Patent FR967566A successfully refreshed from Google Patents.
Patent US4081298A successfully refreshed from Google Patents.
US4081298A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Heat treatment of iron-nickel-phosphorus-boron glassy metal alloys
Assignee: Honeywell International Inc
•
Filing: 1976-09-07
•
Granted: 1978-03-28
•
Expires: 1996-09-07
Abstract
Abstract A process is provided for improving magnetic properties of certain glassy metal alloys which comprises immersing toroidally wound cores of glassy metal alloy filaments in a thermally stable, nonferromagnetic, electrically inert and chemically unreactive liquid, maintaining the liquid at a temperature of between about 310 DEG and 350 DEG C for about 3/4 to 8 hrs., depending on the temperature selected, and cooling the filament to about 25 DEG C at a rate not greater than about 30 DEG C/min. through its Curie temperature. Optionally, a magnetic field of about 1 to 10 Oe may be applied circumferentially around the cores during cooling through the Curie temperature to further improve the magnetic properties of the glassy metal alloy.
Inventors
- 👤 Lewis Isaac Mendelsohn
- 👤 Kevin James Durand
- 👤 Ethan Allen Nesbitt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 19:09
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/147; H01F1/153; H01F1/15341; C; C21; C21D; C21D1/00; C21D1/04; C21D6/00; C21D6/001; C22; C22C; C22C45/00; C22C45/008
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
142 words
A process for increasing induction, decreasing coercivity and increasing permeability of a substantially glassy metal alloy consisting essentially of about 38 to 42 atom percent iron, about 38 to 42 atom percent nickel, and about 12 to 16 atom percent phosphorus and about 4 to 8 atom percent boron comprising: a. immersing at least one toroidally wound filament of said alloy in a heat-transfer liquid heated to a temperature of between about 310° and 350° C, said liquid being (1) thermally stable to at least 350° C (2) nonferromagnetic, (3) electrically inert and (4) substantially unreactive with said alloy; b. maintaining said temperature between about 310° and 350° C for about 3/4 to 8 hrs, depending on the temperature selected; and c. cooling said filament to about 25° C at a rate not greater than about 30° C/min through its Curie temperature.
Claim 2
Dependent Claim
142 words
A process for increasing induction, decreasing coercivity and increasing permeability of a substantially glassy metal alloy consisting essentially of about 38 to 42 atom percent iron, about 38 to 42 atom percent nickel, and about 12 to 16 atom percent phosphorus and about 4 to 8 atom percent boron comprising: a. immersing at least one toroidally wound filament of said alloy in a heat-transfer liquid heated to a temperature of between about 310° and 350° C, said liquid being (1) thermally stable to at least 350° C (2) nonferromagnetic, (3) electrically inert and (4) substantially unreactive with said alloy; b. maintaining said temperature between about 310° and 350° C for about 3/4 to 8 hrs, depending on the temperature selected; and c. cooling said filament to about 25° C at a rate not greater than about 30° C/min through its Curie temperature.
Claim 3
Dependent Claim
22 words
The process of claim 1 in which said alloy has the approximate composition Fe 40 Ni 40 P 14 B 6 .
Claim 4
Dependent Claim
17 words
The process of claim 1 in which said liquid consists essentially of a stabilized iron-containing diorganopolysiloxane compound.
Claim 5
Dependent Claim
19 words
The process of claim 3 in which said liquid consists essentially of an iron stabilized trimethyl end blocked dimethylsiloxane.
Claim 6
Dependent Claim
18 words
The process of claim 1 in which said temperature is maintained at about 320° C to 330° C.
Claim 7
Dependent Claim
17 words
The process of claim 5 in which said temperature is maintained from about 13/4 to 21/2 hrs.
Claim 8
Dependent Claim
16 words
The process of claim 1 in which said cooling rate is about 20° to 30° C/min.
Claim 9
Dependent Claim
32 words
The process of claim 1 in which during immersion a magnetic field of about 1 to 10 Oe is circumferentially applied around said toroidally wound filament during cooling through the Curie temperature.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-27 | 1981-09-26 | 1982-03-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-27 | 1985-09-26 | 1986-03-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-27 | 1989-09-26 | 1990-03-28 | $7700.00 | Window Closed / Lapsed |