Nonwoven polypropylene fabric and process
Assignee: EIDP Inc
•
Filing: 1977-03-30
•
Granted: 1978-04-25
•
Expires: 1997-03-30
Abstract
Abstract There is disclosed a bonded, nonwoven sheet of continuous isotactic polypropylene filaments having a nonselvage portion with specified properties rendering the sheet useful as a carpet backing, said properties including an average bond strength, for bonds having a strength greater than 0.1 gram, of at least 0.9 gram and less than the fiber breaking strength, the sheet being characterized by a selvage having an average bond strength which is from about 15-400% greater than the average bond strength of the non-selvage portion of said sheet. There is also disclosed a process for producing said sheet.
Inventors
- 👤 David Alan Cheshire
- 👤 Samir Costandi Debbas
- 👤 Richard Thomas Eger
- 👤 Ken Stephen Schermacher
- 👤 Paul Thomas Twohig
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 11:39
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/02; B32B5/12; B32B5/022; B32B5/22; B32B5/24; B32B5/26; D; D04; D04H; D04H3/00; D04H3/02; D04H3/03; B32B2262/00; B32B2262/02; B32B2262/0253; B32B2471/00; B32B2471/02; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10T; Y10T428/00; Y10T428/24; Y10T428/24058; Y10T428/24124; Y10T428/24777; Y10T442/00; Y10T442/60; Y10T442/68; Y10T442/69
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
165 words
A bonded, nonwoven sheet of continuous, isotactic polypropylene filaments having a breaking strength of at least 7 grams, said sheet consisting essentially of filaments and binder; said sheet having (a) a non-selvage portion in which filaments are interconnected at a multiplicity of points throughout said portion by bonds, the average bond strength for bonds having a strength greater than 0.1 gram being at least 0.9 gram and less than the fiber breaking strength, the bond strength distribution of said bonds having a variance of at least 4, the number of said bonds being such that the product of the number of bonds per cubic centimeter and the average bond strength is greater than 5 × 10 4 g/cm 3 , and this product divided by the fiber breaking strength being less than 9 × 10 3 /cm 3 and (b) a selvage having an average bond strength which is from about 15-400% greater than the average bond strength of the non-selvage portion of said sheet.
Claim 2
Dependent Claim
165 words
A bonded, nonwoven sheet of continuous, isotactic polypropylene filaments having a breaking strength of at least 7 grams, said sheet consisting essentially of filaments and binder; said sheet having (a) a non-selvage portion in which filaments are interconnected at a multiplicity of points throughout said portion by bonds, the average bond strength for bonds having a strength greater than 0.1 gram being at least 0.9 gram and less than the fiber breaking strength, the bond strength distribution of said bonds having a variance of at least 4, the number of said bonds being such that the product of the number of bonds per cubic centimeter and the average bond strength is greater than 5 × 10 4 g/cm 3 , and this product divided by the fiber breaking strength being less than 9 × 10 3 /cm 3 and (b) a selvage having an average bond strength which is from about 15-400% greater than the average bond strength of the non-selvage portion of said sheet.
Claim 3
Dependent Claim
30 words
The sheet of claim 1 wherein the selvage has an average bond strength which is from 15-100% greater than the average bond strength of the non-selvage portion of said sheet.
Claim 4
Dependent Claim
225 words
A nonwoven sheet of claim 1 wherein said sheet is comprised of a machine direction layer at each surface of the sheet with each of the two machine direction layers constituting from about 20-30% of the sheet weight and a cross-machine direction layer which constitutes from about 40-60% of the sheet weight; the non-selvage portion of each of said layers consisting essentially of from about 65-90% by weight of filaments having a weight average break elongation of less than 400% and from 10-35% by weight of binder, filaments with a weight average elongation of less than 400% in each layer having an average denier per filament of from about 6-60 and a tenacity of at least 2.0 gpd, the filaments of the non-selvage portion of the sheet being disposed in such a manner as to provide the following directionality values; MD/45° ≧ 1.5, XD/45° ≧ 1.5 and (MD+XD)/45° of from 3.5 to 30, wherein MD is a measure of the total filament length of the sheet in the sheet length direction, XD is a measure of the total filament length of the sheet in the direction perpendicular to the sheet length direction, and 45° is the average of the measures of the total filament length of the sheet in directions at 45° to the sheet length direction, said sheet having a neckdown of from 1-5%.
Claim 5
Dependent Claim
38 words
A sheet of claim 3 wherein each machine direction layers has a selvage with an average bond strength which is from about 20 to 400% greater than the average bond strength of the non-selvage portion of said sheet.
Claim 6
Dependent Claim
30 words
The sheet of claim 3 wherein the selvage has an average bond strength which is from 15-100% greater than the average bond strength of the non-selvage portion of said sheet.
Claim 7
Dependent Claim
131 words
In a process for preparing a nonwoven sheet of continuous filaments of isotactic polypropylene wherein an unbonded sheet is formed by melt-spinning isotactic polypropylene filaments, drawing said or some of said filaments, and depositing said filaments on a moving belt and the thusly formed sheet is then thermally bonded under restraint to provide a sheet having a non-selvage portion as described in claim 1, the improvement comprising depositing in the selvage of said unbonded sheet filaments or filament segments having low orientation such that the weight average break elongation of filaments in the selvage is from about 360-800% and the ratio of weight average break elongation of filaments in the selvage to weight average break elongation of filaments in the non-selvage portion of said unbonded sheet is at least about 1.10.
Claim 8
Dependent Claim
19 words
The process of claim 6 wherein the weight average break elongation of filaments in the selvage is from 360-500%.
Claim 9
Dependent Claim
138 words
In a process for preparing a nonwoven sheet of continuous filaments of isotactic polypropylene wherein an unbonded sheet is formed by melt-spinning isotactic polypropylene filaments, drawing said or some of said filaments, and depositing said filaments on a moving belt and the thusly formed sheet is then thermally bonded under restraint to provide a sheet having a non-selvage portion as described in claim 3, the improvement comprising depositing in the selvage of the outer layers of said unbonded sheet filaments or filament segments having low orientation such that the weight average break elongation of filaments in the selvage of the outer layers is from about 400-800% and the ratio of weight average break elongation of filaments in the selvage to weight average break elongation of filaments in the non-selvage portion of said outer layers is at least 1.20.
Claim 10
Dependent Claim
23 words
The process of claim 8 wherein the weight average elongation of filaments in the selvage of the outer layers is from about 400-600%.
References Cited (Backward Citations)
US3360421A
Cited
US3502538A
Cited
US3821062A
Cited
US3895151A
Cited
US3991244A
Cited
US3993812A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-04-24 | 1981-10-24 | 1982-04-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-04-24 | 1985-10-24 | 1986-04-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-04-24 | 1989-10-24 | 1990-04-25 | $7700.00 | Window Closed / Lapsed |