Multi-layer blow molded container and process for preparation thereof
Assignee: Toyo Seikan Group Holdings Ltd
•
Filing: 1975-02-21
•
Granted: 1978-03-21
•
Expires: 1995-02-21
Abstract
Abstract In a multi-layer blow molded container having a joint portion at least in the bottom portion thereof, barrier characteristics to gases such as oxygen and water vapor and liquids such as water, solvents, aqueous ammonia and salt water and interlaminar strength characteristics such as interlaminar adhesion strength, peel strength and impact strength in the content-filled state can be highly improved by blow molding a parison of a laminate structure of two or more polymer layers in which the polymer composition is different with respect to the thickness direction of the container wall but substantially identical with respect to the plane direction and each of the polymer layers is continuous with respect to the plane direction, in such a manner that a tapered projection protruding outwardly in the thickness direction of the container wall is formed in the joint portion so that each of the polymer layers is substantially continuous in this joint portion. This improved container can easily be prepared according to the customary blow molding technique by using a pair of split molds having such a configuration that a tapered concave groove is formed in the section pinching off the parison when the molds are registered with each other.
Inventors
- 👤 Toru Suzuki
- 👤 Shunsaku Hirata
- 👤 Jinichi Yazaki
- 👤 Shinichi Miyazaki
- 👤 Shigezo Nohara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 22:16
CPC Classifications
B; B29; B29C; B29C49/00; B29C49/22; B65; B65D; B65D1/00; B65D1/02; B65D1/0207; B65D1/0215; B29C2949/00; B29C2949/07; B29C2949/081; B29C2949/082; B29C2949/0829; B29C2949/0839; Y; Y10; Y10S; Y10S220/00; Y10S220/14; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1379; Y10T428/1383; Y10T428/24; Y10T428/24628; Y10T428/31504; Y10T428/31725; Y10T428/31739; Y10T428/31743; Y10T428/31746; Y10T428/31786; Y10T428/31797; Y10T428/31855; Y10T428/31909; Y10T428/31913
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
140 words
A plastic container composed of a container wall formed by blow-molding a tubular parison and provided with a joint portion at least in the bottom thereof formed by pinching off said parison, wherein said container wall has a multi-layer molded structure including an inner surface layer composed of a polyolefin, an outer surface layer composed of a polyolefin and an oxygen-barrier intermediate layer composed of a saponified ethylene-vinyl acetate copolymer having an ethylene content of 25 to 75 mole % and a degree of saponification of at least 93%, a polymer blend of said saponified copolymer and other thermoplastic resin, or a polyamide, and wherein said joint portion forms a tapered projection protruding outwardly in the thickness direction of the container wall so that each of the polymer layers constituting the multi-layer structure is substantially continuous in said joint portion.
Claim 2
Dependent Claim
140 words
A plastic container composed of a container wall formed by blow-molding a tubular parison and provided with a joint portion at least in the bottom thereof formed by pinching off said parison, wherein said container wall has a multi-layer molded structure including an inner surface layer composed of a polyolefin, an outer surface layer composed of a polyolefin and an oxygen-barrier intermediate layer composed of a saponified ethylene-vinyl acetate copolymer having an ethylene content of 25 to 75 mole % and a degree of saponification of at least 93%, a polymer blend of said saponified copolymer and other thermoplastic resin, or a polyamide, and wherein said joint portion forms a tapered projection protruding outwardly in the thickness direction of the container wall so that each of the polymer layers constituting the multi-layer structure is substantially continuous in said joint portion.
Claim 3
Dependent Claim
40 words
A plastic container as set forth in claim 1 wherein said joint portion forms a tapered projection protruding outwardly in the thickness direction of the container wall and said projection has an opening angle of about 45° to about 120°.
Claim 4
Dependent Claim
24 words
A plastic container as set forth in claim 2 wherein said projection has a V-figured sectional form of an opening angle of substantially 90°.
Claim 5
Dependent Claim
21 words
A plastic container as set forth in claim 1 wherein said projection has a protrusion length of 0.5 to 5 mm.
Claim 6
Dependent Claim
52 words
A plastic container as set forth in claim 1 wherein the oxygen-barrier intermediate layer is composed of a polymer blend of said saponified ethylene-vinyl acetate copolymer and at least one member selected from polyolefins and thermoplastic polymer containing carbonyl groups at a concentration of 120 to 1400 meq/100 g of the polymer.
Claim 7
Dependent Claim
56 words
A plastic container as set forth in claim 5 wherein said blend comprises 100 parts by weight of said saponified ethylene-vinyl acetate copolymer and 0.5 to 120 parts by weight of at least one member selected from polyolefins and thermoplastic polymers containing carbonyl groups at a concentration of 120 to 1400 meq/100 g of the polymer.
Claim 8
Dependent Claim
193 words
A plastic container composed of a container wall formed by blow-molding a tubular parison and provided with a joint portion at least in the bottom thereof formed by pinching off said parison, wherein said container wall has a multi-layer structure including an inner surface layer of a polyolefin, an outer surface layer composed of a polyolefin and an oxygen-barrier intermediate layer composed of a polymer bland of (a) 100 parts by weight of a saponified ethylene-vinyl acetate copolymer having an ethylene content of 25 to 75 mole % and a degree of saponification of at least 93% and 0.5 to 120 parts by weight of at least one member selected from polyolefins and thermoplastic polymers containing carbonyl groups at a concentration of 120 to 1400 meq/100 g of the polymer, and wherein said joint portion forms a tapered projection protruding outwardly in the thickness direction of the container wall so that each of the polymer layers constituting the multi-layer structure is substantially continuous in said joint portion, said projection having a V-figured sectional form of an opening angle of about 45° to about 120° and a protrusion length of 0.5 to 5 mm.
Claim 9
Dependent Claim
193 words
A plastic container composed of a container wall formed by blow-molding a tubular parison and provided with a joint portion at least in the bottom thereof formed by pinching off said parison, wherein said container wall has a multi-layer structure including an inner surface layer of a polyolefin, an outer surface layer composed of a polyolefin and an oxygen-barrier intermediate layer composed of a polymer bland of (a) 100 parts by weight of a saponified ethylene-vinyl acetate copolymer having an ethylene content of 25 to 75 mole % and a degree of saponification of at least 93% and 0.5 to 120 parts by weight of at least one member selected from polyolefins and thermoplastic polymers containing carbonyl groups at a concentration of 120 to 1400 meq/100 g of the polymer, and wherein said joint portion forms a tapered projection protruding outwardly in the thickness direction of the container wall so that each of the polymer layers constituting the multi-layer structure is substantially continuous in said joint portion, said projection having a V-figured sectional form of an opening angle of about 45° to about 120° and a protrusion length of 0.5 to 5 mm.
Claim 10
Dependent Claim
171 words
A process for the preparation of plastic containers comprising forming a tubular parison of a multi-layer structure including an inner surface layer composed of a polyolefin, and an outer surface layer of a polyolefin and an oxygen-barrier intermediate layer composed of a saponified ethylene-vinyl acetate copolymer having an ethylene content of 25 to 75 mole % and a degree of saponification of at least 93% and selectively a polyamide by means of co-melt-extrusion and a polymer blend of said saponified copolymer and other thermoplastic resin, providing a split mold including a pair of mold halves having such a configuration that a tapered concave groove is formed interiorly of the mold in the section pinching off the parison when the mold halves are resistered with each other, supporting the co-melt-extruded parison in said split mold, and inflating the parison in the split mold to form an outwardly protruding projection in the joint portion of the parison so that each of the layers constituting the parison is substantially continuous in said joint portion.
Claim 11
Dependent Claim
171 words
A process for the preparation of plastic containers comprising forming a tubular parison of a multi-layer structure including an inner surface layer composed of a polyolefin, and an outer surface layer of a polyolefin and an oxygen-barrier intermediate layer composed of a saponified ethylene-vinyl acetate copolymer having an ethylene content of 25 to 75 mole % and a degree of saponification of at least 93% and selectively a polyamide by means of co-melt-extrusion and a polymer blend of said saponified copolymer and other thermoplastic resin, providing a split mold including a pair of mold halves having such a configuration that a tapered concave groove is formed interiorly of the mold in the section pinching off the parison when the mold halves are resistered with each other, supporting the co-melt-extruded parison in said split mold, and inflating the parison in the split mold to form an outwardly protruding projection in the joint portion of the parison so that each of the layers constituting the parison is substantially continuous in said joint portion.
References Cited (Backward Citations)
US2710987A
Cited
US3457337A
Cited
US3561629A
Cited
US3869056A
Cited
US3847728A
Cited
US3892828A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-03-20 | 1981-09-19 | 1982-03-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-03-20 | 1985-09-19 | 1986-03-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-03-20 | 1989-09-19 | 1990-03-21 | $7700.00 | Window Closed / Lapsed |