US4083926A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Cooling aluminum chloride vapors by contact with solid aluminum chloride
Assignee: Alcoa Corp
•
Filing: 1977-02-03
•
Granted: 1978-04-11
•
Expires: 1997-02-03
Abstract
Abstract Hot vapors of aluminum chloride and by-products produced in the chlorination of aluminous material to form aluminum chloride are cooled by contacting the vapors with solid aluminum chloride as the vapors exit from the reactor and before the vapors come in contact with filter materials. This cooling reduces the temperature of the vapors from an initial temperature of about 600°-800° C down to about 300°-350° C thereby preventing or inhibiting attack of the filter materials by the hot vapors.
Inventors
- 👤 Marlyn D. Ballain
- 👤 Roy E. Hardwick
- 👤 Robert L. Hargis
- 👤 Larry K. King
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 17:10
CPC Classifications
C; C01; C01F; C01F7/00; C01F7/48; C01F7/56; C01F7/58; C01F7/60; C01P; C01P2004/00; C01P2004/60; C01P2004/61
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
130 words
In an improved process for the production of high-purity aluminum chloride suitable for electrolytic reduction to metallic aluminum by the chlorination of aluminous material to produce aluminum chloride at a temperature above the vaporization point of aluminum chloride followed by filtration of the aluminum chloride vapors and subsequent condensation of the aluminum chloride vapors in a fluidized bed, the improvement which comprises: contacting the hot aluminum chloride vapors with sufficient solid aluminum chloride particles recycled by a fluidizing gas, after condensation in the fluidized bed back to a point located between a chlorination zone and a filtration zone to cool the vapors by vaporization of the solid aluminum chloride to a temperature of about 300°-350° C to permit subsequent filtration of the aluminum chloride vapors to remove solid impurities therefrom.
Claim 2
Dependent Claim
130 words
In an improved process for the production of high-purity aluminum chloride suitable for electrolytic reduction to metallic aluminum by the chlorination of aluminous material to produce aluminum chloride at a temperature above the vaporization point of aluminum chloride followed by filtration of the aluminum chloride vapors and subsequent condensation of the aluminum chloride vapors in a fluidized bed, the improvement which comprises: contacting the hot aluminum chloride vapors with sufficient solid aluminum chloride particles recycled by a fluidizing gas, after condensation in the fluidized bed back to a point located between a chlorination zone and a filtration zone to cool the vapors by vaporization of the solid aluminum chloride to a temperature of about 300°-350° C to permit subsequent filtration of the aluminum chloride vapors to remove solid impurities therefrom.
Claim 3
Dependent Claim
29 words
The process of claim 1 wherein a metering system controls the amount of aluminum chloride particles transported back to said point between said chlorination zone and said filtration zone.
Claim 4
Dependent Claim
13 words
The process of claim 2 wherein said metering system includes a rotary valve.
Claim 5
Dependent Claim
64 words
The process of claim 3 wherein the temperature at said point is monitored by a thermocouple which controls the speed of said rotary valve to feed an increased amount of aluminum chloride to said point in response to an increase in temperature and to decrease the amount fed to said point in response to a decrease in temperature beyond a range of 300°-350° C.
Claim 6
Dependent Claim
30 words
The process of claim 1 wherein 1-2 kilograms of solid aluminum chloride particles are recycled back to said point for each kilogram of aluminum chloride generated in said chlorination zone.
Claim 7
Dependent Claim
20 words
The process of claim 5 wherein said recycled particles have a size range of 4-25 microns to permit quick vaporization.
References Cited (Backward Citations)
US2580635A
Cited
US3446579A
Cited
US3694170A
Cited
US3786135A
Cited
US3930800A
Cited
US3956455A
Cited
US3929975A
Cited
US4029750A
Cited
US3878293A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-04-10 | 1981-10-10 | 1982-04-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-04-10 | 1985-10-10 | 1986-04-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-04-10 | 1989-10-10 | 1990-04-11 | $7700.00 | Window Closed / Lapsed |