Process for electrograining aluminum substrates for lithographic printing
Assignee: Nippon Light Metal Research Laboratory Ltd
•
Filing: 1976-11-04
•
Granted: 1978-05-02
•
Expires: 1996-11-04
Abstract
Abstract Aluminum substrates are electrograined for lithographic printing in an electrolytic cell using an electrolyte of hydrochloric acid or nitric acid, and a "regulated alternating current" whereby the inter-electrode voltage is applied with a higher anodic voltage than the cathodic voltage, the ratio of cathodic coulombic input to anodic coulombic input is less than one and preferably in the range of 0.3-0.8, and the anodic half cycle period or time is not longer than the cathodic half cycle period or time, thereby to impart to the substrate a "pits-within-a-pit" grain structure uniformly over its entire surface.
Inventors
- 👤 Masahiro Takahashi
- 👤 Teruo Miyashita
- 👤 Akira Morita
- 👤 Ken Sato
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 05:48
CPC Classifications
B; B41; B41N; B41N3/00; B41N3/03; B41N3/034
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
109 words
A process for electrolytically etching aluminum substrates to impart thereto a uniform "pits-within-a-pit" surface structure for lithographic printing, comprising the steps of subjecting the aluminum substrate to electrolytic etching in an electrolytic cell filled with an electrolyte consisting essentially of hydrochloric acid or nitric acid; by means of a regulated alternating current applying an inter-electrode voltage with the anodic voltage of greater magnitude than cathodic voltage and the ratio of the cathodic coulombic input to the anodic coulombic input being less than 1, said ratio being in the range of 0.3-0.8 for a hydrochloric acid containing electrolyte and in the range of 0.4-0.8 for a nitric acid containing electrolyte.
Claim 2
Dependent Claim
109 words
A process for electrolytically etching aluminum substrates to impart thereto a uniform "pits-within-a-pit" surface structure for lithographic printing, comprising the steps of subjecting the aluminum substrate to electrolytic etching in an electrolytic cell filled with an electrolyte consisting essentially of hydrochloric acid or nitric acid; by means of a regulated alternating current applying an inter-electrode voltage with the anodic voltage of greater magnitude than cathodic voltage and the ratio of the cathodic coulombic input to the anodic coulombic input being less than 1, said ratio being in the range of 0.3-0.8 for a hydrochloric acid containing electrolyte and in the range of 0.4-0.8 for a nitric acid containing electrolyte.
Claim 3
Dependent Claim
25 words
The process according to claim 1, wherein the anodic half-cycle period in said regulated alternating current is equal or less than the cathodic half-cycle period.
Claim 4
Dependent Claim
19 words
The process according to claim 1, wherein said coulombic input ratio is in the range of 0.4 to 0.7.
Claim 5
Dependent Claim
24 words
The process according to claim 1, wherein, said anodic voltage is 10 to 50V, and said cathodic voltage is lower than said anodic voltage.
Claim 6
Dependent Claim
13 words
The process of claim 1 wherein said cell includes a graphite counter electrode.
References Cited (Backward Citations)
US2901412A
Cited
US3072546A
Cited
US3330743A
Cited
US3887447A
Cited
US3861917A
Cited
US3892636A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-01 | 1981-10-31 | 1982-05-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-01 | 1985-10-31 | 1986-05-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-01 | 1989-10-31 | 1990-05-02 | $7700.00 | Window Closed / Lapsed |