Method of producing molded parts with a smooth noncellular skin and a cellular core from foamable thermoplastic material
Assignee: Institute of Metal Science, Equipment and Technologies
•
Filing: 1975-11-24
•
Granted: 1978-05-30
•
Expires: 1995-11-24
Abstract
Abstract A method of injection molding foamed articles wherein, after the mold is closed and while the mold is held closed, a gas counterpressure is generated within the mold cavity against which a portion of the foamable resin is injected under a pressure which prevents foaming. Thereafter, a shape-forming element adapted to be retracted to be flush with a wall of the mold cavity in the final phase thereof, is advanced to force the nonfoamed material, still against the gas counterpressure, into the remainder of the cavity. After a skin has formed, on the mass within the mold cavity the latter element is retracted to permit foaming, preferably after foaming has been initiated by allowing a portion of the foamable mass to recede into the injection cylinder during the inception of the foaming process.
Inventors
- 👤 Angel Tonchev Balevski
- 👤 Ivan Dimov Nikolov
- 👤 Evgeni Hristov Mateev
- 👤 Todor Kostadinov Trifonov
- 👤 Vassil Vladimirov Kojuharov
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:29
CPC Classifications
B; B29; B29C; B29C44/00; B29C44/02; B29C44/10; B29C44/105; Y; Y10; Y10S; Y10S264/00; Y10S264/14; Y10S264/83
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
230 words
A method of producing a molded foamed article having a predetermined shape and volume with a smooth noncellular skin and cellular core from a foamable injection-moldable thermoplastic resin material containing a blowing agent, comprising the steps of: (a) closing a mold and defining thereby a mold cavity having a variable volume; (b) heating a gas to a temperature higher than that of said mold; (c) introducing said gas into said cavity at a pressure higher than the partial pressure of the gaseous products evolved upon the decomposition of said blowing agent and lower than the injection pressure of said materials; (d) pulsing said gas in said cavity; (e) injecting said material from an injection cylinder into said cavity against said gas pressure and occupying a portion of the volume thereof; (f) projecting a shape-forming element forming a major part of one wall of said cavity into said cavity against said material to thereby reduce the volume of said cavity and press said material to occupy said cavity entirely; (g) permitting said material in contact with the walls of said cavity to form a skin; (h) retracting said shape-forming element from its projected position and allowing said material to expand to the full volume of said cavity; (i) permitting the fully-expanded material to harden; and (j) opening said mold and ejecting the molded article from said cavity by advancing said element.
Claim 2
Independent Claim
230 words
A method of producing a molded foamed article having a predetermined shape and volume with a smooth noncellular skin and cellular core from a foamable injection-moldable thermoplastic resin material containing a blowing agent, comprising the steps of: (a) closing a mold and defining thereby a mold cavity having a variable volume; (b) heating a gas to a temperature higher than that of said mold; (c) introducing said gas into said cavity at a pressure higher than the partial pressure of the gaseous products evolved upon the decomposition of said blowing agent and lower than the injection pressure of said materials; (d) pulsing said gas in said cavity; (e) injecting said material from an injection cylinder into said cavity against said gas pressure and occupying a portion of the volume thereof; (f) projecting a shape-forming element forming a major part of one wall of said cavity into said cavity against said material to thereby reduce the volume of said cavity and press said material to occupy said cavity entirely; (g) permitting said material in contact with the walls of said cavity to form a skin; (h) retracting said shape-forming element from its projected position and allowing said material to expand to the full volume of said cavity; (i) permitting the fully-expanded material to harden; and (j) opening said mold and ejecting the molded article from said cavity by advancing said element.
Claim 3
Dependent Claim
68 words
The method defined in claim 1 wherein: prior to the injection of said material in step (e), said shape-forming element is advanced into said cavity thereby reducing the volume thereof, said method further comprising the steps of injecting said material into said cavity and filling the reduced volume thereof and retracting said shape-forming element to allow the expansion of said material to the full volume of said cavity.
Claim 4
Dependent Claim
47 words
The method defined in claim 1, further comprising the step of interrupting the pulsing of said gas in step (d) during the expansion of said material, said expansion being induced at least in part by permitting said material in said cavity to recede into said injection cylinder.
Claim 5
Dependent Claim
32 words
The method defined in claim 3 wherein after a portion of said material recedes into said injection cylinder, said cylinder is disconnected from said mold cavity and step (h) is carried out.
Claim 6
Dependent Claim
27 words
The method defined in claim 1 wherein the pulsing of said gas in step (d) is interrupted prior to retraction of said shape-forming element in step (h).
Claim 7
Dependent Claim
34 words
The method defined in claim 1 wherein egression of a portion of said material from said cavity is permitted upon retraction of said shape-forming element in step (h) to permit expansion of said material.
References Cited (Backward Citations)
US2530289A
Cited
US2829117A
Cited
US3058161A
Cited
US3029472A
Cited
US3268635A
Cited
US3694529A
Cited
US3773873A
Cited
US3776989A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-29 | 1981-11-28 | 1982-05-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-29 | 1985-11-28 | 1986-05-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-29 | 1989-11-28 | 1990-05-30 | $7700.00 | Window Closed / Lapsed |