine exhaust gas, the sensor having a solid oxygen-ion electrolyte layer, a first electrode layer formed on one side of the electrolyte layer to be exposed to the exhaust gas, a second electrode layer formed on the other side of the electrolyte layer, and a porous coating of a heat-resistant and chemically stable material which comprises at least one of alumina and silica and is formed on the outside of the first electrode layer, the improvement comprising said porous coating consisting of a first porous matrix which is formed by plasma-spraying fine particles of a first material selected from the group consisting of alumina, spinel, alumina cement, beryllia, zirconia, nickel oxide, silicon carbide, boron carbide and boron nitride onto the outer surface of the first electrode layer, the particle size of said fine particles being in the range from 5 to 50 microns, and a second matrix which consists essentially of at least one of alumina and silica and is formed by impregnating said first matrix with at least one aqueous dispersion system selected from the group consisting of alumina sol, silica sol, and an aqueous dispersion of fine particles of alumina and then baking the impregnated first matrix, said porous coating having a thickness in the range from 5 to 500 microns.
Claim 11
Dependent Claim
228 words
In an oxygen sensor for detecting a variation in the oxygen concentration in a combustion engine exhaust gas, the sensor having a solid oxygen-ion electrolyte layer, a first electrode layer formed on one side of the electrolyte layer to be exposed to the exhaust gas, a second electrode layer formed on the other side of the electrolyte layer, and a porous coating of a heat-resistant and chemically stable material which comprises at least one of alumina and silica and is formed on the outside of the first electrode layer, the improvement comprising said porous coating consisting of a first porous matrix which is formed by plasma-spraying fine particles of a first material selected from the group consisting of alumina, spinel, alumina cement, beryllia, zirconia, nickel oxide, silicon carbide, boron carbide and boron nitride onto the outer surface of the first electrode layer, the particle size of said fine particles being in the range from 5 to 50 microns, and a second matrix which consists essentially of at least one of alumina and silica and is formed by impregnating said first matrix with at least one aqueous dispersion system selected from the group consisting of alumina sol, silica sol, and an aqueous dispersion of fine particles of alumina and then baking the impregnated first matrix, said porous coating having a thickness in the range from 5 to 500 microns.
Claim 12
Dependent Claim
32 words
An oxygen sensor according to claim 8 wherein the total pore volume in said porous coating ranges from between about 0.09 to 0.16 cm 2 per one gram of said porous coating.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-26 | 1981-12-26 | 1982-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-26 | 1985-12-26 | 1986-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-26 | 1989-12-26 | 1990-06-27 | $7700.00 | Window Closed / Lapsed |