Treating a polymeric shape with nonionic fluorochemical surfactants and product therefrom
Assignee: Diamond Shamrock Chemicals Co
•
Filing: 1976-04-27
•
Granted: 1978-06-06
•
Expires: 1996-04-27
Abstract
Abstract 6-Hydroxyhexyl perfluoroisopropyl ether is prepared by reaction of hexafluoroacetone and potassium fluoride to obtain an alcoholate which is then reacted with 1-chloro-6-hexanol. One mole of the ether may be reacted with about 1 mole to about 20 moles of ethylene oxide. One mole of 2,2,3,4,4,4-hexafluorobutanol may also be reacted with about 1 mole to about 6 moles of propylene oxide and then about 1 mole to about 20 moles of ethylene oxide. Both ethoxylates are nonionic surfactants which are useful as antistatic agents and lubricants for polymeric shapes such as nylon films and filaments.
Inventors
- 👤 Alex J. Szur
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 20:55
CPC Classifications
D; D06; D06M; D06M13/00; D06M13/10; D06M13/165; C; C07; C07C; C07C29/00; C07C29/68; C07C31/00; C07C31/34; C07C31/40; C07C43/00; C07C43/02; C07C43/03; C07C43/04; C07C43/13; C07C43/135; C07C43/137; C08; C08G; C08G65/00; C08G65/02; C08G65/26; C08G65/2639; C08L; C08L77/00; C09; C09K; C09K23/00; C09K23/007; Y; Y10; Y10S; Y10S260/00; Y10S260/15; Y10S260/19; Y10S260/21; Y10T; Y10T428/00; Y10T428/23907; Y10T428/23986; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2964; Y10T428/2967; Y10T428/2969; Y10T428/31504; Y10T428/3154; Y10T428/31725; Y10T428/8305
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
87 words
A process of treating a polymeric shape with an effective amount of a nonionic fluorochemical surfactant selected from the group consisting of: (a) condensation product of one mole of 6-hydroxyhexyl perfluoroisopropyl ether with from about 1 to about 20 moles of ethylene oxide, and (b) condensation product of one mole of 2,2,3,4,4,4-hexafluorobutanol with from about 1 to about 6 moles of propylene oxide and with from about 0 to about 20 moles of ethylene oxide to improve lubricity properties, antistatic properties and antisoiling properties of the shape.
Claim 2
Dependent Claim
87 words
A process of treating a polymeric shape with an effective amount of a nonionic fluorochemical surfactant selected from the group consisting of: (a) condensation product of one mole of 6-hydroxyhexyl perfluoroisopropyl ether with from about 1 to about 20 moles of ethylene oxide, and (b) condensation product of one mole of 2,2,3,4,4,4-hexafluorobutanol with from about 1 to about 6 moles of propylene oxide and with from about 0 to about 20 moles of ethylene oxide to improve lubricity properties, antistatic properties and antisoiling properties of the shape.
Claim 3
Dependent Claim
28 words
The process of claim 1 wherein from about 0.1 to about 5% of the surfactant based on the weight of the polymeric shape is applied to the shape.
Claim 4
Dependent Claim
14 words
The process of claim 1 wherein the shape is treated to improve lubricity properties.
Claim 5
Dependent Claim
14 words
The process of claim 1 wherein the shape is treated to improve antistatic properties.
Claim 6
Dependent Claim
14 words
The process of claim 1 wherein the shape is treated to improve antisoiling properties.
Claim 7
Dependent Claim
11 words
The process of claim 1 wherein the polymeric shape is nylon.
Claim 8
Dependent Claim
12 words
The process of claim 6 wherein the polymeric shape is nylon fiber.
Claim 9
Dependent Claim
15 words
The process of claim 1 wherein the surfactant is applied externally to the polymeric shape.
Claim 10
Dependent Claim
15 words
The process of claim 1 wherein the surfactant is incorporated internally in the polymeric shape.
Claim 11
Dependent Claim
10 words
A polymeric shape produced by the process of claim 1.
Claim 12
Dependent Claim
49 words
The process of claim 1 wherein the polymeric shape is treated with an effective amount of a condensation product of one mole of 6-hydroxyhexyl perfluoroisopropyl ether with from about 1 to about 20 moles of ethylene oxide to improve lubricity properties, antistatic properties and antisoiling properties of the shape.
Claim 13
Dependent Claim
28 words
The process of claim 11 wherein from about 0.1 to about 5% of the surfactant based on the weight of the polymeric shape is applied to the shape.
Claim 14
Dependent Claim
14 words
The process of claim 11 wherein the shape is treated to improve lubricity properties.
Claim 15
Dependent Claim
14 words
The process of claim 11 wherein the shape is treated to improve antistatic properties.
Claim 16
Dependent Claim
14 words
The process of claim 11 wherein the shape is treated to improve antisoiling properties.
Claim 17
Dependent Claim
11 words
The process of claim 1 wherein the polymeric shape is nylon.
Claim 18
Dependent Claim
12 words
The process of claim 11 wherein the polymeric shape is nylon fiber.
Claim 19
Dependent Claim
15 words
The process of claim 11 wherein the surfactant is applied externally to the polymeric shape.
Claim 20
Dependent Claim
15 words
The process of claim 11 wherein the surfactant is incorporated internally in the polymeric shape.
Claim 21
Dependent Claim
10 words
A polymeric shape produced by the process of claim 11.
Claim 22
Dependent Claim
59 words
The process of claim 1 wherein the polymeric shape is treated with an effective amount of a condensation product of one mole of 2,2,3,4,4,4-hexafluorobutanol with from about 1 to about 6 moles of propylene oxide and with from about 0 to about 20 moles of ethylene oxide to improve lubricity properties, antistatic properties and antisoiling properties of the shape.
Claim 23
Dependent Claim
28 words
The process of claim 21 wherein from about 0.1 to about 5% of the surfactant based on the weight of the polymeric shape is applied to the shape.
Claim 24
Dependent Claim
14 words
The process of claim 21 wherein the shape is treated to improve lubricity properties.
Claim 25
Dependent Claim
14 words
The process of claim 21 wherein the shape is treated to improve antistatic properties.
Claim 26
Dependent Claim
14 words
The process of claim 21 wherein the shape is treated to improve antisoiling properties.
Claim 27
Dependent Claim
11 words
The process of claim 21 wherein the polymeric shape is nylon.
Claim 28
Dependent Claim
12 words
The process of claim 21 wherein the polymeric shape is nylon fiber.
Claim 29
Dependent Claim
15 words
The process of claim 21 wherein the surfactant is applied externally to the polymeric shape.
Claim 30
Dependent Claim
15 words
The process of claim 21 wherein the surfactant is incorporated internally in the polymeric shape.
Claim 31
Dependent Claim
10 words
A polymeric shape produced by the process of claim 21.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-05 | 1981-12-05 | 1982-06-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-05 | 1985-12-05 | 1986-06-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-05 | 1989-12-05 | 1990-06-06 | $7700.00 | Window Closed / Lapsed |