US4093759A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Glass container coated with polyurethane
Assignee: Artience Co Ltd
•
Filing: 1976-02-17
•
Granted: 1978-06-06
•
Expires: 1996-02-17
Abstract
Abstract A process for preventing the scattering of glass fragments in the event of the bursting of a glass container such as a bottle, which comprises coating the surface of the glass container with a resin composition in a thickness of at least 100 microns, said composition comprising a dispersion of (A) a powder with a particle diameter of about 1 to 100 microns of a solid compound capable of reaction with (B) upon heating to form a higher molecular weight cured product, in (B) a normally liquid urethane prepolymer having a molecular weight of at least 400 per isocyanato group, and being capable of forming a film having a tensile strength of at least 300 kg/cm 2 and a percent elongation of at least 200%.
Inventors
- 👤 Akira Otsuki
- 👤 Michihisa Naito
- 👤 Yukifumi Mashimo
- 👤 Akira Ikeda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 13:44
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/28; C03C17/32; C03C17/322; B; B65; B65D; B65D23/00; B65D23/08; B65D23/0807; B65D23/0814; Y; Y10; Y10S; Y10S215/00; Y10S215/06; Y10T; Y10T428/00; Y10T428/13; Y10T428/131; Y10T428/1317; Y10T428/1321; Y10T428/25; Y10T428/254; Y10T428/26; Y10T428/269; Y10T428/31504; Y10T428/31551; Y10T428/31598; Y10T428/31601
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
143 words
A glass container carrying on the surface thereof a single layer coating of a transparent non-tacky film in a thickness of at least 100 microns and having a tensile strength of at least 300 kg/cm 2 and a percent elongation of at least 200%, said film being a cured high molecular weight compound formed by the reaction of a powder having a particle diameter of about 1 to 100 microns of a solid compound having a melting point of more than 20° C. selected from the group consisting of melamine, benzoguanamine, and acetoguanamine with 0.9 to 1.5 equivalents per equivalent of said powder of a urethane prepolymer which is normally liquid and has at least 2 isocyanate groups and has a molecular weight of at least 400 per isocyanate group, said coating having been cured at a temperature of 180° to 200° C.
Claim 2
Dependent Claim
143 words
A glass container carrying on the surface thereof a single layer coating of a transparent non-tacky film in a thickness of at least 100 microns and having a tensile strength of at least 300 kg/cm 2 and a percent elongation of at least 200%, said film being a cured high molecular weight compound formed by the reaction of a powder having a particle diameter of about 1 to 100 microns of a solid compound having a melting point of more than 20° C. selected from the group consisting of melamine, benzoguanamine, and acetoguanamine with 0.9 to 1.5 equivalents per equivalent of said powder of a urethane prepolymer which is normally liquid and has at least 2 isocyanate groups and has a molecular weight of at least 400 per isocyanate group, said coating having been cured at a temperature of 180° to 200° C.
Claim 3
Dependent Claim
68 words
The container of claim 1 wherein said urethane prepolymer is a reaction product of 1 equivalent of a polyol selected from the group consisting of polypropylene glycol, polyethylene glycol adipate, polybutylene glycol adipate, polytetramethylene glycol, a polyester-polyol, trimethylolpropane, 1,4-butylene glycol, trimethylhexanediol, and 2,2,4-trimethyl-1,3-pentanediol, and 2 equivalents of a diisocyanate selected from the group consisting of tolylene diisocyanate, hexamethylene diisocyanate, isophorone diisocyanate, 4,4-diphenylmethane diisocyanate, xylylene diisocyanate and naphthalene diisocyanate.
Claim 4
Dependent Claim
26 words
The container of claim 1 wherein said normally solid compound is a powder of melamine or benzoguanamine having a particle diameter of 3 to 10 microns.
Claim 5
Dependent Claim
20 words
The container of claim 1 wherein the ratio between said urethane prepolymer and said solid compound is an equivalent ratio.
References Cited (Backward Citations)
US3105062A
Cited
US3178049A
Cited
US3341499A
Cited
US3386962A
Cited
US3428609A
Cited
US3428610A
Cited
US3629168A
Cited
DE2026909A1
Cited
US3666835A
Cited
US3730927A
Cited
US3726835A
Cited
US3889031A
Cited
US3823032A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-06-05 | 1981-12-05 | 1982-06-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-06-05 | 1985-12-05 | 1986-06-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-06-05 | 1989-12-05 | 1990-06-06 | $7700.00 | Window Closed / Lapsed |