Assignee: Shipley Co Inc
•
Filing: 1976-06-29
•
Granted: 1978-03-21
•
Expires: 1996-06-29
Abstract
Abstract An improved etchant solution for selectively etching unprotected areas of metal film from a substrate which comprises between about 65 and about 90 parts by weight phosphoric acid, between about 0.5 and about 5 parts by weight of a perchloric acid component and between about 9 and about 30 parts by weight water, which composition contains from 0 to about 5% by weight total volume of a neutral or anionic wetting agent. The invention also comprises the method of utilizing the etchant composition and the improved precision device produced thereby.
Inventors
- 👤 Angelo J. Battisti
- 👤 Frank J. Loprest
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 11:46
CPC Classifications
C; C23; C23F; C23F1/00; C23F1/10; C23F1/14; C23F1/16; C23F1/20
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
84 words
A composition for etching an aluminum film or alloys thereof containing a predominant proportion of aluminum, said composition consisting of between about 65 and about 90 parts by weight phosphoric acid, between about 0.5 and about 5 parts by weight of a perchloric component selected from the group consisting of perchloric acid, perchloric anhydride and a perchloric hydrate, and between about 9 and about 30 parts by weight water, and from 0 to about 5% by weight of a neutral or anionic wetting agent.
Claim 2
Dependent Claim
84 words
A composition for etching an aluminum film or alloys thereof containing a predominant proportion of aluminum, said composition consisting of between about 65 and about 90 parts by weight phosphoric acid, between about 0.5 and about 5 parts by weight of a perchloric component selected from the group consisting of perchloric acid, perchloric anhydride and a perchloric hydrate, and between about 9 and about 30 parts by weight water, and from 0 to about 5% by weight of a neutral or anionic wetting agent.
Claim 3
Dependent Claim
12 words
The composition of claim 1 wherein the perchloric component is perchloric acid.
Claim 4
Dependent Claim
28 words
The composition of claim 1 wherein the composition contains between about 0.01% up to about 1.5% by weight wetting agent and said wetting agent is a fluorinated hydrocarbon.
Claim 5
Dependent Claim
22 words
The composition of claim 3 wherein the wetting agent is an alkali metal, or an ammonium, salt of a perfluorinated carboxylic acid.
Claim 6
Dependent Claim
12 words
The composition of claim 1 wherein the composition contains no wetting agent.
Claim 7
Dependent Claim
45 words
A process for selectively etching an exposed area of aluminum or aluminum alloy metal film deposited on a substrate and having an exposed area and a resist coated area, which comprises contacting said exposed area of metal film with the etching composition of claim 1.
Claim 8
Dependent Claim
27 words
The process of claim 6 wherein the metal film on the substrate and the resist coating are each between about 50 mu and about 5,000 mu thick.
Claim 9
Dependent Claim
14 words
The process of claim 7 wherein the resist coating is a negative working photoresist.
Claim 10
Dependent Claim
14 words
The process of claim 7 wherein the resist coating is a positive working photoresist.
Claim 11
Dependent Claim
20 words
The process of claim 9 wherein the positive working photoresist is an acrylic type polymer having a diazo oxide sensitizer.
Claim 12
Dependent Claim
40 words
The process of claim 6 wherein the thickness of the metal film on the substrate is between about 200 mu and about 2,500 mu and the thickness of the resist coating is between about 100 mu and about 1,500 mu.
Claim 13
Dependent Claim
28 words
The process of claim 6 wherein the etching with the composition of claim 1 is carried out at a temperature between about 25° C and about 110° C.
Claim 14
Dependent Claim
22 words
The process of claim 12 wherein the etching rate is between about 50 mu and about 1,200 mu film thickness per minute.
Claim 15
Dependent Claim
19 words
The process of claim 6 wherein the composition of claim 1 is employed at a pH below about 1.5.
Claim 16
Dependent Claim
24 words
The process of claim 6 wherein the metal film is an aluminum film which is deposited on the substrate by the process of evaporation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-20 | 1981-09-19 | 1982-03-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-20 | 1985-09-19 | 1986-03-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-20 | 1989-09-19 | 1990-03-21 | $7700.00 | Window Closed / Lapsed |