Cementing against evaporites
Assignee: Mobil Oil AS
•
Filing: 1976-08-16
•
Granted: 1978-05-16
•
Expires: 1996-08-16
Abstract
Abstract This specification discloses a method of cementing pipe in a well and discloses a cement slurry which may be used for cementing pipe against evaporite sections penetrated by the well. The cement slurry is formulated from hydraulic cement, silica flour, attapulgite, sodium chloride, weighting agent, dispersing and retarding agent, and water, and has a density within the range of about 13.0 to 21.0 pounds per gallon.
Inventors
- 👤 Joseph U. Messenger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 12:51
CPC Classifications
C; C09; C09K; C09K8/00; C09K8/42; C09K8/46; C04; C04B; C04B28/00; C04B28/02
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
160 words
A method of cementing a pipe in a well penetrating the earth, comprising the steps of: (a) forming a pumpable cement slurry comprised of hydraulic cement, silica flour in an amount within the range of 30 to 40 percent based on cement, attapulgite in an amount within the range of 0.1 percent to 4 percent based on cement, sodium chloride in an amount within the range of 18 to 37 percent based on mixing water, d-glucons delta lactone in an amount within the range of 0.05 to 1 percent based on cement, water and hematite in an amount to provide a density of said cement slurry within the range of about 13 to 21 pounds per gallon; (b) positioning said slurry in the annular space formed intermediate said pipe in the wall of said well; and (c) maintaining said slurry in said annular space to allow said slurry to set and bond said pipe to said wall of said well.
Claim 2
Independent Claim
160 words
A method of cementing a pipe in a well penetrating the earth, comprising the steps of: (a) forming a pumpable cement slurry comprised of hydraulic cement, silica flour in an amount within the range of 30 to 40 percent based on cement, attapulgite in an amount within the range of 0.1 percent to 4 percent based on cement, sodium chloride in an amount within the range of 18 to 37 percent based on mixing water, d-glucons delta lactone in an amount within the range of 0.05 to 1 percent based on cement, water and hematite in an amount to provide a density of said cement slurry within the range of about 13 to 21 pounds per gallon; (b) positioning said slurry in the annular space formed intermediate said pipe in the wall of said well; and (c) maintaining said slurry in said annular space to allow said slurry to set and bond said pipe to said wall of said well.
Claim 3
Dependent Claim
161 words
In a method of cementing pipe in a well against an evaporite section containing a sodium chloride salt penetrated by said well, the improvement comprising: (a) forming a pumpable cement slurry comprised of hydraulic cement, silica flour in an amount within the range of 30 to 40 percent based on cement, attapulgite in an amount within the range of .1 to 4 percent based on cement, sodium chloride in an amount within the range of 18 to 37 percent based on mixing water, d-glucono delta lactone is an amount within the range of 0.05 to 1 percent based on cement, hematite in an amount to provide a slurry density within the range of 13 to 21 pounds per gallon, and water; (b) positioning said pumpable slurry in the annular space formed intermediate said pipe and said evaporite section; and (c) maintaining said slurry in said annular space to allow said slurry to set and bond said pipe to said evaporite section.
Claim 4
Dependent Claim
161 words
In a method of cementing pipe in a well against an evaporite section containing a sodium chloride salt penetrated by said well, the improvement comprising: (a) forming a pumpable cement slurry comprised of hydraulic cement, silica flour in an amount within the range of 30 to 40 percent based on cement, attapulgite in an amount within the range of .1 to 4 percent based on cement, sodium chloride in an amount within the range of 18 to 37 percent based on mixing water, d-glucono delta lactone is an amount within the range of 0.05 to 1 percent based on cement, hematite in an amount to provide a slurry density within the range of 13 to 21 pounds per gallon, and water; (b) positioning said pumpable slurry in the annular space formed intermediate said pipe and said evaporite section; and (c) maintaining said slurry in said annular space to allow said slurry to set and bond said pipe to said evaporite section.
Claim 5
Dependent Claim
68 words
The method of claim 2 wherein said pumpable aqueous cement slurry is comprised of Class G portland cement, 35 percent silica flour, 1.0 percent attapulgite, 37.2 percent sodium chloride based on water, 31.9 percent hematite, and 0.3 percent d-glucono delta lactone, and mixed with 6.5 gallons of fresh water per 94-pound sack of said cement to yield a pumpable slurry having a density of 17.2 pounds per gallon.
Claim 6
Independent Claim
161 words
A method of cementing a pipe in a well penetrating the earth, comprising the steps of: (a) forming a pumpable cement slurry comprised of hydraulic cement, silica flour in an amount within the range of 30 to 40 percent based on cement, attapulgite in an amount within the range of 0.1 percent to 4 percent based on cement, sodium chloride in an amount within the range of 18 to 37 percent based on mixing water, d-glucono delta lactone in an amount within the range of 0.05 to 1 percent based on cement, water and weighting agent in an amount to provide a density of said cement slurry within the range of about 13 to 21 pounds per gallon; (b) positioning said slurry in the annular space formed intermediate said pipe in the wall of said well; and (c) maintaining said slurry in said annular space to allow said slurry to set and bond said pipe to said wall of said well.
Claim 7
Independent Claim
161 words
A method of cementing a pipe in a well penetrating the earth, comprising the steps of: (a) forming a pumpable cement slurry comprised of hydraulic cement, silica flour in an amount within the range of 30 to 40 percent based on cement, attapulgite in an amount within the range of 0.1 percent to 4 percent based on cement, sodium chloride in an amount within the range of 18 to 37 percent based on mixing water, d-glucono delta lactone in an amount within the range of 0.05 to 1 percent based on cement, water and weighting agent in an amount to provide a density of said cement slurry within the range of about 13 to 21 pounds per gallon; (b) positioning said slurry in the annular space formed intermediate said pipe in the wall of said well; and (c) maintaining said slurry in said annular space to allow said slurry to set and bond said pipe to said wall of said well.
References Cited (Backward Citations)
US2805719A
Cited
US2961044A
Cited
US3064957A
Cited
US3071481A
Cited
US3208523A
Cited
US3197317A
Cited
US3360046A
Cited
US3467193A
Cited
US3581825A
Cited
US3937282A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-15 | 1981-11-14 | 1982-05-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-15 | 1985-11-14 | 1986-05-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-15 | 1989-11-14 | 1990-05-16 | $7700.00 | Window Closed / Lapsed |