Copper coated, iron-carbon eutectic alloy powders
Assignee: Ford Motor Co
•
Filing: 1976-05-14
•
Granted: 1978-05-30
•
Expires: 1996-05-14
Abstract
Abstract A mechanical mixture of selected powders is subjected to compressive forces to define a pre-compact, the pre-compact then being subjected to liquid phase sintering for producing a raw alloy steel product which is more economical and has enhanced physical properties, particularly tensile strength as compared to sintered compacts produced by the prior art to date. The improvement in physical properties and processing technique results principally from the use of a mechanical mixture consisting of a base iron powder and a coated alloyed additive powder having selected alloying ingredients (such as manganese, nickel, molybdenum, in an iron-carbon system); the particles of the alloyed powder have a thin flash coating of a low melting metal, such as copper, to control carbon diffusion into the base iron powder during liquid phase sintering.
Inventors
- 👤 Sydney M. Kaufman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 09:35
CPC Classifications
C; C22; C22C; C22C33/00; C22C33/02; C22C33/0207; B; B22; B22F; B22F1/00; B22F1/17; B22F2998/00; Y; Y10; Y10S; Y10S75/00; Y10S75/95; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12181
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
152 words
A method of preconditioning a master alloy intermediate powder useful in being blended with a base metal powder for making liquid-phase sintered shapes, comprising: (a) selecting an iron-carbon-prealloyed powder containing at least one alloying ingredient selected from the group consisting of manganese, chromium, molybdenum, nickel, copper, vanadium, said alloying ingredients each being present in an amount of about 2.5% by weight and the total of said alloying ingredients being in the range of 0.5-20% by weight, (b) sizing said iron-carbon-alloy powder to a mesh size of -100, and (c) substantially enveloping each particle of said iron-carbon-alloying powder with a metal which can be dissolved in said prealloyed powder and which is effective to act as a barrier to carbon diffusion in the solid state condition and which barrier metal remains substantially solid only up to the point of melting of said prealloyed powder, said envelope having a thickness of about 200 microns.
Claim 2
Independent Claim
152 words
A method of preconditioning a master alloy intermediate powder useful in being blended with a base metal powder for making liquid-phase sintered shapes, comprising: (a) selecting an iron-carbon-prealloyed powder containing at least one alloying ingredient selected from the group consisting of manganese, chromium, molybdenum, nickel, copper, vanadium, said alloying ingredients each being present in an amount of about 2.5% by weight and the total of said alloying ingredients being in the range of 0.5-20% by weight, (b) sizing said iron-carbon-alloy powder to a mesh size of -100, and (c) substantially enveloping each particle of said iron-carbon-alloying powder with a metal which can be dissolved in said prealloyed powder and which is effective to act as a barrier to carbon diffusion in the solid state condition and which barrier metal remains substantially solid only up to the point of melting of said prealloyed powder, said envelope having a thickness of about 200 microns.
Claim 3
Dependent Claim
17 words
The method as in claim 1, in which said enveloping step is carried out by electrolytic deposition.
Claim 4
Dependent Claim
26 words
The method as in claim 1, in which said enveloping step is carried out chemically whereby said alloy particles are immersed in a copper salt solution.
Claim 5
Dependent Claim
39 words
The method as in claim 1, wherein said enveloping step is carried out mechanically by use of a ball mill containing copper abrading balls, said enveloping step being carried out for a period sufficient to coat a continuous envelope.
Claim 6
Dependent Claim
23 words
The method as in claim 1, in which the metal of step (c) is selected from the group consisting of copper, silver, platinum.
References Cited (Backward Citations)
US3379521A
Cited
US3775100A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-29 | 1981-11-28 | 1982-05-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-29 | 1985-11-28 | 1986-05-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-29 | 1989-11-28 | 1990-05-30 | $7700.00 | Window Closed / Lapsed |