Process for the production of aluminum chloride and related products
Assignee: Toth Aluminum Corp
•
Filing: 1976-01-22
•
Granted: 1978-04-11
•
Expires: 1996-01-22
Abstract
Abstract The present invention provides a process for the production of aluminum chloride and alumina of metallurgical grade purity, and valuable by-products from aluminous ores like clay, bauxites and laterites. The process comprises carbo-chlorination of the ore to produce aluminum chloride and other metal chlorides. The aluminum chloride is separated, purified and utilized as such or oxidized to make alumina while the other metal chlorides are processed to recover maximum values.
Inventors
- 👤 Alfred Lippman
- 👤 Roger Frank Sebenik
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 19:34
CPC Classifications
C; C22; C22B; C22B34/00; C22B34/10; C22B34/12; C22B34/1218; C22B34/1222; C01; C01B; C01B33/00; C01B33/08; C01F; C01F7/00; C01F7/02; C01F7/20; C01F7/22; C01F7/48; C01F7/56; C01F7/58; C01F7/60; C01F7/62; C01G; C01G49/00; C01G49/10; Y; Y02; Y02P; Y02P10/00; Y02P10/20; Y10; Y10S; Y10S423/00; Y10S423/09; Y10S423/12
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
155 words
A process for the production of aluminum chloride comprising the following steps: A. carbo-chlorinating at up to 1,000° C a dehydrated iron containing aluminous ore to produce a mixed chloride gas stream comprising primarily aluminum chloride, iron chloride, (other metal chloride) titanium cloride, silicon chloride, vaporous components and carbon oxides; and B. extracting the aluminum chloride and iron chloride components out of the mixed chloride gas stream by contacting the stream with a liquid metal chloride solvent in which the aluminum chloride and iron chloride are soluble to preferentially dissolve the aluminum chloride and iron chloride, then distilling the aluminum chloride and iron chloride from the liquid metal chloride solvent, subsequently separating the aluminum chloride from the iron chloride by rectification to obtain essentially aluminum chloride, and contacting the aluminum chloride with molten aluminum capable of reacting with impurity chlorides to form compounds that will not contaminate the aluminum chloride effluent to obtain aluminum chloride.
Claim 2
Dependent Claim
155 words
A process for the production of aluminum chloride comprising the following steps: A. carbo-chlorinating at up to 1,000° C a dehydrated iron containing aluminous ore to produce a mixed chloride gas stream comprising primarily aluminum chloride, iron chloride, (other metal chloride) titanium cloride, silicon chloride, vaporous components and carbon oxides; and B. extracting the aluminum chloride and iron chloride components out of the mixed chloride gas stream by contacting the stream with a liquid metal chloride solvent in which the aluminum chloride and iron chloride are soluble to preferentially dissolve the aluminum chloride and iron chloride, then distilling the aluminum chloride and iron chloride from the liquid metal chloride solvent, subsequently separating the aluminum chloride from the iron chloride by rectification to obtain essentially aluminum chloride, and contacting the aluminum chloride with molten aluminum capable of reacting with impurity chlorides to form compounds that will not contaminate the aluminum chloride effluent to obtain aluminum chloride.
Claim 3
Dependent Claim
29 words
The process of claim 1 further characterized as comprising the additional step of: oxidizing the aluminum chloride with a source of oxygen to produce alumina as an end product.
Claim 4
Dependent Claim
23 words
The process of claim 1 further characterized in that: said aluminous ore is selected from the group consisting of: clay, bauxite or laterite.
Claim 5
Dependent Claim
15 words
The process of claim 1 further characterized in that: said aluminous ore comprises kaolinitic clay.
Claim 6
Dependent Claim
18 words
The process of claim 1 further characterized in that: said aluminous ore is dehydrated by heating before chlorination.
Claim 7
Dependent Claim
29 words
The process of claim 1 further characterized in that: said aluminous ore is carbo-chlorinated in a fluid bed reactor at a temperature of about 150° C to 1000° C.
Claim 8
Dependent Claim
20 words
The process of claim 6 further characterized in that: said liquid metal chloride solvent comprises sodium chloride and aluminum chloride.
Claim 9
Dependent Claim
42 words
The process of claim 7 further characterized in that: the mixed chloride gas solvent is at a temperature of 115° C to 185° C and thereafter separated from the liquid metal chloride solvent at a temperature of 185° C to 190° C.
Claim 10
Dependent Claim
51 words
The process of claim 7 further characterized in that: the mixture of aluminum chloride and iron chloride vapors separated from the liquid metal chloride solvent is subsequently separated at a temperature of from about 190° C to about 500° C to produce separate essentially pure aluminum chloride and iron chloride components.
Claim 11
Dependent Claim
60 words
The process claim 1 further characterized in that: the absorbed iron chloride and aluminum chloride in the liquid metal chloride solvent are separated therefrom by rectification as a mixture at a temperature of 210° C to 500° C and at a pressure of about at least 3 atmospheres to maintain some of the aluminum chloride and iron chloride as liquids.
Claim 12
Dependent Claim
67 words
The process of claim 1 further characterized in that: the metal chlorides and carbon oxides components of the mixed chloride gas stream from which the aluminum chloride and iron chloride mixture has been essentially separated are then subsequently cooled sufficient to phase separate out the silicon chloride and titanium chloride components as a mixture at a temperature within about minus 35° C to about plus 35° C.
Claim 13
Dependent Claim
52 words
The process of claim 11 further characterized in that: the mixture of silicon chloride and titanium chloride are phase separated from the carbon oxide gases is subsequently rectified at a temperature of from about minus 35° C to about plus 15° C to produce essentially separate silicon chloride and titanium chloride components.
Claim 14
Dependent Claim
24 words
The process of claim 9 further characterized in that: the essentially pure iron chloride component is oxidized to recover its chlorine and iron values.
Claim 15
Dependent Claim
23 words
The process of claim 12 further characterized in that: the essentially silicon chloride component is oxidized to recover its chlorine and silica values.
Claim 16
Dependent Claim
24 words
The process of claim 9 further characterized in that: the essentially pure titanium chloride component is oxidized to recover its chlorine and titania values.
References Cited (Backward Citations)
US2084289A
Cited
US2533021A
Cited
US3066010A
Cited
US3294482A
Cited
US3436211A
Cited
US3793003A
Cited
US3938969A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-04-10 | 1981-10-10 | 1982-04-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-04-10 | 1985-10-10 | 1986-04-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-04-10 | 1989-10-10 | 1990-04-11 | $7700.00 | Window Closed / Lapsed |