Packaging materials having excellent gas permeation resistance and process for preparation thereof
Assignee: Toyo Seikan Group Holdings Ltd
•
Filing: 1976-02-23
•
Granted: 1978-04-04
•
Expires: 1996-02-23
Abstract
Abstract A packaging material having an improved gas permeation resistance, which comprises at least one layer composed of (A) an ethylene-vinyl alcohol copolymer having a vinyl alcohol content of 50 to 75 mole % and a residual vinyl ester content of up to 4 mole % based on the sum of the vinyl alcohol and vinyl ester or (B) a blend of said ethylene-vinyl alcohol copolymer with up to 150% by weight, based on said copolymer, of at least one thermoplastic polymer other than said copolymer, said ethylenevinyl alcohol copolymer having a main endothermic peak satisfying substantially the following requirement: Y.sub.1 = 1.64X + 68.0 wherein Y 1 stands for the main endothermic peak temperature (° C.) in the differential thermal analysis, and X stands for the vinyl alcohol content (mole %) in the ethylene-vinyl alcohol copolymer, And at least one subsidary endothermic peak satisfying substantially the following requirement: 0.67 X + 76.7 ≧ Y.sub.2 ≧ 0.40 X + 40.0 preferably 0.67 X + 76.7 ≧ Y.sub.2 ≧ 0.34 X + 88.0 wherein Y 2 stands for the subsidary endothermic peak temperature (° C.) in the differential thermal analysis, and X is as defined above, The ratio (Rs) of the subsidary endothermic peak area to the main endothermic peak area being at least 2.5%.
Inventors
- 👤 Muneki Yamada
- 👤 Sadao Hirata
- 👤 Akira Kishimoto
- 👤 Shunsaku Hirata
- 👤 Toru Suzuki
- 👤 Fumio Kano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 22:51
CPC Classifications
B; B29; B29C; B29C49/00; B29C49/22; B32; B32B; B32B27/00; B32B27/06; B32B27/08; B32B1/00; B32B27/30; B32B27/306; B32B27/308; B32B27/32; B32B27/36; B32B27/365; B65; B65D; B65D65/00; B65D65/38; B32B2270/00; B32B2307/00; B32B2307/70; B32B2307/724; B32B2307/7242; B32B2307/7244; B32B2323/00; B32B2323/04; B32B2323/10; B32B2329/00; B32B2329/04; B32B2333/00; B32B2333/04; B32B2333/12; B32B2355/00; B32B2355/02; B32B2367/00; B32B2369/00; B32B2439/00; B32B2439/40; B32B2439/60; B32B2439/70; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1379; Y10T428/31504; Y10T428/31725; Y10T428/31739; Y10T428/31743; Y10T428/31746; Y10T428/31786; Y10T428/31797; Y10T428/31855; Y10T428/31909; Y10T428/31913; Y10T428/3192; Y10T428/31924; Y10T428/31928; Y10T428/31931; Y10T428/31935
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
224 words
A packaging material having an improved gas permeation resistance, which comprises at least one layer composed of (A) an ethylene-vinyl alcohol copolymer having a vinyl alcohol content of 50 to 75 mole % and a residual vinyl ester content of up to 4 mole % based on the sum of the vinyl alcohol and vinyl ester or (B) a blend of said ethylene-vinyl alcohol copolymer with 25 to 150% by weight, based on said copolymer, of at least one thermoplastic polymer selected from the group consisting of polyolefins and carbonyl group-containing polymers, said ethylene-vinyl alcohol copolymer having a main endothermic peak satisfying substantially the following requirement: Y.sub.1 = 1.64X + 68.0 wherein Y 1 stands for the main endothermic peak temperature (° C.) in the differential thermal analysis, and X stands for the vinyl alcohol content (mole %) in the ethylene-vinyl alcohol copolymer. and at least one subsidary endothermic peak satisfying substantially the following requirement: 0.67 X + 76.7 .sup.≧ = Y.sub.2 .sup.≧ = 0.40 X + 40.0 preferably 0.67 X + 76.7 .sup.≧ = Y.sub.2 .sup.≧ = 0.34 X + 88.0 wherein Y 2 stands for the subsidary endothermic peak temperature (° C.) in the differential thermal analysis, and X is as defined above. the ratio (Rs) of the subsidary endothermic peak area to the main endothermic peak area being at least 2.5%.
Claim 2
Dependent Claim
224 words
A packaging material having an improved gas permeation resistance, which comprises at least one layer composed of (A) an ethylene-vinyl alcohol copolymer having a vinyl alcohol content of 50 to 75 mole % and a residual vinyl ester content of up to 4 mole % based on the sum of the vinyl alcohol and vinyl ester or (B) a blend of said ethylene-vinyl alcohol copolymer with 25 to 150% by weight, based on said copolymer, of at least one thermoplastic polymer selected from the group consisting of polyolefins and carbonyl group-containing polymers, said ethylene-vinyl alcohol copolymer having a main endothermic peak satisfying substantially the following requirement: Y.sub.1 = 1.64X + 68.0 wherein Y 1 stands for the main endothermic peak temperature (° C.) in the differential thermal analysis, and X stands for the vinyl alcohol content (mole %) in the ethylene-vinyl alcohol copolymer. and at least one subsidary endothermic peak satisfying substantially the following requirement: 0.67 X + 76.7 .sup.≧ = Y.sub.2 .sup.≧ = 0.40 X + 40.0 preferably 0.67 X + 76.7 .sup.≧ = Y.sub.2 .sup.≧ = 0.34 X + 88.0 wherein Y 2 stands for the subsidary endothermic peak temperature (° C.) in the differential thermal analysis, and X is as defined above. the ratio (Rs) of the subsidary endothermic peak area to the main endothermic peak area being at least 2.5%.
Claim 3
Dependent Claim
55 words
A packaging material as set forth in claim 1 wherein the ethylene-vinyl alcohol copolymer is a saponified product formed by saponifying an ethylene-vinyl acetate copolymer having an ethylene content of 25 to 50 mole % and a vinyl acetate content of 75 to 50 mole % at a degree of saponification of at least 96%.
Claim 4
Dependent Claim
45 words
A packaging material as set forth in claim 1 wherein the ethylene-vinyl alcohol copolymer has an intrinsic viscosity of 0.07 to 0.17 l/g as measured in a mixed solvent of 85% by weight of phenol and 15 % by weight of water at 30° C.
Claim 5
Dependent Claim
77 words
A packaging material as set forth in claim 1 which has a multi-layer molded structure comprising at least one layer (a) composed of (A) said ethylene-vinyl alcohol copolymer or (B) said blend thereof and at least one layer (b) composed of a thermoplastic copolymer which has a water absorption lower than 3.5%, when it has been allowed to stand in an atmosphere of a temperature of 23° C. and a relative humidity of 50% for 5 days.
Claim 6
Dependent Claim
16 words
A packaging material as set forth in claim 4 wherein said layer (b) comprises a polyolefin.
Claim 7
Dependent Claim
76 words
A packaging material as set forth in claim 1 which has a multi-layer molded structure comprising an outer surface layer of a polyolefin, an intermediate layer composed of a blend containing said ethylene-vinyl alcohol copolymer (EV), a polyolefin (PO) and a carbonyl group-containing thermoplastic polymer (C) at a weight ratio EV : PO : C of from 100 : 25 : 4 to 100 : 100 : 20, and an inner surface layer of a polyolefin.
Claim 8
Dependent Claim
69 words
A packaging material as set forth in claim 6 wherein a heat-resistant and pressure-resistant innermost layer composed of a thermoplastic resin is formed inside the inner surface layer, said thermoplastic resin of the innermost layer being selected from the group consisting of (i) polyesters, (ii) polyproplylenes, (iii) polycarbonates, (iv) methyl methacrylate-grafted acrylonitrile-styrene copolymers, methyl methacrylate-grafted acrylonitrile-butadiene copolymers and methyl methacrylate-grafted acrylonitrile-styrene-butadiene copolymers, (v) acrylonitrile-styrene-butadiene copolymers and (vi) polymethyl methacrylate.
Claim 9
Dependent Claim
17 words
A packaging material as set forth in claim 1 which is a bottle formed by blow molding.
Claim 10
Dependent Claim
13 words
A packaging material as set forth in claim 1 which is a film.
Claim 11
Dependent Claim
190 words
A process for the preparation of packaging materials which comprises the steps of (1) forming a molded structure comprising at least one layer composed of (A) an ethylene-vinyl alcohol copolymer having a vinyl alcohol content of 50 to 75 mole % and a residual vinyl ester content of up to 4 mole % based on the sum of the vinyl alcohol and vinyl ester or (B) a blend of said copolymer with 25 to 150% by weight, based on said copolymer, of at least one thermoplastic polymer selected from the group consisting of polyolefins and carbonyl group-containing polymers, and (2) maintaining the so formed structure under temperature and time conditions satisfying the following requirements: 0.67 X + 66.7 .sup.≧ = Y.sub.3 .sup.≧ = 0.40 X + 30.0 preferably 0.67 X + 66.7 .sup.≧ = Y.sub.3 .sup.≧ = 0.34 X + 78.0 wherein Y 3 stands for the heat treatment temperature (° C.) and X stands for the vinyl alcohol content (mole %) in the ethylene-vinyl alcohol copolymer, and t .sup.≧ = 0.5 X - 20 wherein t stands for the heat treatment time (minute) and X is as defined above.
Claim 12
Dependent Claim
190 words
A process for the preparation of packaging materials which comprises the steps of (1) forming a molded structure comprising at least one layer composed of (A) an ethylene-vinyl alcohol copolymer having a vinyl alcohol content of 50 to 75 mole % and a residual vinyl ester content of up to 4 mole % based on the sum of the vinyl alcohol and vinyl ester or (B) a blend of said copolymer with 25 to 150% by weight, based on said copolymer, of at least one thermoplastic polymer selected from the group consisting of polyolefins and carbonyl group-containing polymers, and (2) maintaining the so formed structure under temperature and time conditions satisfying the following requirements: 0.67 X + 66.7 .sup.≧ = Y.sub.3 .sup.≧ = 0.40 X + 30.0 preferably 0.67 X + 66.7 .sup.≧ = Y.sub.3 .sup.≧ = 0.34 X + 78.0 wherein Y 3 stands for the heat treatment temperature (° C.) and X stands for the vinyl alcohol content (mole %) in the ethylene-vinyl alcohol copolymer, and t .sup.≧ = 0.5 X - 20 wherein t stands for the heat treatment time (minute) and X is as defined above.
Claim 13
Dependent Claim
16 words
A process according to claim 10 wherein the molded structure is one formed by melt molding.
Claim 14
Dependent Claim
21 words
A packaged foodstuff comprising a packaging material as set forth in claim 1 and a foodstuff filled in said packaging material.
Claim 15
Dependent Claim
23 words
A packaging material as set forth in claim 1 wherein said polyolefin is one selected from the group consisting of polyethylene and polypropylene.
Claim 16
Dependent Claim
30 words
A packaging material as set forth in claim 1 wherein said carbonyl group-containing polymer has a carbonyl group at a concentration of 120 to 1400 meq/100 g of the polymer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-04-03 | 1981-10-03 | 1982-04-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-04-03 | 1985-10-03 | 1986-04-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-04-03 | 1989-10-03 | 1990-04-04 | $7700.00 | Window Closed / Lapsed |