Magnetohydrodynamic electrode
Assignee: United States Department of Energy
•
Filing: 1977-03-01
•
Granted: 1978-06-06
•
Expires: 1997-03-01
Abstract
Abstract An electrode capable of withstanding high temperatures and suitable for use as a current collector in the channel of a magnetohydrodynamic (MHD) generator consists of a sintered powdered metal base portion, the upper surface of the base being coated with a first layer of nickel aluminide, an intermediate layer of a mixture of nickel aluminide - refractory ceramic on the first layer and a third or outer layer of a refractory ceramic material on the intermediate layer. The sintered powdered metal base resists spalling by the ceramic coatings and permits greater electrode compliance to thermal shock. The density of the powdered metal base can be varied to allow optimization of the thermal conductivity of the electrode and prevent excess heat loss from the channel.
Inventors
- 👤 David D. Marchant
- 👤 Don H. Killpatrick
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 11:14
CPC Classifications
B; B22; B22F; B22F7/00; B22F7/002; H; H02; H02K; H02K44/00; H02K44/08; H02K44/10
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
96 words
An electrode for use in a magnetohydrodynamic generator comprising: a base portion of sintered powdered metal having a predetermined density, the base having a lower surface for attaching the electrode to a magnetohydrodynamic generator, two parallel side walls and an upper surface; a first layer of nickel aluminide on the upper surface; an intermediate layer of nickel aluminide and refractory ceramic on the first layer, the refractory ceramic being electrically conductive at MHD operating temperature; and an outer layer of refractory ceramic on the intermediate layer, the refractory ceramic being electrically conductive at MHD operating temperatures.
Claim 2
Dependent Claim
96 words
An electrode for use in a magnetohydrodynamic generator comprising: a base portion of sintered powdered metal having a predetermined density, the base having a lower surface for attaching the electrode to a magnetohydrodynamic generator, two parallel side walls and an upper surface; a first layer of nickel aluminide on the upper surface; an intermediate layer of nickel aluminide and refractory ceramic on the first layer, the refractory ceramic being electrically conductive at MHD operating temperature; and an outer layer of refractory ceramic on the intermediate layer, the refractory ceramic being electrically conductive at MHD operating temperatures.
Claim 3
Dependent Claim
20 words
The electrode of claim 1 wherein the side walls are coated with a layer of refractory ceramic electrical insulating material.
Claim 4
Dependent Claim
23 words
The electrode of claim 2 wherein the base is prepared of an electrically conductive, nonferromagnetic, oxidation-resistant metal or alloy melting above 1000° C.
Claim 5
Dependent Claim
21 words
The electrode of claim 3 wherein the density of the base is from 60 to about 100% of the theoretical density.
Claim 6
Dependent Claim
32 words
The electrode of claim 4 wherein the refractory ceramic is selected from the group consisting of stabilized zirconium oxide, stabilized hafnium oxide, iron-doped spinel, chromium-doped spinel, yttrium oxide and strontium-doped lanthanum chromite.
Claim 7
Dependent Claim
31 words
The electrode of claim 5 wherein the sintered powdered metal is selected from the group consisting of stainless steel, niobium, hafnium, tantalum, molybdenum, and alloys of niobium-zirconium, hafnium-tantalum, nickel-chromium and nickel-molybdenum.
Claim 8
Dependent Claim
26 words
The electrode of claim 6 wherein the intermediate layer consists of 25 to 75 weight percent nickel aluminide and 25 to 75 weight percent refractory ceramic.
Claim 9
Dependent Claim
28 words
The electrode of claim 7 wherein the refractory ceramic electrical insulating material is selected from the group consisting of spinel, magnesium oxide, alumina, strontium zirconate or calcium zirconate.
Claim 10
Dependent Claim
37 words
The electrode of claim 1 wherein the first, intermediate and outer layers extend over the two side walls and the outer layers on the side walls are coated with a layer of refractory ceramic electrical insulating material.
Claim 11
Dependent Claim
67 words
The electrode of claim 1 wherein the two side walls consist of an upstream side wall and a downstream side wall relative to the plasma flow in an MHD generator, the first, intermediate and outer layers extend over the upstream side wall and the outer layer on the upstream side wall and the downstream side wall are coated with a layer of refractory ceramic electrical insulating material.
Claim 12
Dependent Claim
80 words
The electrode of claim 10 wherein the base of the electrode is attached to an intermediate mounting plate of copper, the bottom edges of the first, intermediate and outer layers and the refractory insulating material on the upstream side contact the mounting plate, the downstream side wall of the electrode contains a layer of copper and an outer layer of refractory ceramic electrical insulating material, the bottom edges of the copper layer and the refractory ceramic contact the mounting plate.
References Cited (Backward Citations)
US3149253A
Cited
US3274408A
Cited
US3280349A
Cited
US3430082A
Cited
US3454798A
Cited
US3531421A
Cited
US3574144A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-05 | 1981-12-05 | 1982-06-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-05 | 1985-12-05 | 1986-06-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-05 | 1989-12-05 | 1990-06-06 | $7700.00 | Window Closed / Lapsed |