High solids coating compositions containing tetrahydric adduct
Assignee: DeSoto Inc
•
Filing: 1976-06-23
•
Granted: 1978-04-11
•
Expires: 1996-06-23
Abstract
Abstract Essentially solvent-free resinous coating compositions are provided which are sufficiently fluid to permit effective application, and which cure on baking at low temperature to provide hard stain- and detergent-resistant coatings. These are made by copolymerizing monoethylenic monomers including monoethylenic monomer having a functional group reactive with N-methylol functionality and selected from carboxylic acid, hydroxy and amide groups, the copolymerization being carried out in a solvent medium consisting essentially of tetrahydric adduct of propylene oxide with pentaerythritol having a molecular weight of at least about 400. The copolymer solution has added thereto an aminoplast resin to provide a stable solution in which proportions are important so that coatings can be easily applied and cured to provide the desired characteristics without liberating large amounts of volatile material.
Inventors
- 👤 Kazys Sekmakas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 23:34
CPC Classifications
C; C09; C09D; C09D161/00; C09D161/20
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
176 words
A fluid resinous coating composition containing less than about 20% of volatile organic solvent and which cures on baking, said coating composition consisting essentially of a mixture of: (1) a copolymer of monoethylenic monomers including from about 5-20% of monoethylenic monomer having a functional group reactive with the N-methylol group and selected from carboxylic acid, hydroxy, and amide groups, said copolymer being produced by copolymerization in an organic solvent medium consisting essentially of component (2) below; (2) liquid tetrahydric adduct of propylene oxide with pentaerythritol having a molecular weight of at least about 400, said copolymer being dissolved in said tetrahydric adduct; and (3) an aminoplast resin; said copolymer constituting from about 4.5% to 30% of the mixture, the tetrahydric adduct constituting from about 30%-60% of the mixture, and the balance of the mixture of the three components consisting essentially of aminoplast resin, there being at least about 0.8 parts of aminoplast resin per part of copolymer, and said copolymer being present in an amount of from about 15%-80% of the weight of the tetrahydric adduct.
Claim 2
Dependent Claim
176 words
A fluid resinous coating composition containing less than about 20% of volatile organic solvent and which cures on baking, said coating composition consisting essentially of a mixture of: (1) a copolymer of monoethylenic monomers including from about 5-20% of monoethylenic monomer having a functional group reactive with the N-methylol group and selected from carboxylic acid, hydroxy, and amide groups, said copolymer being produced by copolymerization in an organic solvent medium consisting essentially of component (2) below; (2) liquid tetrahydric adduct of propylene oxide with pentaerythritol having a molecular weight of at least about 400, said copolymer being dissolved in said tetrahydric adduct; and (3) an aminoplast resin; said copolymer constituting from about 4.5% to 30% of the mixture, the tetrahydric adduct constituting from about 30%-60% of the mixture, and the balance of the mixture of the three components consisting essentially of aminoplast resin, there being at least about 0.8 parts of aminoplast resin per part of copolymer, and said copolymer being present in an amount of from about 15%-80% of the weight of the tetrahydric adduct.
Claim 3
Dependent Claim
55 words
A coating composition as recited in claim 1 in which the copolymer is present in an amount of 8%-25%, the tetrahydric adduct is present in an amount of from 32%-50%, and the aminoplast resin is present in an amount of from 25%-60%, there being at least 2 parts of tetrahydric adduct per part of copolymer.
Claim 4
Dependent Claim
24 words
A coating composition as recited in claim 1 in which at least about 15% of the copolymer is constituted by styrene or vinyl toluene.
Claim 5
Dependent Claim
34 words
A coating composition as recited in claim 1 in which at least about 75% of the copolymer is constituted by nonreactive monoethylenic monomers containing the single ethylenic group as the sole functional group thereof.
Claim 6
Dependent Claim
49 words
A coating composition as recited in claim 1 in which at least about 40% of the copolymer is selected from styrene, vinyl toluene, methyl methacrylate, acrylonitrile and vinyl acetate, and the balance of the copolymer, except for the reactive monomer, consists essentially of alkyl esters of monoethylenic carboxylic acid.
Claim 7
Dependent Claim
19 words
A coating composition as recited in claim 5 in which said copolymer includes from about 45%-70% of isobutyl acrylate.
Claim 8
Dependent Claim
23 words
A coating composition as recited in claim 1 in which said aminoplast resin is present in the form of a liquid methyl ether.
Claim 9
Dependent Claim
16 words
A coating composition as recited in claim 7 in which said aminoplast resin is hexamethoxymethyl melamine.
Claim 10
Dependent Claim
27 words
A coating composition as recited in claim 1 in which said tetrahydric adduct is a polyether having a molecular weight in the range of 500 to 1,000.
Claim 11
Dependent Claim
16 words
A coating composition as recited in claim 1 containing less than 5% of volatile organic solvent.
Claim 12
Dependent Claim
16 words
A coating composition as recited in claim 1 containing less than 1% of volatile organic solvent.
Claim 13
Dependent Claim
18 words
A coating composition as recited in claim 1 in which said reactive monomer consists of monoethylenic carboxylic acid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-04-10 | 1981-10-10 | 1982-04-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-04-10 | 1985-10-10 | 1986-04-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-04-10 | 1989-10-10 | 1990-04-11 | $7700.00 | Window Closed / Lapsed |