Protective lubricating compositions for recordings
Assignee: BAE Systems Space & Mission Systems Inc
•
Filing: 1976-09-10
•
Granted: 1978-06-20
•
Expires: 1996-09-10
Abstract
Abstract An article of manufacture and a method are disclosed herein for improving lubricity and wear resistance of a given substrate by applying thereto a composition consisting essentially of low-molecular weight tetrafluoroethylene telomers, an antistatic agent, preferably in the form of a tertiary amine, and a volatile organic solvent, and removing the volatile solvent to produce a thin, dry coating upon said substrate. The compositions herein disclosed have been found to be most effective as preservatives for coating gramophone or phonograph records which provide marked reduction of record groove wear while substantially minimizing noise and harmonic distortion.
Inventors
- 👤 Robert P. Pardee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 15:21
CPC Classifications
B; B05; B05D; B05D5/00; B05D5/08; G; G11; G11B; G11B23/00; G11B23/50; G11B23/505; G11B3/00; G11B3/58; G11B3/589; C; C10; C10M; C10M2207/00; C10M2207/28; C10M2207/281; C10M2207/282; C10M2207/283; C10M2207/286; C10M2209/00; C10M2209/10; C10M2209/103; C10M2209/104; C10M2211/00; C10M2211/06; C10M2213/00; C10M2213/02; C10M2213/06; C10M2213/062; C10M2215/00; C10M2215/02; C10M2215/04; C10M2215/042; C10M2215/24; C10M2215/26; C10M2223/00; C10M2223/02; C10M2223/04; C10M2223/042; C10N; C10N2040/00; C10N2040/30; C10N2040/32; C10N2040/34; C10N2040/36; C10N2040/38; C10N2040/40; C10N2040/42; C10N2040/44; C10N2040/50; C10N2050/00; C10N2050/015; C10N2050/02; Y; Y10; Y10S; Y10S428/00; Y10S428/90
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
208 words
A composition for imparting wear resistance and lubricity to a substrate upon which recorded signals have been stored and from which said signals can be recalled by dynamic means, said composition consisting essentially of an essentially homogeneous halogenated organic solution of a major proportion of an inert halogenated solvent, a low-molecular weight tetrafluoroethylene telomer, said telomer being a member selected from the group consisting of: R(CF.sub.2 --CF.sub.2).sub.a X wherein R is a haloalkyl containing 1 to 4 carbon atoms, X is a member selected from the group consisting of chlorine, iodine and fluorine and a is an integer from about 6 to about 16, and R'(CF.sub.2 --CF.sub.2).sub.b Y wherein R' is a hydrogen-containing moiety of a telogen, said telogen being a tertiary hydrocarbon, Y is a member selected from the group consisting of chlorine and chlorofluoroalkyl, and b is an integer from about 3 to about 8, said telomer being present in an amount of about 0.001 to 2.0 weight percent based on the total weight of said composition, and an antistatic agent selected from the group consisting of tertiary amines, fatty quaternary ammonium compounds, fatty esters, phosphate esters and polyethylene glycols, said antistatic agent being present in an amount effective to substantially reduce or remove electrostatic charge.
Claim 2
Dependent Claim
208 words
A composition for imparting wear resistance and lubricity to a substrate upon which recorded signals have been stored and from which said signals can be recalled by dynamic means, said composition consisting essentially of an essentially homogeneous halogenated organic solution of a major proportion of an inert halogenated solvent, a low-molecular weight tetrafluoroethylene telomer, said telomer being a member selected from the group consisting of: R(CF.sub.2 --CF.sub.2).sub.a X wherein R is a haloalkyl containing 1 to 4 carbon atoms, X is a member selected from the group consisting of chlorine, iodine and fluorine and a is an integer from about 6 to about 16, and R'(CF.sub.2 --CF.sub.2).sub.b Y wherein R' is a hydrogen-containing moiety of a telogen, said telogen being a tertiary hydrocarbon, Y is a member selected from the group consisting of chlorine and chlorofluoroalkyl, and b is an integer from about 3 to about 8, said telomer being present in an amount of about 0.001 to 2.0 weight percent based on the total weight of said composition, and an antistatic agent selected from the group consisting of tertiary amines, fatty quaternary ammonium compounds, fatty esters, phosphate esters and polyethylene glycols, said antistatic agent being present in an amount effective to substantially reduce or remove electrostatic charge.
Claim 3
Dependent Claim
208 words
A composition for imparting wear resistance and lubricity to a substrate upon which recorded signals have been stored and from which said signals can be recalled by dynamic means, said composition consisting essentially of an essentially homogeneous halogenated organic solution of a major proportion of an inert halogenated solvent, a low-molecular weight tetrafluoroethylene telomer, said telomer being a member selected from the group consisting of: R(CF.sub.2 --CF.sub.2).sub.a X wherein R is a haloalkyl containing 1 to 4 carbon atoms, X is a member selected from the group consisting of chlorine, iodine and fluorine and a is an integer from about 6 to about 16, and R'(CF.sub.2 --CF.sub.2).sub.b Y wherein R' is a hydrogen-containing moiety of a telogen, said telogen being a tertiary hydrocarbon, Y is a member selected from the group consisting of chlorine and chlorofluoroalkyl, and b is an integer from about 3 to about 8, said telomer being present in an amount of about 0.001 to about 2.0 weight percent based on the total weight of said composition, and as an antistatic agent, a tertiary amine of the formula: ##STR3## wherein R" is an alkyl group having from about 4 to 20 carbon atoms present in an amount effective to substantially reduce or remove electrostatic charge.
Claim 4
Dependent Claim
208 words
A composition for imparting wear resistance and lubricity to a substrate upon which recorded signals have been stored and from which said signals can be recalled by dynamic means, said composition consisting essentially of an essentially homogeneous halogenated organic solution of a major proportion of an inert halogenated solvent, a low-molecular weight tetrafluoroethylene telomer, said telomer being a member selected from the group consisting of: R(CF.sub.2 --CF.sub.2).sub.a X wherein R is a haloalkyl containing 1 to 4 carbon atoms, X is a member selected from the group consisting of chlorine, iodine and fluorine and a is an integer from about 6 to about 16, and R'(CF.sub.2 --CF.sub.2).sub.b Y wherein R' is a hydrogen-containing moiety of a telogen, said telogen being a tertiary hydrocarbon, Y is a member selected from the group consisting of chlorine and chlorofluoroalkyl, and b is an integer from about 3 to about 8, said telomer being present in an amount of about 0.001 to about 2.0 weight percent based on the total weight of said composition, and as an antistatic agent, a tertiary amine of the formula: ##STR3## wherein R" is an alkyl group having from about 4 to 20 carbon atoms present in an amount effective to substantially reduce or remove electrostatic charge.
Claim 5
Dependent Claim
30 words
The composition of claim 2 wherein said antistatic agent is present in an amount of about 0.001 to about 1.0 weight percent based on the total weight of the composition.
Claim 6
Dependent Claim
19 words
The composition of claim 2 wherein said tertiary amine has a molecular weight between about 150 and about 400.
Claim 7
Dependent Claim
11 words
The composition of claim 2 wherein said tertiary amine is N,N-bis(2-hydroxyethyl)dodecylamine.
Claim 8
Dependent Claim
11 words
The composition of claim 2 wherein said tertiary amine is N,N-bis(2-hydroxyethyl)tridecylamine.
Claim 9
Dependent Claim
11 words
The composition of claim 2 wherein said tertiary amine is N,N-bis(2-hydroxyethyl)tetradecylamine.
Claim 10
Dependent Claim
27 words
The composition of claim 2 wherein the tetrafluoroethylene telomer having the structural formula: R'(CF.sub.2 --CF.sub.2).sub.b Y has b as an integer from about 3 to about 6.
Claim 11
Dependent Claim
28 words
The composition of claim 2 wherein said tetrafluoroethylene telomer is present in an amount of about 0.005 to about 0.15 based on the total weight of said composition.
Claim 12
Dependent Claim
207 words
A composition for imparting wear resistance and lubricity to a substrate upon which recorded signals have been stored and from which said signals can be recalled by dynamic means, said composition consisting of an essentially homogeneous halogenated organic solution of a major proportion of an inert halogenated solvent, a low-molecular weight tetrafluoroethylene telomer, said telomer being a member selected from the group consisting of: R(CF.sub.2 --CF.sub.2).sub.a X wherein R is a haloalkyl containing 1 to 4 carbon atoms, X is a member selected from the group consisting of chlorine, iodine and fluorine and a is an integer from about 6 to about 16, and R'(CF.sub.2 --CF.sub.2).sub.b Y wherein R' is a hydrogen containing moiety of a telogen, said telogen being a tertiary hydrocarbon, Y is a member selected from the group consisting of chlorine and chlorofluoroalkyl, and b is an integer from 3 to about 8, said telomer being present in an amount of about 0.001 to about 2.0 weight percent based on the total weight of said composition and as an antistatic agent, a tertiary amine of the formula: ##STR4## wherein R" is an alkyl group having from about 4 to 20 carbon atoms present in an amount effective to substantially reduce or remove electrostatic charge.
Claim 13
Dependent Claim
207 words
A composition for imparting wear resistance and lubricity to a substrate upon which recorded signals have been stored and from which said signals can be recalled by dynamic means, said composition consisting of an essentially homogeneous halogenated organic solution of a major proportion of an inert halogenated solvent, a low-molecular weight tetrafluoroethylene telomer, said telomer being a member selected from the group consisting of: R(CF.sub.2 --CF.sub.2).sub.a X wherein R is a haloalkyl containing 1 to 4 carbon atoms, X is a member selected from the group consisting of chlorine, iodine and fluorine and a is an integer from about 6 to about 16, and R'(CF.sub.2 --CF.sub.2).sub.b Y wherein R' is a hydrogen containing moiety of a telogen, said telogen being a tertiary hydrocarbon, Y is a member selected from the group consisting of chlorine and chlorofluoroalkyl, and b is an integer from 3 to about 8, said telomer being present in an amount of about 0.001 to about 2.0 weight percent based on the total weight of said composition and as an antistatic agent, a tertiary amine of the formula: ##STR4## wherein R" is an alkyl group having from about 4 to 20 carbon atoms present in an amount effective to substantially reduce or remove electrostatic charge.
Claim 14
Dependent Claim
30 words
The composition of claim 10 wherein said antistatic agent is present in an amount of about 0.001 to about 1.0 weight percent based on the total weight of the composition.
Claim 15
Dependent Claim
19 words
The composition of claim 10 wherein said tertiary amine has a molecular weight between about 150 and about 400.
Claim 16
Dependent Claim
11 words
The composition of claim 10 wherein said tertiary amine is N,N-bis(2-hydroxyethyl)dodecylamine.
Claim 17
Dependent Claim
11 words
The composition of claim 10 wherein said tertiary amine is N,N-bis(2-hydroxyethyl)tridecylamine.
Claim 18
Dependent Claim
11 words
The composition of claim 10 wherein said tertiary amine is N,N-bis(2-hydroxyethyl)tetradecylamine.
Claim 19
Dependent Claim
27 words
The composition of claim 10 wherein the tetrafluoroethylene telomer having the structural formula: R'(CF.sub.2 --CF.sub.2).sub.b Y has b as an integer from about 3 to about 6.
Claim 20
Dependent Claim
28 words
The composition of claim 10 wherein said tetrafluoroethylene telomer is present in an amount of about 0.005 to about 0.15 based on the total weight of said composition.
Claim 21
Dependent Claim
114 words
A composition of matter capable of imparting wear resistance and lubricity to the playing surface of a phonograph record consisting essentially of an essentially homogeneous halogenated organic solution of a major proportion of an inert halogenated solvent, tetrafluoroethylene telomers having maximum average molecular weight of about 1800 or less, said inert halogenated solvent being a member selected from the group consisting of trichlorotrifluorethane, trichlorethane, benzotrifluoride, perfluorodimethylcyclobutane, chloroform, tetrachloroethylene, trichloroethylene, methylene chloride, carbon tetrachloride, dichloroethylene and dichloroethane, and an antistatic agent selected from the group consisting of tertiary amines, fatty quaternary ammonium compounds, fatty esters, phosphate esters and polyethylene glycols, said agent being present in an amount effective to substantially reduce or remove electrostatic charge.
Claim 22
Dependent Claim
114 words
A composition of matter capable of imparting wear resistance and lubricity to the playing surface of a phonograph record consisting essentially of an essentially homogeneous halogenated organic solution of a major proportion of an inert halogenated solvent, tetrafluoroethylene telomers having maximum average molecular weight of about 1800 or less, said inert halogenated solvent being a member selected from the group consisting of trichlorotrifluorethane, trichlorethane, benzotrifluoride, perfluorodimethylcyclobutane, chloroform, tetrachloroethylene, trichloroethylene, methylene chloride, carbon tetrachloride, dichloroethylene and dichloroethane, and an antistatic agent selected from the group consisting of tertiary amines, fatty quaternary ammonium compounds, fatty esters, phosphate esters and polyethylene glycols, said agent being present in an amount effective to substantially reduce or remove electrostatic charge.
Claim 23
Dependent Claim
114 words
A composition of matter capable of imparting wear resistance and lubricity to the playing surface of a phonograph record consisting of an essentially homogeneous halogenated organic solution of a major proportion of an inert halogenated solvent tetrafluoroethylene telomers having a maximum average molecular weight of about 1800 or less, said inert halogenated solvent being a member selected from the group consisting of trichlorotrifluoroethane, trichloroethane, benzotrifluoride, perfluorodimethylcyclobutane, chloroform, tetrachloroethylene, trichloroethylene, methylene chloride, carbon tetrachloride, dichloroethylene and dichloroethane, and an antistatic agent selected from the group consisting of tertiary amines, fatty quaternary ammonium compounds, fatty esters, phosphate esters and polyethylene glycols, said agent being present in an amount effective to substantially reduce or remove electrostatic charge.
Claim 24
Dependent Claim
114 words
A composition of matter capable of imparting wear resistance and lubricity to the playing surface of a phonograph record consisting of an essentially homogeneous halogenated organic solution of a major proportion of an inert halogenated solvent tetrafluoroethylene telomers having a maximum average molecular weight of about 1800 or less, said inert halogenated solvent being a member selected from the group consisting of trichlorotrifluoroethane, trichloroethane, benzotrifluoride, perfluorodimethylcyclobutane, chloroform, tetrachloroethylene, trichloroethylene, methylene chloride, carbon tetrachloride, dichloroethylene and dichloroethane, and an antistatic agent selected from the group consisting of tertiary amines, fatty quaternary ammonium compounds, fatty esters, phosphate esters and polyethylene glycols, said agent being present in an amount effective to substantially reduce or remove electrostatic charge.
Claim 25
Dependent Claim
144 words
A composition of matter capable of imparting wear resistance and lubricity to the playing surface of a phonograph record consisting essentially of an essentially homogeneous, halogenated organic solution of a major proportion of an inert halogenated solvent tetrafluoroethylene telomers having maximum average molecular weight of about 1800 or less, the concentration of said telomers being about 0.001 to about 2.0 weight percent based on the total weight of the solution, said inert halogenated solvent being a member selected from the group consisting of trichlorotrifluoroethane, trichloroethane, benzotrifluoroide, perfluorodimethylcyclobutane, chloroform, tetrachloroethylene, trichlorethylene, methylene chloride, carbon tetrachloride, dichloroethylene and dichloroethane, and an antistatic agent selected from the group consisting of tertiary amines, fatty quaternary ammonium compounds, fatty esters, phosphate esters and polyethylene glycols, said agent being present in an amount from about 0.001 to about 1.0 weig ht percent based on the total weight of the solution.
Claim 26
Dependent Claim
144 words
A composition of matter capable of imparting wear resistance and lubricity to the playing surface of a phonograph record consisting essentially of an essentially homogeneous, halogenated organic solution of a major proportion of an inert halogenated solvent tetrafluoroethylene telomers having maximum average molecular weight of about 1800 or less, the concentration of said telomers being about 0.001 to about 2.0 weight percent based on the total weight of the solution, said inert halogenated solvent being a member selected from the group consisting of trichlorotrifluoroethane, trichloroethane, benzotrifluoroide, perfluorodimethylcyclobutane, chloroform, tetrachloroethylene, trichlorethylene, methylene chloride, carbon tetrachloride, dichloroethylene and dichloroethane, and an antistatic agent selected from the group consisting of tertiary amines, fatty quaternary ammonium compounds, fatty esters, phosphate esters and polyethylene glycols, said agent being present in an amount from about 0.001 to about 1.0 weig ht percent based on the total weight of the solution.
Claim 27
Dependent Claim
142 words
A composition of matter capable of imparting wear resistance and lubricity to the playing surface of a phonograph record consisting of an essentially homogeneous, halogenated organic solution of a major proportion of an inert halogenated solvent tetrafluoroethylene telomers having maximum average molecular weight of about 1800 or less, the concentration of said telomers being about 0.001 to about 2.0 weight percent based on the total weight of the solution, said inert halogenated solvent being a member selected from the group consisting of trichlorotrifluoroethane, trichloroethane, benzotrifluoride, perfluorodimethylcyclobutane, chloroform, tetrachloroethylene, trichlorethylene, methylene chloride, carbon tetrachloride, dichlorethylene and dichloroethane, and an antistatic agent selected from the group consisting of tertiary amines, fatty quaternary ammonium compounds, fatty esters, phosphate esters and polyethylene glycols, said agent being present in an amount from about 0.001 to about 1.0 weight percent based on the total weight of the solution.
Claim 28
Dependent Claim
142 words
A composition of matter capable of imparting wear resistance and lubricity to the playing surface of a phonograph record consisting of an essentially homogeneous, halogenated organic solution of a major proportion of an inert halogenated solvent tetrafluoroethylene telomers having maximum average molecular weight of about 1800 or less, the concentration of said telomers being about 0.001 to about 2.0 weight percent based on the total weight of the solution, said inert halogenated solvent being a member selected from the group consisting of trichlorotrifluoroethane, trichloroethane, benzotrifluoride, perfluorodimethylcyclobutane, chloroform, tetrachloroethylene, trichlorethylene, methylene chloride, carbon tetrachloride, dichlorethylene and dichloroethane, and an antistatic agent selected from the group consisting of tertiary amines, fatty quaternary ammonium compounds, fatty esters, phosphate esters and polyethylene glycols, said agent being present in an amount from about 0.001 to about 1.0 weight percent based on the total weight of the solution.
References Cited (Backward Citations)
US2411159A
Cited
US3105824A
Cited
US3067262A
Cited
US3862860A
Cited
US3954637A
Cited
US3998989A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-19 | 1981-12-19 | 1982-06-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-19 | 1985-12-19 | 1986-06-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-19 | 1989-12-19 | 1990-06-20 | $7700.00 | Window Closed / Lapsed |