Recovering material
Assignee: Federal Mogul Engineering Ltd
•
Filing: 1977-01-14
•
Granted: 1978-04-25
•
Expires: 1997-01-14
Abstract
Abstract This invention is a method of recovering an expensive bearing lining alloy from a multilayer bearing material comprising the alloy bonded to a steel backing, possibly through a pure aluminium foil. The multi-layer scrap material is heated sufficiently for severance of the bond between the components to be started, and then is given repeated mechanical shocks which complete the severance of the components which can then be separated from one another by a magnetic method, or possibly by a gravitational method.
Inventors
- 👤 Anthony Dennis Michael
- 👤 John Albert White
- 👤 Gerald Louis Griffin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 08:27
CPC Classifications
C; C22; C22B; C22B25/00; C22B25/06; C22B7/00; C22B7/005; Y; Y02; Y02P; Y02P10/00; Y02P10/20
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
124 words
A method for recovering a tin-containing alloy layer from a multilayered material comprising in adjacent layers a steel layer, an intermediate aluminum foil layer and said tin-containing alloy layer which comprises; heating said multilayered material to a temperature of at least the melting point of tin but below the melting point of said tin-containing alloy, for a time sufficient to allow the molten tin to penetrate said aluminum foil layer and to come into contact with said steel layer, but for insufficient time for aluminum and steel to alloy between said aluminum foil layer and said steel layer; and thereafter subjecting said multilayered material in said heated state to repetitive mechanical shocks to effect separation of said steel layer from said aluminum foil layer.
Claim 2
Independent Claim
124 words
A method for recovering a tin-containing alloy layer from a multilayered material comprising in adjacent layers a steel layer, an intermediate aluminum foil layer and said tin-containing alloy layer which comprises; heating said multilayered material to a temperature of at least the melting point of tin but below the melting point of said tin-containing alloy, for a time sufficient to allow the molten tin to penetrate said aluminum foil layer and to come into contact with said steel layer, but for insufficient time for aluminum and steel to alloy between said aluminum foil layer and said steel layer; and thereafter subjecting said multilayered material in said heated state to repetitive mechanical shocks to effect separation of said steel layer from said aluminum foil layer.
Claim 3
Dependent Claim
17 words
The method of claim 1, wherein said separated layers are classified by use of a magnetic field.
Claim 4
Dependent Claim
16 words
The method of claim 1, wherein said tin-containing alloy is an alloy of aluminum and tin.
Claim 5
Dependent Claim
17 words
The method of claim 1, wherein there is at least 6% by weight in said tin-containing alloy.
Claim 6
Dependent Claim
17 words
The method of claim 4, wherein there is 20% by weight of tin in said tin-containing alloy.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-04-24 | 1981-10-24 | 1982-04-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-04-24 | 1985-10-24 | 1986-04-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-04-24 | 1989-10-24 | 1990-04-25 | $7700.00 | Window Closed / Lapsed |