Coated silicon-iron product and process therefor
Assignee: General Electric Co
•
Filing: 1977-03-07
•
Granted: 1978-06-27
•
Expires: 1997-03-07
Abstract
Abstract A boron-containing electrical steel sheet is provided with an electrolytically-deposited boron-containing Mg(OH) 2 primary coating about 0.05 mil thick and a secondary coating of electrolytically-deposited Mg(OH) 2 about 0.15 mil thick.
Inventors
- 👤 Ronald H. Arendt
- 👤 Matthew J. Curran
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 05:47
CPC Classifications
C; C25; C25D; C25D9/00; C25D9/04; C25D9/08; C25D9/10; C25D5/00; C25D5/48; C25D5/50; H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/147; H01F1/14766; H01F1/14775; H01F1/14783
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
184 words
The method of producing grain-oriented silicon-iron sheet which comprises the steps of providing a finegrained primary-recrystallized silicon-iron sheet containing 2.2 to 4.5 percent silicon, between about three and 50 parts per million boron, and between about 15 and 95 parts per million nitrogen in the ratio to boron of one to 15 parts per part of boron, electrolyzing a solid MgO containing aqueous solution consisting essentially of magnesium acetate and magnesium metaborate and containing magnesia with the silicon-iron sheet being arranged as the cathode in said solution and the said solution being at a temperature of at least about 65° C and thereby covering the sheet with a boron-containing adherent electrically-insulating but relatively thin coating of Mg(OH) 2 , and then electrolyzing a solid MgO-containing aqueous solution consisting essentially of magnesium acetate with the resulting coated sheet arranged as the cathode in the said magnesium acetate solution and thereby covering the boroncontaining Mg(OH) 2 coating with a substantially thicker Mg(OH) 2 coating, and thereafter subjecting the resulting double-coated sheet to a final heat treatment to develop (110) secondary recrystallization texture in the silicon-iron sheet.
Claim 2
Independent Claim
184 words
The method of producing grain-oriented silicon-iron sheet which comprises the steps of providing a finegrained primary-recrystallized silicon-iron sheet containing 2.2 to 4.5 percent silicon, between about three and 50 parts per million boron, and between about 15 and 95 parts per million nitrogen in the ratio to boron of one to 15 parts per part of boron, electrolyzing a solid MgO containing aqueous solution consisting essentially of magnesium acetate and magnesium metaborate and containing magnesia with the silicon-iron sheet being arranged as the cathode in said solution and the said solution being at a temperature of at least about 65° C and thereby covering the sheet with a boron-containing adherent electrically-insulating but relatively thin coating of Mg(OH) 2 , and then electrolyzing a solid MgO-containing aqueous solution consisting essentially of magnesium acetate with the resulting coated sheet arranged as the cathode in the said magnesium acetate solution and thereby covering the boroncontaining Mg(OH) 2 coating with a substantially thicker Mg(OH) 2 coating, and thereafter subjecting the resulting double-coated sheet to a final heat treatment to develop (110) secondary recrystallization texture in the silicon-iron sheet.
Claim 3
Dependent Claim
26 words
The method of claim 1 in which the electrolyzing is carried out with an electrolyte consisting of an aqueous magnesium acetate-borate solution containing solid magnesium hydroxide.
Claim 4
Dependent Claim
23 words
The method of claim 2 in which the electrolyte contains 0.2 mole of magnesium acetate and has a pH from 8.0 to 8.5.
Claim 5
Dependent Claim
36 words
The method of claim 1 in which the boron containing initial or primary coating is about 0.02 to 0.07 mil thick and the Mg(OH) 2 secondary layer or overcoat is about 0.10 to 0.18 mil thick.
Claim 6
Dependent Claim
22 words
The method of claim 4 in which the total thickness of the electrically-insulating coatings is between about 0.10 and 0.40 mil thick.
Claim 7
Dependent Claim
19 words
The method of claim 4 in which the total thickness of the two electrolytically-deposited coatings is about 0.20 mil.
Claim 8
Dependent Claim
26 words
The method of claim 1 in which the electrolyte is maintained at a temperature between about 90° and 95° C throughout the period of electrolytic codeposition.
Claim 9
Dependent Claim
11 words
The double-coated, primary-recrystallized silicon-iron sheet of the process of claim 1.
References Cited (Backward Citations)
US3054732A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-26 | 1981-12-26 | 1982-06-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-26 | 1985-12-26 | 1986-06-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-26 | 1989-12-26 | 1990-06-27 | $7700.00 | Window Closed / Lapsed |