Epoxy resin compositions
Assignee: Individual
•
Filing: 1973-08-13
•
Granted: 1978-05-30
•
Expires: 1993-08-13
Abstract
Abstract Curable epoxy resin compositions are disclosed comprising an epoxy resin based on epichlorohydrin and a dihydric phenol having combined therewith a metallic fluoborate salt, said composition being free from a strong acid or the hydrolyzable ester thereof. Fluoborate salts in aqueous solution are used as a curing agent and these salts are shown in combination with a surfactant or a polyalcohol. The resulting epoxy resin composition may be made autocatalytic. Epoxy foam formulations and fire retardant epoxy formulations are described. Fluoborate salts set forth include the salts of tin, copper, zinc, nickel, lead and silver. The use of adducted combinations of these salts is also shown.
Inventors
- 👤 Russell A. Skiff
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 05:16
CPC Classifications
C; C08; C08G; C08G59/00; C08G59/18; C08G59/68
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
82 words
An autocatalytic process for curing an epoxy resin composition at room temperature without the use of a strong acid or the hydrolyzable ester thereof, said process comprising: mixing at room temperature an epoxy resin made from epichlorohydrin and a dihydric phenol with at least 1/2 part of an aqueous solution of a metalic fluoborate salt per 100 parts of resin said composition being free from a strong acid or the hydrolyzable ester thereof; and maintaining the resulting mixture free from external heat.
Claim 2
Dependent Claim
82 words
An autocatalytic process for curing an epoxy resin composition at room temperature without the use of a strong acid or the hydrolyzable ester thereof, said process comprising: mixing at room temperature an epoxy resin made from epichlorohydrin and a dihydric phenol with at least 1/2 part of an aqueous solution of a metalic fluoborate salt per 100 parts of resin said composition being free from a strong acid or the hydrolyzable ester thereof; and maintaining the resulting mixture free from external heat.
Claim 3
Dependent Claim
24 words
The process of claim 1 wherein said metallic fluoborate salt is selected from the group consisting of tin, copper, zinc, nickel, lead and silver.
Claim 4
Dependent Claim
22 words
The process of claim 1 wherein said aqueous solution contains between about 40 and 50 percent by weight of said fluoborate salt.
Claim 5
Dependent Claim
79 words
An autocatalytic process for curing an epoxy resin composition at room temperature without the use of a strong acid or the hydrolyzable ester thereof, said process comprising: mixing at room temperature an epoxy resin made from epichlorohydrin and a dihydric phenol with at least 1/2 part per 100 parts of resin of tin fluoborate in aqueous solution, said composition being free from a strong acid or the hydrolyzable ester thereof; and maintaining the resulting mixture free from external heat.
Claim 6
Dependent Claim
79 words
An autocatalytic process for curing an epoxy resin composition at room temperature without the use of a strong acid or the hydrolyzable ester thereof, said process comprising: mixing at room temperature an epoxy resin made from epichlorohydrin and a dihydric phenol with at least 1/2 part per 100 parts of resin of tin fluoborate in aqueous solution, said composition being free from a strong acid or the hydrolyzable ester thereof; and maintaining the resulting mixture free from external heat.
Claim 7
Dependent Claim
37 words
The process of claim 4 wherein said dihydric phenol is bisphenol A, said resin has an epoxide equivalent between 185 and 200, and said tin fluoborate is between 1/2 and 3 parts per 100 parts of resin.
Claim 8
Dependent Claim
23 words
The process of claim 5 wherein said tin fluoborate is present at a level of about 1 part per 100 parts of resin.
Claim 9
Dependent Claim
41 words
The process of claim 4 wherein said dihydric phenol is bisphenol A, said resin has an epoxide equivalent between about 300 and 325 and said tin fluoborate is present at a level of about 1/2 part per 100 parts of resin.
Claim 10
Dependent Claim
46 words
The process of claim 4 wherein said dihydric phenol is bisphenol A, said resin has a surfactant added thereto and an epoxide equivalent of about 200 and said tin fluoborate is present at a level of between 1/2 and 62 parts per 100 parts of resin.
Claim 11
Dependent Claim
39 words
The process of claim 4 wherein said epoxy resin is modified with butyl glycidyl ether having an epoxide equivalent between about 180 and 195 and said tin fluoborate is between 1/2 and 25 parts per 100 parts of resin.
Claim 12
Dependent Claim
20 words
The process of claim 9 wherein said tin fluoborate is between 1/2 and 1 part per 100 parts of resin.
Claim 13
Dependent Claim
79 words
An autocatalytic process for curing an epoxy resin composition at room temperature without the use of a strong acid or the hydrolyzable ester thereof, said process comprising: mixing at room temperature an epoxy resin made from epichlorohydrin and a dihydric phenol with at least 1/2 part per 100 parts of resin of copper fluoborate in aqueous solution, said composition being free from a strong acid or the hydrolyzable ester thereof; and maintaining the resulting mixture free from external heat.
Claim 14
Dependent Claim
79 words
An autocatalytic process for curing an epoxy resin composition at room temperature without the use of a strong acid or the hydrolyzable ester thereof, said process comprising: mixing at room temperature an epoxy resin made from epichlorohydrin and a dihydric phenol with at least 1/2 part per 100 parts of resin of copper fluoborate in aqueous solution, said composition being free from a strong acid or the hydrolyzable ester thereof; and maintaining the resulting mixture free from external heat.
Claim 15
Dependent Claim
39 words
The process of claim 11 wherein said dihydric phenol is bisphenol A, said resin has an epoxide equivalent between about 185 and 200 and said copper fluoborate is present between 1/2 and 25 parts per 100 parts of resin.
Claim 16
Dependent Claim
39 words
The process of claim 11 wherein said dihydric phenol is bisphenol A, said resin has an epoxide equivalent between about 300 and 325 and said copper fluoborate is present between 1/2 and 1 part per 100 parts of resin.
Claim 17
Dependent Claim
38 words
The process of claim 11 wherein said dihydric phenol is bisphenol A, and has an epoxide equivalent between about 185 and 200 and said copper fluoborate is between about 0.4 and 20 parts per 100 parts of resin.
Claim 18
Dependent Claim
46 words
The process of claim 11 wherein said epoxy resin is a bisphenol A epichlorophydrin diepoxide resin modified with butyl glycidyl ether having an epoxide equivalent between about 180 and 195 and said copper fluoborate is between about 0.4 and 20 parts per 100 parts of resin.
Claim 19
Dependent Claim
79 words
An autocatalytic process for curing an epoxy resin composition at room temperature without the use of a strong acid or the hydrolyzable ester thereof, said process comprising: mixing at room temperature an epoxy resin made from epichlorohydrin and a dihydric phenol with at least 1/2 part per 100 parts of resin of zinc fluoborate in aqueous solution, said composition being free from a strong acid or the hydrolyzable ester thereof; and maintaining the resulting mixture free from external heat.
Claim 20
Dependent Claim
79 words
An autocatalytic process for curing an epoxy resin composition at room temperature without the use of a strong acid or the hydrolyzable ester thereof, said process comprising: mixing at room temperature an epoxy resin made from epichlorohydrin and a dihydric phenol with at least 1/2 part per 100 parts of resin of zinc fluoborate in aqueous solution, said composition being free from a strong acid or the hydrolyzable ester thereof; and maintaining the resulting mixture free from external heat.
Claim 21
Dependent Claim
38 words
The process of claim 16 wherein said dihydric phenol is bisphenol A, and has an epoxide equivalent between about 185 and 200 and said zinc fluoborate is between about 0.4 and 12 parts per 100 parts of resin.
Claim 22
Dependent Claim
47 words
The process of claim 16 wherein said dihydric phenol is bisphenol A, said resin has a surfactant added thereto and has an epoxide equivalent of about 200 and said zinc fluoborate is present at a level between about 0.4 and 2.4 parts per 100 parts of resin.
Claim 23
Dependent Claim
79 words
An autocatalytic process for curing an epoxy resin composition at room temperature without the use of a strong acid or the hydrolyzable ester thereof, said process comprising: mixing at room temperature an epoxy resin made from epichlorohydrin and a dihydric phenol with at least 1/2 part per 100 parts of resin of nickel fluoborate in aqueous solution, said composition being free from a strong acid or the hydrolyzable ester thereof; and maintaining the resulting mixture free from external heat.
Claim 24
Dependent Claim
79 words
An autocatalytic process for curing an epoxy resin composition at room temperature without the use of a strong acid or the hydrolyzable ester thereof, said process comprising: mixing at room temperature an epoxy resin made from epichlorohydrin and a dihydric phenol with at least 1/2 part per 100 parts of resin of nickel fluoborate in aqueous solution, said composition being free from a strong acid or the hydrolyzable ester thereof; and maintaining the resulting mixture free from external heat.
Claim 25
Dependent Claim
38 words
The process of claim 19 wherein said dihydric phenol is bisphenol A, and has an epoxide equivalent between about 185 and 200 and said nickel fluoborate is between about 1/2 and 7 parts per 100 parts of resin.
Claim 26
Dependent Claim
47 words
The process of claim 19 wherein said dihydric phenol is bisphenol A, said resin has a surfactant added thereto and has an epoxide equivalent of about 200 and said nickel fluoborate is present at a level between about 1/2 and 15 parts per 100 parts of resin.
Claim 27
Dependent Claim
46 words
The process of claim 19 wherein said epoxy resin is a bisphenol A epichlorohydrin diepoxide resin modified with butyl glycidyl ether having an epoxide equivalent between about 180 and 195 and said nickel fluoborate is between about 1/2 and 3 parts per 100 parts of resin.
Claim 28
Dependent Claim
79 words
An autocatalytic process for curing an epoxy resin composition at room temperature without the use of a strong acid or the hydrolyzable ester thereof, said process comprising: mixing at room temperature an epoxy resin made from epichlorohydrin and a dihydric phenol with at least 1/2 part per 100 parts of resin of lead fluoborate in aqueous solution, said composition being free from a strong acid or the hydrolyzable ester thereof; and maintaining the resulting mixture free from external heat.
Claim 29
Dependent Claim
79 words
An autocatalytic process for curing an epoxy resin composition at room temperature without the use of a strong acid or the hydrolyzable ester thereof, said process comprising: mixing at room temperature an epoxy resin made from epichlorohydrin and a dihydric phenol with at least 1/2 part per 100 parts of resin of lead fluoborate in aqueous solution, said composition being free from a strong acid or the hydrolyzable ester thereof; and maintaining the resulting mixture free from external heat.
Claim 30
Dependent Claim
47 words
The process of claim 23 wherein said dihydric phenol is bisphenol A, said resin has a surfactant added thereto and has an expoxide equivalent of about 200 and said lead fluoborate is present at a level between about 1/2 and 3 parts per 100 parts of resin.
Claim 31
Dependent Claim
67 words
An autocatalytic process for curing an epoxy resin composition at room temperature without the use of a strong acid or the hydrolyzable ester thereof, said process comprising: mixing at room temperature an epoxy resin made from epichlorohydrin and a dihydric phenol with a catalyst consisting essentially of an aqueous mixture of a metallic fluoborate salt and a surfactant; and maintaining the resulting mixture free from external heat.
Claim 32
Dependent Claim
67 words
An autocatalytic process for curing an epoxy resin composition at room temperature without the use of a strong acid or the hydrolyzable ester thereof, said process comprising: mixing at room temperature an epoxy resin made from epichlorohydrin and a dihydric phenol with a catalyst consisting essentially of an aqueous mixture of a metallic fluoborate salt and a surfactant; and maintaining the resulting mixture free from external heat.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-29 | 1981-11-28 | 1982-05-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-29 | 1985-11-28 | 1986-05-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-29 | 1989-11-28 | 1990-05-30 | $7700.00 | Window Closed / Lapsed |