High duty ductile cast iron with superplasticity and its heat treatment methods
Assignee: Riken Piston Ring Industrial Co Ltd
•
Filing: 1975-06-04
•
Granted: 1978-06-20
•
Expires: 1995-06-04
Abstract
Abstract A spheroidal graphite cast iron containing some carbide stabilizing elements to have the maximum strain rate sensitivity factor of more than 0.3 and having very refined grain matrix structure, so that having an improved toughness at room temperature and having a matrix which is composed of fine austenite and fine ferrite grains and superplastic properties at the temperature between the eutectoid transformation temperature range and 50 DEG C higher than that temperature range; and the method of heat treatment to obtain the said spheroidal graphite cast iron.
Inventors
- 👤 Katsuya Ikawa
- 👤 Yuichi Tanaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 18:28
CPC Classifications
C; C21; C21D; C21D8/00; C21D5/00; Y; Y10; Y10S; Y10S420/00; Y10S420/902
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
100 words
A ductile cast iron; having a structure comprising a grain refined matrix and the spheroidal graphites, said matrix being composed substantially of ferrite and fine cementite particles in said ferrite room temperature and composed substantially of fine austenite and fine ferrite grains at the temperature ranging from eutectoid temperature to about 50° C above the eutectoid temperature, and containing enough amount of at least one of carbide stabilizing elements to obtain maximum strain rate sensitivity factor of more than 0.3 on the deformation at the temperature ranging from the eutectoid temperature to about 50° C high above that eutectoid temperature.
Claim 2
Dependent Claim
100 words
A ductile cast iron; having a structure comprising a grain refined matrix and the spheroidal graphites, said matrix being composed substantially of ferrite and fine cementite particles in said ferrite room temperature and composed substantially of fine austenite and fine ferrite grains at the temperature ranging from eutectoid temperature to about 50° C above the eutectoid temperature, and containing enough amount of at least one of carbide stabilizing elements to obtain maximum strain rate sensitivity factor of more than 0.3 on the deformation at the temperature ranging from the eutectoid temperature to about 50° C high above that eutectoid temperature.
Claim 3
Dependent Claim
30 words
The ductile cast iron of claim 1, in which said structure of matrix being composed of ferrite and very fine grained cementite particles dispersed in said ferrite at room temperature.
Claim 4
Dependent Claim
31 words
The ductile cast iron of claim 1, in which said structure of matrix being hemp leaf-like pearlite structure composed of ferrite with very fine cementite particles deposited therein at room temperature.
Claim 5
Dependent Claim
17 words
The ductile cast iron of claim 1, in which said carbide stabilizing elements include manganese and molybdenum.
Claim 6
Dependent Claim
20 words
The ductile cast iron of claim 1, in which is contained 0.4 - 1.5% manganese as the carbide stabilizing element.
Claim 7
Dependent Claim
93 words
A ductile cast iron which has a tensile strength of more than 75 Kg/mm 2 and elongation of more than 5% due to its grain refined matrix structure substantially composed of ferrite and fine cementite particles distributed therein, said ductile cast iron has a common chemical composition as that of ordinary ductile cast iron, but with some cementite stabilizing element to obtain a maximum strain rate sensitivity factor of more than 0.3 on the deformation at the temperature ranging from eutectoid temperature range to about 50° C high above that eutectoid temperature range.
Claim 8
Dependent Claim
93 words
A ductile cast iron which has a tensile strength of more than 75 Kg/mm 2 and elongation of more than 5% due to its grain refined matrix structure substantially composed of ferrite and fine cementite particles distributed therein, said ductile cast iron has a common chemical composition as that of ordinary ductile cast iron, but with some cementite stabilizing element to obtain a maximum strain rate sensitivity factor of more than 0.3 on the deformation at the temperature ranging from eutectoid temperature range to about 50° C high above that eutectoid temperature range.
Claim 9
Dependent Claim
48 words
A method of heat treatment to obtain the ductile cast iron of claim 1, in case a martensitic structure is not formed in said matrix by air cooling from the austenite temperature range; comprising repeated cycles of rapid heating to the austenite temperature range followed by air cooling.
Claim 10
Dependent Claim
55 words
A method of heat treatment to obtain the ductile cast iron of claim 1, in case a martensitic structure is formed in said matrix by air cooling from the austenite temperature range; comprising successive steps of (i) heating to said austenite temperature range followed by air cooling, and (ii) tempering at the eutectoid temperature range.
Claim 11
Dependent Claim
30 words
The ductile cast iron of claim 1, having a tensile strength of more than 75 Kg/mm 2 and elongation of more than 5% due to its very fine pearlite matrix.
References Cited (Backward Citations)
US3000770A
Cited
US3013911A
Cited
US2796373A
Cited
US3005736A
Cited
US3155498A
Cited
US3850699A
Cited
US3860457A
Cited
US3893873A
Cited
US3951697A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-19 | 1981-12-19 | 1982-06-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-19 | 1985-12-19 | 1986-06-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-19 | 1989-12-19 | 1990-06-20 | $7700.00 | Window Closed / Lapsed |